A kind of cobalt-cerium/sepiolite catalyst and its preparation method and application

A sepiolite and catalyst technology, applied in the field of cobalt-cerium/sepiolite catalyst and preparation thereof, can solve problems such as high price, unfavorable large-scale industrial application, etc., and achieve enhanced life, enhanced reforming performance and service life, The effect of increasing the conversion rate

Active Publication Date: 2022-03-29
ANHUI UNIV OF SCI & TECH
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, noble metal catalysts show high catalytic activity in reforming hydrogen production, but their expensive price is not conducive to large-scale industrial application

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of cobalt-cerium/sepiolite catalyst and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0036] The content of active component cobalt (Co) in the cobalt-cerium / sepiolite catalyst prepared in this embodiment is 5wt.%, the content of additive cerium (Ce) is 3wt.%, and the remaining ingredients are sepiolite. Preparation method as follows:

[0037] Take 10.00 g of sepiolite raw material, add it to 5 mol / L nitric acid, stir it magnetically for 2 hours in a constant temperature water bath at 40°C, then carry out suction filtration, washing, drying, and mechanical crushing to obtain solid powder I; put solid powder I in a tube In a type furnace, it was heated to 400°C at a heating rate of 1°C / min, and then calcined in an air atmosphere for 4 hours to obtain purified sepiolite; weigh 1.2346g Co(NO 3 ) 2 ·6H 2 O, 0.4648g Ce(NO 3 ) 3 ·6H 2 O and 2.9052g cetyltrimethylammonium bromide (surfactant to metal ion molar ratio S / M=1.5) were placed in a 250mL round bottom beaker and dissolved in 100mL deionized water to form solution I. Weigh 4.4043 g of the purified sepiol...

Embodiment 2

[0039] The content of active component cobalt (Co) in the cobalt-cerium / sepiolite catalyst prepared in this embodiment is 15wt.%, the content of additive cerium (Ce) is 24wt.%, and the remaining ingredients are sepiolite. Preparation method as follows:

[0040] Take 10.00 g of sepiolite raw material, add it to 10 mol / L nitric acid, and stir it magnetically for 4 hours under constant temperature water bath at 80°C, then carry out suction filtration, washing, drying, and mechanical crushing to obtain solid powder I; put solid powder I in a tube In a type furnace, heated to 700°C at a heating rate of 4°C / min, and then calcined in an air atmosphere for 2 hours to obtain purified sepiolite; weigh 2.6229g CH 3 COOCo·4H 2 O, 2.5336g CH 3 COOCe·xH 2 O and 4.5626g polysorbate 80 (surfactant and metal ion molar ratio S / M=0.5) were placed in a 250mL round bottom beaker and added to 100mL deionized water to completely dissolve to form solution I. Weigh 2.5046 g of the purified sepioli...

Embodiment 3

[0042] The content of active component cobalt (Co) in the cobalt-cerium / sepiolite catalyst prepared in this embodiment is 10wt.%, the content of additive cerium (Ce) is 8wt.%, and the remaining ingredients are sepiolite. Preparation method as follows:

[0043] Take 10.00 g of sepiolite raw material, add it to 6 mol / L nitric acid, and stir it magnetically for 4 hours under the condition of constant temperature water bath at 55°C, then carry out suction filtration, washing, drying, and mechanical crushing to obtain solid powder I; put solid powder I in a tube In a type furnace, heated to 700°C at a heating rate of 4°C / min, and then calcined in air atmosphere for 1.5h to obtain purified sepiolite; weigh 1.2346g Co(NO 3 ) 2 ·6H 2 O, 0.7373g CH 3 COOCe·xH 2 O and 2.0466g sodium lauryl sulfate (surfactant and metal ion molar ratio S / M=1) were placed in a 250mL round bottom beaker and added to 100mL deionized water to completely dissolve to form solution I. Weigh 4.2595 g of the...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a cobalt-cerium / sepiolite catalyst and its preparation method and application. The catalyst comprises sepiolite as a carrier and cobalt and cerium as active components loaded on the sepiolite. The cobalt-cerium / sepiolite catalyst of the present invention utilizes cerium oxide as an auxiliary component to interact with cobalt during the calcination and reduction process, thereby improving the conversion rate of bio-oil and its model, hydrogen production rate and stability. At the same time, ceria, as an auxiliary agent, undergoes a rapid redox cycle for oxygen transfer during the reforming process, improving the conversion rate of carbon-containing species and hydrogen production efficiency, avoiding the formation of carbon deposits covering metal sites, and thus enhancing catalyst life.

Description

technical field [0001] The invention relates to the field of catalysts, in particular to a cobalt-cerium / sepiolite catalyst and its preparation method and application. Background technique [0002] In recent years, the efficient use of biomass energy is the main way to solve the energy crisis and alleviate the deterioration of the ecological environment. At present, one of the more mature processes for biomass utilization is the high-temperature pyrolysis of biomass under anoxic conditions to prepare bio-oil. Bio-oil is not a real solution, but an emulsion. Different components exist in bio-oil with different droplet sizes, and bio-oil has certain acidity, rich in water and oxygen, As a result, its calorific value is low, and it is easy to corrode equipment, so it cannot be directly used in internal combustion engines. To improve the combustion characteristics of bio-oil, the bio-oil must be strictly dehydrated and deoxidized. This will undoubtedly increase the cost of bi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): B01J23/83B01J35/10C01B3/32
Inventor 陈明强汪春生王一双汤志远杨忠连张涵王君
Owner ANHUI UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap