Solar thermal-insulation and water-proof coating

A waterproof coating and solar energy technology, which is applied in the field of solar energy, can solve the problems of poor thermal stability and corrosion resistance of black nickel coatings, and achieve improved physical and chemical properties, good thermal stability and weather resistance, and excellent gloss and color retention. Effect

Inactive Publication Date: 2018-07-20
JIANGSU SHUANGNENG SOLAR ENERGY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Due to the poor thermal stability and corrosion resistance of black nickel coating, it is usually only suitable for low temperature solar thermal utilization

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] The thermal insulation and waterproof coating for solar energy of the present invention is made of the following components in proportion by weight fraction:

[0020] 44 parts of film-forming agent, 28 parts of acrylic resin with a concentration of 48%-53%, 1.0 parts of carbon black, 1.1 parts of chromium oxide green, 8 parts of methyl isobutyl ketone, 13 parts of film-forming aid, and 4 parts of enamel black , 44 parts of light absorbing agent, 5 parts of organic bentonite, 0.1 part of silicone oil with a concentration of 0.5%-1.5%, 23 parts of solvent, 4 parts of iron manganese black pigment, 6 parts of additives, 8 parts of butyl acetate, and 6 parts of organic bentonite.

[0021] In the above formula, the wavelength of ultraviolet light irradiation is 200nm-400nm, the film-forming agent is modified casein-gelatin, and the light-absorbing agent is cobalt blue powder, cobalt manganese copper oxide blended into black; or use chromium oxide green powder, selenium vulcani...

Embodiment 2

[0023] The thermal insulation and waterproof coating for solar energy of the present invention is made of the following components in proportion by weight fraction:

[0024] 87 parts of film-forming agent, 35 parts of acrylic resin with a concentration of 48%-53%, 2.4 parts of carbon black, 1.8 parts of chromium oxide green, 10 parts of methyl isobutyl ketone, 25 parts of film-forming aid, and 9 parts of enamel black , 63 parts of light absorbing agent, 10 parts of organic bentonite, 0.1 part of silicone oil with a concentration of 0.5%-1.5%, 47 parts of solvent, 8 parts of iron-manganese black pigment, 23 parts of additives, 10 parts of butyl acetate, and 12 parts of organic bentonite.

[0025] In the above formula, the wavelength of ultraviolet light irradiation is 200nm-400nm, the film-forming agent is modified casein-gelatin, and the light-absorbing agent is cobalt blue powder, cobalt manganese copper oxide blended into black; or use chromium oxide green powder, selenium vu...

Embodiment 3

[0027] The thermal insulation and waterproof coating for solar energy of the present invention is made of the following components in proportion by weight fraction:

[0028] 65 parts of film-forming agent, 31 parts of acrylic resin with a concentration of 48%-53%, 1.7 parts of carbon black, 1.4 parts of chromium oxide green, 9 parts of methyl isobutyl ketone, 19 parts of film-forming aid, and 7 parts of enamel black , 55 parts of light absorbing agent, 7 parts of organic bentonite, 0.1 part of silicone oil with a concentration of 0.5%-1.5%, 35 parts of solvent, 6 parts of iron-manganese black pigment, 13 parts of additives, 9 parts of butyl acetate, and 9 parts of organic bentonite.

[0029] In the above formula, the wavelength of ultraviolet light irradiation is 200nm-400nm, the film-forming agent is modified casein-gelatin, and the light-absorbing agent is cobalt blue powder, cobalt manganese copper oxide blended into black; or use chromium oxide green powder, selenium vulcan...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
wavelengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to a solar thermal-insulation and water-proof coating. The coating is prepared from components in parts by weight as follows: 44-87 parts of a film-forming agent, 28-35 parts ofacrylic resin with concentration being 48%-53%, 1.0-2.4 parts of carbon black, 1.1-1.8 parts of chromium oxide green, 8-10 parts of methyl isobutyl ketone, 13-25 parts of a coalescing agent, 4-9 partsof enamel black, 44-63 parts of a light absorption agent, 5-10 parts of organobentonite, 0.1 parts of silicone oil with concentration being 0.5%-1.5%, 23-47 parts of a solvent, 4-8 parts of ferrimanganic black pigment, 6-23 parts of an auxiliary, 8-10 parts of butyl acetate and 6-12 parts of organobentonite. The coating has the advantages of excellent weather fastness and light and color retention performance, is mainly applied to conversion of solar energy into thermal energy, and is particularly suitable for the fields such as a solar water heater, a greenhouse and the like.

Description

technical field [0001] The invention relates to the field of solar energy, in particular to a thermal insulation and waterproof coating for solar energy. Background technique [0002] Solar absorbing coatings have a great impact on the technical and economic performance of solar energy utilization. In order to improve the efficiency of solar energy devices and reduce costs, solar science and technology workers in various countries attach great importance to the research and development of solar absorbing coatings, and have developed a variety of coatings. has been used in production with good results. [0003] Electroplating coating is a mature technology of solar absorbing materials, which can be divided into black chromium coating or black nickel coating. The absorption ratio α and emission ratio ε of black chromium coating are 0.93-0.97 and 0.07 respectively. -0.15, α / ε is 6-13, with excellent spectral selectivity. The thermal stability and high temperature resistance o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D189/00C09D133/00C09D5/32C09D5/08C09D7/63C09D7/61C09D7/45C09D7/47
CPCC09D189/00C08L2201/08C08L2205/035C09D5/08C09D5/18C09D5/32C09D133/00C09D189/005C08L89/005C08L33/00C08K13/02C08K3/04C08K5/06C08K3/346C08L89/00
Inventor 贲道祥
Owner JIANGSU SHUANGNENG SOLAR ENERGY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com