Environment-friendly reaction type polishing brightener composition and preparation method and application thereof

A brightener and reactive technology, which is applied in the field of environmentally friendly reactive polishing brightener composition and its preparation, can solve the problems of narrow practical range, harm to human health, and high cost, and achieve increased residence time and polishing efficiency. Rust lubricant, good cleaning effect

Inactive Publication Date: 2019-08-23
广东锴力环保新材料有限公司
View PDF4 Cites 19 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, chemical brighteners used in stainless steel hardware tools can be basically divided into five types: aqua regia solution, sulfuric acid solution, phosphoric acid solution, acetic acid solution and hydrogen peroxide solution. The brightener contains nitric acid, which will produce a large amount of harmful gases such as nitrogen oxides during polishing, thereby polluting the environment and endangering human health; while the hydrogen peroxide type polishing fluid is easy to decompose, difficult to maintain, high cost, and narrow application range.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly reaction type polishing brightener composition and preparation method and application thereof
  • Environment-friendly reaction type polishing brightener composition and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] An environmentally friendly reactive polishing brightener composition by mass percentage: dodecylbenzenesulfonic acid 8.0%, diethanolamine 3.0%, triethanolamine 1.0%, fatty alcohol polyoxyethylene ether 2.0%, citric acid 4.0%, coconut Oil 0.5%, ethyl cellulose 0.5%, 2-mercaptobenzothiazole 0.5%, sulfamic acid 2.0%, water 78.5%.

[0028] The preparation steps of the above-mentioned environmentally friendly reactive polishing brightener composition are as follows:

[0029] 1) Prepare the following raw materials (mass percentage): dodecylbenzenesulfonic acid 8.0%, diethanolamine 3.0%, triethanolamine 1.0%, fatty alcohol polyoxyethylene ether 2.0%, citric acid 4.0%, coconut oil 0.5% %, ethyl cellulose 0.5%, 2-mercaptobenzothiazole 0.5%, sulfamic acid 2.0%, water 78.5%.

[0030] 2) Mix 8.0% dodecylbenzenesulfonic acid and 50% water and stir evenly;

[0031] 3) Add 3.0% diethanolamine, 1.0% triethanolamine, and 0.5% coconut oil, stir evenly, heat to 50-60°C and react for ab...

Embodiment 2

[0034] An environmentally friendly reactive polishing brightener composition by mass percentage: dodecylbenzenesulfonic acid 7.0%, isopropanolamine 3.0%, triethanolamine 1.0%, bisphenol A polyoxyethylene ether 1.5%, glycolic acid 2.0% %, gluconic acid 1.5%, palm stearic acid 0.5%, carboxymethyl cellulose 0.5%, benzotriazole 0.5%, octyl phosphoric acid 1.0%, water 80.5%.

[0035] The preparation steps of the above-mentioned environmentally friendly reactive polishing brightener composition are as follows:

[0036] 1) Prepare the following raw materials (mass percentage): dodecylbenzenesulfonic acid 7.0%, isopropanolamine 3.0%, triethanolamine 1.0%, bisphenol A polyoxyethylene ether 1.5%, glycolic acid 2.0%, Gluconic Acid 1.5%, Palm Stearic Acid 0.5%, Carboxymethyl Cellulose 0.5%, Benzotriazole 0.5%, Octyl Phosphate 1.0%, Water 80.5%.

[0037] 2) Mix 7.0% dodecylbenzenesulfonic acid and 50% water and stir evenly;

[0038] 3) Add isopropanolamine 3.0%, triethanolamine 1.0%, bis...

Embodiment 3

[0041] An environmentally friendly reactive polishing brightener composition by mass percentage: 6.0% of heavy alkylbenzenesulfonic acid, 3.0% of monoethanolamine, 1.5% of polyether, 3.0% of ethylenediaminetetraacetic acid, 0.5% of methyl cellulose, castor Sesame oil 0.5%, thiourea 0.5%, sodium bisulfate 2.0%, water 83.0%.

[0042] The preparation steps of the above-mentioned environmentally friendly reactive polishing brightener composition are as follows:

[0043]1) Prepare the following raw materials (mass percentage): heavy alkylbenzenesulfonic acid 6.0%, monoethanolamine 3.0%, polyether 1.5%, ethylenediaminetetraacetic acid 3.0%, methylcellulose 0.5%, ricinoleic acid 0.5%, thiourea 0.5%, sodium bisulfate 2.0%, water 83.0%.

[0044] 2) Mix 6.0% of heavy alkylbenzenesulfonic acid and 50% of water;

[0045] 3) Add 3.0% monoethanolamine, 1.5% polyether, and 0.5% ricinoleic acid, stir evenly, heat to 50-60°C and react for about 30 minutes;

[0046] 4) Stop heating, and fina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses an environment-friendly reaction type polishing brightener composition and a preparation method and application thereof and belongs to the field of fine chemical engineering. The components of the environment-friendly reaction type polishing brightener composition comprises, by mass, 5%-10% of polishing agent, 3%-6% of alcohol amine, 3%-5% of complexing agent, 1%-4% of surface activating agent, 0.5%-2.0% of brightener, 0.1%-0.5% of thickening agent, 0.5%-2% of corrosion inhibitor, 1%-3% of pickling agent and 75%-85% of water. The environment-friendly reaction type polishing brightener composition prepared is an upgraded replacement product of a traditional brightener, the cleaning and brightening effects on a stainless steel material are obvious, no corrosion is caused to a base material, and the composition is environment-friendly.

Description

technical field [0001] The invention belongs to the field of fine chemicals, and in particular relates to an environment-friendly reactive polishing brightener composition and its preparation method and application. Background technique [0002] Stainless steel has excellent properties such as high corrosion resistance, wear resistance, and easy processing. It is more and more widely used in industries such as automobiles, motorcycles, daily hardware, construction, and road guardrails. In recent years, the application of stainless steel has been increasing rapidly, but there is often a layer of gray oxide film or burrs on the surface, which affects the quality of the product. Therefore, polishing the surface of stainless steel is the most commonly used treatment process for stainless steel products. [0003] The brightener acts on the surface of the workpiece to cause microscopic plastic deformation, thereby reducing the surface roughness; the brightener acts on the surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C23F3/06C23G1/08
CPCC23F3/06C23G1/088
Inventor 王涛邴智武
Owner 广东锴力环保新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap