Preparation method and application of a 1t phase molybdenum disulfide supported titanium dioxide nanotube array

A nanotube array, titanium dioxide technology, applied in chemical instruments and methods, physical/chemical process catalysts, metal/metal oxide/metal hydroxide catalysts, etc., can solve the problems of poor degradation effect of antibiotic wastewater, etc. The effect of easy mass production and large specific surface area

Active Publication Date: 2021-06-29
NANCHANG HANGKONG UNIVERSITY
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The present invention aims to solve the current technical problem of poor degradation effect on antibiotic wastewater, and provides a preparation method and application of a 1T phase molybdenum disulfide-loaded titanium dioxide nanotube array

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method and application of a 1t phase molybdenum disulfide supported titanium dioxide nanotube array
  • Preparation method and application of a 1t phase molybdenum disulfide supported titanium dioxide nanotube array
  • Preparation method and application of a 1t phase molybdenum disulfide supported titanium dioxide nanotube array

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach 1

[0023] Specific embodiment 1: This embodiment is a method for preparing a 1T phase molybdenum disulfide-supported titanium dioxide nanotube array, which is specifically carried out according to the following steps:

[0024] 1. Prepare titanium wire: Wind the titanium wire into a spiral shape, then ultrasonically clean it with acetone, ethanol and deionized water for 0.5h to 1h respectively, and finally place it in a drying oven to dry;

[0025] 2. Place the dried titanium wire in step 1 as the anode in the electrolytic cell, and the platinum mesh as the cathode in the electrolytic cell; the solute of the electrolyte is hydrofluoric acid, the solvent is dimethyl sulfoxide, and the hydrogen fluoride in the electrolyte is The mass fraction of the acid is 2% to 3%; it is oxidized at room temperature and under the condition of a constant voltage of DC power supply of 30V to 35V for 8h to 10h. After the oxidation is completed, it is taken out and dried to obtain an amorphous form bas...

specific Embodiment approach 2

[0028] Specific embodiment 2: The difference between this embodiment and specific embodiment 1 is that in step 1, the titanium wire is wound into a spiral shape, and then ultrasonically cleaned with acetone, ethanol and deionized water for 0.5h respectively, and finally placed in a drying box dry. Others are the same as the first embodiment.

specific Embodiment approach 3

[0029] Specific embodiment three: the difference between this embodiment and specific embodiment one or two is that: the solute of the electrolytic solution described in step one is hydrofluoric acid, the solvent is dimethyl sulfoxide, the quality of hydrofluoric acid in the electrolytic solution The score is 2%. Others are the same as those in Embodiment 1 or 2.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
Login to View More

Abstract

A preparation method and application of a 1T phase molybdenum disulfide supported titanium dioxide nanotube array, relating to a preparation method and application of a titanium dioxide nanotube array. The invention aims to solve the technical problem that the degradation effect of antibiotic waste water is not good at present. The preparation method of the present invention is carried out according to the following steps: 1. preparing titanium wire; 2. preparing amorphous titanium dioxide; 3. annealing; 4. hydrothermal reaction. The composite material of the 1T phase molybdenum disulfide-loaded titania nanotube array of the present invention is used as a catalyst for photoelectric catalytic degradation of antibiotics in antibiotic wastewater. The composite material prepared by the present invention is under the action of sunlight and electricity, wherein the TiO 2 Hydroxyl radicals generated by NTS can oxidatively degrade antibiotic molecules, while 1T phase MoS 2 It can quickly reduce and dehalogenate antibiotic molecules in an electrocatalytic environment, so as to achieve the purpose of rapidly degrading pollutants, and can degrade more than 95% of antibiotics within 2 hours.

Description

technical field [0001] The invention relates to a preparation method and application of a titanium dioxide nanotube array. Background technique [0002] Since the introduction of penicillin in 1929, antibiotics have been instrumental in improving the health of humans and animals. Veterinary antibiotics are also commonly added to animal feed in some countries to improve growth rate and feed efficiency. Antibiotics for human and veterinary use are primarily excreted in urine and feces, with a significant fraction excreted in the unchanged active form. Antibiotic contamination is also present in different environmental areas such as WWTPs, livestock farms, river water and soil and groundwater. Residual antibiotics in the environment can adversely affect non-target organisms, contaminate food and drinking water supplies, and increase bacterial resistance. [0003] Florfenicol, as an antibiotic, is a new generation of amide alcohol semi-synthetic antibiotics developed by Seher...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/28B01J35/02C02F1/30C02F1/46C02F101/36C02F103/34B01J35/00
CPCC02F1/30C02F1/46B01J23/28C02F2101/36C02F2103/343B01J35/33B01J35/40B01J35/39
Inventor 杨利明李耀邦杨丽霞罗胜联
Owner NANCHANG HANGKONG UNIVERSITY