Wear-resistant self-priming pump lining material prepared on basis of fluoroplastic

A technology of self-priming pumps and fluoroplastics, which is applied in the field of pump valve preparation, can solve the problems of pump valve damage, hazards, and affecting work efficiency, etc., and achieve the effect of reasonable raw material ratio, simple process flow, and increased material texture

Inactive Publication Date: 2019-05-07
陆伯川
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

There is no need to install a bottom valve in the pipeline. Just ensure that there is a quantitative suction liquid stored in the pump body before work. Different liquids can use self-priming pumps of different materials. With the continuous improvement of technology, self-priming pumps are also used in various fields. Diverse, in some chemical companies, because a large amount of acid and alkali and highly corrosive liquids need to be transported, the traditional self-priming pump will have corrosion and aging problems when used, and the concentration of these problems will lead to self-priming The pump is aging and damaged
[0003] Fluorine-lined self-priming pumps have solved the corrosion problem of the above-mentioned self-priming pumps in the field of pump valves at the present stage. The process is made of metal casing tightly lined with fluoroplastics. The main flow-passing parts, impeller and pump cover, are made of metal inserts and outsourced with fluoroplastics at high temperature. The application of this method fully solves the aging problem of self-priming pumps. , but there will still be some disadvantages in actual use
[0004] Fluoroplastics are generally plastic materials. In practical applications, due to different application fields, the fluoroplastics in the self-priming pump will transport different materials during normal use. In the industrial or chemical field, some mixed with a large amount of When the mixed liquid of particulate matter is pumped, due to the strong hardness of the particulate matter, the inner lining will be worn, scratched, even cracked and deformed during long-term transportation. In the lightest cases, the actual pump valve will be damaged, resulting in increased maintenance costs and affecting work efficiency. , the severe one will cause the liquid in the pump to overflow, and the harm caused is immeasurable

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] Weigh: 80kg of polytetrafluoroethylene, 60kg of polyperfluoroethylene propylene, 8kg of silicon nitride, 6kg of boron carbide, 8kg of gypsum powder, 6kg of milk thistle extract, 3kg of ethyl acetate, 5kg of zinc stearate, antimony oxide 6kg, modified paraffin wax 2kg, chromium trioxide 3kg, zirconium mullite 6kg, white corundum micropowder 2kg, lignocellulose 3kg, high-strength adhesive 25kg.

Embodiment 2

[0024] Weighing: 81kg of polytetrafluoroethylene, 61kg of polyperfluoroethylene propylene, 9kg of silicon nitride, 7kg of boron carbide, 9kg of gypsum powder, 7kg of milk thistle extract, 4kg of ethyl acetate, 6kg of zinc stearate, antimony oxide 7kg, modified paraffin wax 3kg, chromium trioxide 4kg, zirconium mullite 7kg, white corundum powder 3kg, lignocellulose 4kg, high-strength adhesive 30kg.

[0025] The method for preparing above-mentioned embodiment 1-2 is:

[0026] a. Put the polytetrafluoroethylene and polyperfluoroethylene propylene into the internal mixer, raise the temperature to 120°C within 20min, and stir while heating until all the materials are melted, and then keep at a constant temperature for standby use;

[0027] b, in the raw material after the above-mentioned step a treatment, add the modified paraffin in the raw material, heat up to 150 DEG C, keep standing at a constant temperature, for use;

[0028] c. Take a ball mill to mix the silicon nitride, bo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a wear-resistant self-priming pump lining material prepared on the basis of fluoroplastic, and relates to the technical field of pump valve preparation. The lining material isprepared from the following raw materials in parts by weight: 80-82 parts of polytetrafluoroethylene, 60-62 parts of polyperfluorinated ethylene propylene, 15-25 parts of phenolic resin, 6-8 parts ofmolybdenum disulfide, 3-5 parts of carbon black, 8-10 parts of titanium dioxide, 2-4 parts of ammonium ferrous sulfate, 3-5 parts of barium sulfate, 5-7 parts of magnesium hexasilicate, 3-5 parts of brown fused alumina, 3-5 parts of nano silicon carbide, 6-8 parts of nano zinc oxide, 2-4 parts of boron oxide, 6-8 parts of glass fibers and 40-50 parts of a high-strength adhesive. The lining material has the beneficial effects that the process flow is simple, the raw material ratio is reasonable, the raw materials are cheap and are easily available, anti-corrosion performance of conventional fluoroplastic is ensured, meanwhile, a wear-resistant effect is achieved, the effect is better, the raw materials are easy to obtain, the price is low, and the processing is simple.

Description

technical field [0001] The invention relates to the technical field of pump valve preparation, in particular to a wear-resistant self-priming pump lining material prepared based on fluoroplastics. Background technique [0002] The working principle of the self-priming pump is to fill the pump casing with water before starting the pump. After starting, the impeller rotates at a high speed to make the water in the impeller channel flow to the volute. At this time, a vacuum is formed at the inlet, so that the water inlet check door is opened and suction Air in the tube enters the pump and travels through the impeller channel to the outer edge. Self-priming pump is a self-priming centrifugal pump, which has the advantages of compact structure, convenient operation, stable operation, easy maintenance, high efficiency, long life, and strong self-priming ability. There is no need to install a bottom valve in the pipeline. It is only necessary to ensure that the pump body has a cer...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08L27/18C08L27/12C08L61/06C08L97/00C08L91/06C08K13/02C08K13/04C08K7/14C08K3/30C08K3/04C08K3/22C08K3/34C08K3/38C08K5/00
Inventor 陆伯川
Owner 陆伯川
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products