High-extension, high-adhesion and high-self-healing double network hydrogel and preparation method and application thereof

A hydrogel and double network technology, applied in general culture methods, biochemical equipment and methods, applications, etc., can solve problems such as poor mechanical properties, cytotoxicity, and small pore size, and achieve high stretchability and high viscosity Effect

Active Publication Date: 2019-09-17
DALIAN UNIV OF TECH
View PDF2 Cites 35 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, most traditional hydrogels are composed of permanent covalent bonds or long-term stable strong physical bonds, and their mechanical characteristics are mainly elastic, so there are still many problems in tissue engineering applications: 1) Covalent bonds or long-term stable strong physical bonds The pore size of the cross-linked gel network is small, which makes the mass transfer efficiency of the cells inside the gel low and tends to apoptosis; 2) The chemically cross-linked hydrogel network area is rigid, so it can be used as a three-dimensional extracellular matrix for three-dimensional cell culture 3) Traditional hydrogels do not form adhesion to the contacting tissue/matrix surface due to the hydrophilic surface, so they are usually used to avoid Non-specific adso

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-extension, high-adhesion and high-self-healing double network hydrogel and preparation method and application thereof
  • High-extension, high-adhesion and high-self-healing double network hydrogel and preparation method and application thereof
  • High-extension, high-adhesion and high-self-healing double network hydrogel and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0056] In this example, polyethylene glycol diacrylate (PEGDA) was prepared by a one-step method. 35 g of polyethylene glycol (PEG) with a molecular weight of 35 kDa was dissolved in 80 mL of anhydrous dichloromethane, and 0.74 mL of triethylamine and 1 mL of acryloyl chloride was reacted at room temperature for 24 hours. After the reaction, the impurities were washed with anhydrous magnesium carbonate solution, extracted and separated, precipitated in ether, and then freeze-dried to obtain polyethylene glycol diacrylate with a molecular weight of 35 kDa. Carry out hydrogen NMR spectrum analysis to polyethylene glycol diacrylate ( figure 1 a) It can be seen that a double bond characteristic peak has appeared at 5.80ppm, and infrared spectroscopic analysis ( figure 1 b) at 1730cm -1 The peak corresponding to the C=O bond indicates the successful grafting of acrylate on the polyethylene glycol, and the unreacted polyethylene glycol content and the double bond peak area are det...

Embodiment 2

[0069] According to the data calculated in Example 1, polyethylene glycol with a molecular weight of 35 kDa is selected as the physical network, and 35 kDa is higher than the critical molecular weight of polyethylene glycol.

[0070] Dissolve 0.4 g of polyethylene glycol diacrylate with a molecular weight of 35 kDa and 0.4 g of polyethylene glycol with a molecular weight of 35 kDa in 1 mL of deionized water, and add 0.005 g of 2-hydroxy-4′-(2-hydroxyethoxy Base)-2-methylpropiophenone was mixed at 60° C. for 30 min to form a homogeneous solution to obtain a pre-polymerization solution (pre-polymerization liquid) of a double network hydrogel. Put the pre-polymerization solution at 365nm, 50mw / cm 2 The double network hydrogel was cross-linked under ultraviolet light for 30s, and its viscoelastic data, self-healing efficiency and lap bonding strength are listed in Table 3. Freeze the double-network hydrogel in the -80°C refrigerator for 1 hour and take it out. The cross-section o...

Embodiment 3

[0072] According to the data calculated in Example 1, polyethylene glycol with a molecular weight of 35 kDa is selected as the physical network, and 35 kDa is higher than the critical molecular weight of polyethylene glycol.

[0073] Dissolve 0.4 g of polyethylene glycol diacrylate with a molecular weight of 35 kDa in 1 mL of deionized water, and add 0.005 g of 2-hydroxy-4′-(2-hydroxyethoxy)-2-methylpropiophenone at 60 °C for 30 min to form a uniform solution to obtain a polyethylene glycol diacrylate hydrogel pre-polymerization solution (pre-polymerization solution). Put the pre-polymerization solution at 365nm, 50mW / cm 2 Crosslink under ultraviolet light for 30s to obtain polyethylene glycol diacrylate hydrogel. Dissolve 4 g of polyethylene glycol with a molecular weight of 35 kDa in 10 mL of aqueous solution to obtain a uniform polyethylene glycol solution. The acrylate hydrogel was soaked in polyethylene glycol solution for 24 hours until the polyethylene glycol molecules...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Storage modulusaaaaaaaaaa
Loss modulusaaaaaaaaaa
Adhesive strengthaaaaaaaaaa
Login to view more

Abstract

The invention provides a a design strategy of a novel adhesive hydrogel material and obtains a high-extension, self-healing, and high-adhesion biocompatible hydrogel material. Based on a double network structure design principle, polymerizable polyethylene glycol-based high polymer constitutes a first covalent crosslinked network, and hydrophilic high polymer with ultra-high molecular weight forms a second noncovalent crosslinked network through entanglement. A mesh size of a first network is larger than a molecular effective size of second network high polymer, and molecular weigh of high polymer forming a second network should be larger than a critical entanglement molecular weight thereof, so that effective molecular entanglement is formed, high-extension, self-healing, and high-adhesion characteristics are given to double network hydrogel. The novel hydrogel can rapidly and repeatedly form stable adhesion with surfaces of various materials. Damaged by an external force, the hydrogel can rapidly and repeatedly perform self healing. The material can be used as a cell cultivating carrier, a sewing-free novel dressing, and can be applied to wearble sensors.

Description

technical field [0001] The invention relates to the technical field of biomedical materials, in particular to a high-stretch, high-viscosity, self-healing double-network hydrogel for tissue adhesion, a preparation method and application thereof. Background technique [0002] Hydrogel is a cross-linked hydrophilic polymer, which is composed of a porous gel network, rich in water, allowing the exchange of oxygen and nutrient metabolites, and has viscoelastic characteristics similar to human ECM, so it is widely used It can be used as a platform for studying three-dimensional cellular microenvironment and cell interaction, or as a substrate for constructing engineered tissues. However, most traditional hydrogels are composed of permanent covalent bonds or long-term stable strong physical bonds, and their mechanical characteristics are mainly elastic. There are still many problems in tissue engineering applications: 1) Covalent bonds or long-term stable strong physical bonds Th...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08J3/075C08L71/02A61L24/06A61L24/00A61K9/06A61K47/10A61K47/14C12N5/00
CPCA61K9/06A61K47/10A61K47/14A61L24/001A61L24/0031A61L24/0036A61L24/06A61L2400/06C08J3/075C08J2371/02C08J2471/02C12N5/0068C12N2533/30C08L71/02
Inventor 王华楠陈楷文
Owner DALIAN UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products