A kind of alumina pellet containing molecular sieve and preparation method thereof

A technology for sieving alumina and containing alumina, which is applied in the field of molecular sieve-containing alumina pellets and its preparation, can solve problems such as inability to meet the requirements of moving bed reactions, and achieve easy large-scale industrial production, high molecular sieve content, and improved aromatics yield. rate effect

Active Publication Date: 2022-02-08
CHINA PETROLEUM & CHEM CORP +1
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Chinese patent CN104549554A introduces a method for forming molecular sieve into balls. In this method, molecular sieve powder and alumina powder are evenly mixed, and aluminum sol is sprayed in a rotary molding device to be rotated into balls, wherein the solid content of the aluminum sol is 10-25 % by mass, the crushing strength of molecular sieve pellets prepared by this method can be increased to 30N / particle, but still cannot meet the requirements of moving bed reaction

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of alumina pellet containing molecular sieve and preparation method thereof
  • A kind of alumina pellet containing molecular sieve and preparation method thereof
  • A kind of alumina pellet containing molecular sieve and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033]The present invention also provides a molecular sieve-containing alumina pellet prepared by the provided preparation method. The specific surface area of ​​the alumina pellet containing molecular sieve can be 150-500m 2 / g, preferably 200-400m 2 / g, the pore volume can be 0.3-1.5mL / g, preferably 0.5-1.3mL / g.

[0034] After the molecular sieve-containing alumina pellets of the present invention are loaded with active components, a catalyst containing molecular sieves can be prepared.

[0035] One embodiment is to prepare a catalyst for aromatization of light hydrocarbons. The catalyst includes alumina pellets containing molecular sieves and zinc, based on the alumina pellets containing molecular sieves, the content of the zinc is 0.1-10% by mass, and the The molecular sieve in the alumina ball containing molecular sieve is ZSM-5 molecular sieve. The catalyst is suitable for C 4 -C 6 Monomer hydrocarbons (such as isobutane) or olefinic light hydrocarbons undergo aroma...

example 1

[0042] (1) Preparation of mixed sols.

[0043] Take 54.8g of high-purity pseudo-boehmite (produced by Condea, Germany, brand SB, containing 40g of alumina) prepared by hydrolysis of alkoxy aluminum, 30.0g of urea and 135g of deionized water and mix and stir for 0.5h to form alumina suspension solution; 2.0 g of nitric acid solution with a concentration of 24% by mass was added dropwise to the aluminum hydroxide suspension as the first acid solution for the first peptization, stirred for 0.5 h, and the pH value was controlled to 3.8 to obtain alumina sol.

[0044] Add 40g of HZSM-5 molecular sieve to the alumina sol, the molar ratio of silica to alumina is 50 (produced by Sinopec Catalyst Changling Branch), and 3.0g of nitric acid solution with a concentration of 24% by mass is added dropwise as the second acid The solution was subjected to the second peptization, the pH value was controlled at 2.5, and stirred at 20°C for 2 hours to obtain a mixed sol, the viscosity of the mix...

example 2

[0052] (1) Preparation of mixed sols.

[0053] Get 54.8g of high-purity pseudo-boehmite (produced by Condea, Germany, brand SB, containing 40g of alumina) prepared by hydrolysis of alkoxy aluminum, 35.0g of urea and 140g of deionized water and mix and stir for 0.5h to form aluminum hydroxide To the suspension, 2.0 g of nitric acid solution with a concentration of 24% by mass was added dropwise as the first acid solution for the first peptization, stirred for 0.5 h, and the pH value was controlled to be 3.8 to obtain alumina sol.

[0054] Add 60g of HZSM-5 molecular sieve to the alumina sol, the molar ratio of silicon oxide to aluminum oxide is 50 (produced by Sinopec Catalyst Changling Branch), and 3.2g of nitric acid solution with a concentration of 24% by mass is added dropwise as the second acid The solution was subjected to the second peptization, the pH value was controlled to 2.3, and stirred at 20°C for 2 hours to obtain a mixed sol, the viscosity of the mixed sol was 1...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
specific surface areaaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention relates to a molecular sieve-containing alumina pellet and a preparation method thereof. The preparation method comprises: (1) preparing a mixed sol: mixing pseudoboehmite, urea and deionized water to obtain an aluminum hydroxide suspension; Adding the first acid solution to the aluminum hydroxide suspension for the first peptization to obtain an alumina sol; mixing the alumina sol with molecular sieves and adding the second acid solution for the second peptization to obtain a mixed sol; (2) heating oil Column molding to produce alumina pellets containing molecular sieves: mix the mixed sol obtained in step (1) with hexamethylenetetramine and drop them into a hot oil column to form pellets, take out the pellets, wash, dry and roast , to obtain alumina pellets containing molecular sieves. The molecular sieve-containing alumina pellets provided by the invention have high molecular sieve content and high crushing strength.

Description

technical field [0001] The invention relates to a molecular sieve-containing alumina pellet and a preparation method thereof. Background technique [0002] Molecular sieves are widely used in the petrochemical industry due to their unique pore structure and good catalytic performance. Catalysts containing molecular sieves gradually accumulate carbon on the surface as the operating cycle increases, and the activity decreases. In order to maintain activity, the catalyst needs to be regenerated. Since the fixed-bed reactor cannot be regenerated on-line, there is a large difference in catalyst activity between the beginning and end of production, and it is necessary to increase the temperature to maintain activity, which is not conducive to the stability of the operation of the reaction system. The moving bed reactor can realize the continuous operation of reaction and regeneration, and the catalyst activity can be kept constant. In order to realize the moving bed reaction, a...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J29/40B01J29/18B01J29/22B01J29/70B01J32/00B01J35/08C07C5/27C07C9/16C07C2/00C07C15/02
CPCC07C2/00C07C5/2775B01J29/18B01J29/22B01J29/40B01J29/405B01J29/7007B01J29/7057B01J35/08B01J35/1019B01J35/1038B01J35/1042B01J35/1047C07C2529/22C07C2529/40C07C2529/70B01J2229/18C07C9/16C07C15/02
Inventor 刘建良刘洪全马爱增潘锦程
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com