Preparation method of hydroxyethyl chitosan nano composite bone support material

A hydroxyethyl chitosan and nanocomposite technology, applied in the field of biomedical materials, can solve problems such as poor mechanical properties, and achieve the effects of low cost, good adhesion, and good biological activity

Active Publication Date: 2018-09-04
XINYANG NORMAL UNIVERSITY
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Bioceramics made of calcium phosphate all have poor mechanical properties and have limitations in load-bearing areas

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of hydroxyethyl chitosan nano composite bone support material
  • Preparation method of hydroxyethyl chitosan nano composite bone support material
  • Preparation method of hydroxyethyl chitosan nano composite bone support material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] (1) Preparation of biphasic calcium phosphate nanopowder: 0.4M Ca(NO 3 ) 2 .4H 2 O solution and 0.2M (NH 4 ) 2 HPO 4 The solution was added into a three-necked flask according to the calcium-phosphorus molar ratio of 1.65:1, stirred and mixed evenly, and then the pH was adjusted to 11 with 25% ammonia water to obtain a white powder precipitate. After filtering, the white powder was washed with deionized water. Then dry it at 80°C, put it into a muffle furnace for roasting, first raise the temperature to 1125°C at a rate of 10°C / min, keep it for 1 hour, then drop it to room temperature with the furnace, then take it out and grind it, and finally pass it through a 200-mesh sieve to obtain a two-phase Calcium phosphate nanopowder;

[0025] (2) prepare hydroxyethyl chitosan: get 10g chitosan and join in the 50wt% sodium hydroxide solution of 16.7g and carry out alkalization, obtain chitosan solution, described alkalization is carried out in-20 ℃ refrigerator, The alka...

Embodiment 2

[0029] The preparation process is basically the same as in Example 1, except that the mass ratio of hydroxyethyl chitosan, cellulose, and biphasic calcium phosphate nanopowder in step (2) is 2:1:1.

[0030] The scanning electron micrograph of the composite bone scaffold material that embodiment 2 makes is shown in figure 1 ,in, figure 1 A is the composite bone scaffold material of embodiment 1, figure 1 B is the composite bone scaffold material of Example 2.

Embodiment 3

[0032] The preparation process is basically the same as in Example 1, except that the mass ratio of hydroxyethyl chitosan, cellulose, and biphasic calcium phosphate nanopowder in step (2) is 1:1:2.

[0033] The scanning electron micrograph of the composite bone scaffold material that embodiment 3 makes is shown in figure 1 ,in, figure 1 A is the composite bone scaffold material of embodiment 1, figure 1 B is the composite bone scaffold material of embodiment 2, figure 1 C is the composite bone scaffold material of Example 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a preparation method of a hydroxyethyl chitosan nano composite bone support material. The preparation method comprises the following steps: obtaining phosphorus calcium powderin a precipitating method, roasting, and obtaining hydroxyapatite / beta-tricalcium phosphate two-phase phosphorus calcium nano powder, performing the hydroxyethylation on chitosan, preparing hydroxyethyl chitosan, finally dissolving the hydroxyethyl chitosan in a 1 percent acetum solution, mixing and stirring the hydroxyethyl chitosan, gelatin and two-phase phosphorus calcium nano powder accordingto a mass ratio of (1 to 4) to 1 to (0.5 to 4), degassing, uniformly dispersing, circularly freezing and thawing the solution, and finally drying, thus obtaining the hydroxyethyl chitosan nano composite bone support material. The preparation method is simple in preparation process, easy in operation, capable of realizing the batched preparation, lower in cost, and pollution-free; and by adoptinga ternary material system, a prepared bone support has an appropriate degradation rate, the cell compatibility of the bone support is improved, the biological activity is better, and the cell can be better adhered and proliferated.

Description

technical field [0001] The invention relates to a preparation method of a hydroxyethyl chitosan nanocomposite bone scaffold material, belonging to the technical field of biomedical materials. Background technique [0002] Chitosan is obtained by deacetylation of chitin, which exists widely in nature. This natural polymer has excellent properties such as biocompatibility, blood compatibility, safety, and microbial degradation. One of the better materials. However, chitosan gel needs to be cross-linked during the preparation process, and the cross-linking agent is usually glutaraldehyde. The introduction of the cross-linking agent will reduce the cytocompatibility of the scaffold, and the mechanical properties are also poor. [0003] Bone tissue contains a large amount of phosphorus-calcium materials, such as tricalcium phosphate, hydroxyapatite, calcium carbonate, etc., so phosphorus-calcium materials are often used to prepare artificial bone scaffolds. Calcium phosphate-ba...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): A61L27/48A61L27/46A61L27/58
CPCA61L27/46A61L27/48A61L27/58A61L2430/02C08L5/08C08L1/02
Inventor 聂磊侯孟娟杨亚男李星辰董婧
Owner XINYANG NORMAL UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com