A kind of preparation method of isotropic graphite material

A graphite material, isotropic technology, applied in chemical instruments and methods, inorganic chemistry, non-metallic elements, etc., can solve the problems of large-area cracking, poor mechanical properties, high porosity, etc., and achieve stable product quality and excellent performance , Improve the effect of compactness

Active Publication Date: 2022-03-04
SHANDONG CHENYANG NEW CARBON MATERIAL CO LTD
View PDF10 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] 1) In practice, it is found that the existing graphite preparation technologies using mesocarbon microspheres as raw materials have large-area cracking in the process of molding and sintering, and the final yield is extremely low
[0005] 2) Poor mechanical properties, high brittleness and high porosity
[0006] 3) The mesophase petroleum pitch fiber can only become flexible and have a certain mechanical strength after non-melting treatment, but the existing gas oxidation technology has the problems of long time consumption and large investment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method of isotropic graphite material
  • A kind of preparation method of isotropic graphite material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] A preparation method of isotropic graphite material, comprising the following steps:

[0039] ①Sieving mesophase carbon microspheres after crushing to obtain mesophase carbon microsphere granulation powders with different particle sizes;

[0040] ②Crush the chopped carbon fiber and pass through a 400-mesh sieve to obtain the chopped carbon fiber granulated powder;

[0041] ③The mesophase carbon microsphere granulation powder and chopped carbon fiber granulation powder with 20wt% particle size of 5-10μm, 35wt% particle size of 20-30μm, and 45wt% particle size of 40-50μm were subjected to liquid phase dispersion method Doping and mixing modification with wet ball milling. The dispersant used in the liquid phase dispersion method is sodium dodecylbenzenesulfonate. When wet ball milling, ball: material: water = 2.5:1:0.8, mesophase carbon microspheres The mass ratio of the granulated powder and the chopped carbon fiber granulated powder is 95:5 to obtain a modified mesopha...

Embodiment 2

[0048] A preparation method of isotropic graphite material, comprising the following steps:

[0049] ①Sieving mesophase carbon microspheres after crushing to obtain mesophase carbon microsphere granulation powders with different particle sizes;

[0050] ②Crush the chopped carbon fiber and pass through a 600-mesh sieve to obtain the chopped carbon fiber granulated powder;

[0051]③ 38wt% of mesophase carbon microsphere granulation powder and chopped carbon fiber granulation powder with particle size of 5-10 μm, 22wt% of particle size of 20-30 μm, and 40wt% of particle size of 40-50 μm were subjected to liquid phase dispersion and Wet ball milling is used for doping and mixing modification. The dispersant used in the liquid phase dispersion method is sodium dodecylbenzenesulfonate. Ball: material: water = 3:1:0.8 during wet ball milling, mesophase carbon microspheres The mass ratio of granular powder and chopped carbon fiber granulated powder is 98:2, obtains modified mesophase...

Embodiment 3

[0058] A preparation method of isotropic graphite material, comprising the following steps:

[0059] ①Sieving mesophase carbon microspheres after crushing to obtain mesophase carbon microsphere granulation powders with different particle sizes;

[0060] ②Crush the chopped carbon fiber and pass through a 500-mesh sieve to obtain chopped carbon fiber granulation powder;

[0061] ③The mesophase carbon microsphere granulation powder and chopped carbon fiber granulation powder with 35wt% particle size of 5-10 μm, 15wt% particle size of 20-30 μm, and 50wt% particle size of 40-50 μm were subjected to liquid phase dispersion and Wet ball milling is used for doping and mixing modification. The dispersant used in the liquid phase dispersion method is sodium dodecylbenzenesulfonate. During wet ball milling, ball: material: water = 2.8:1:0.8, mesophase carbon microspheres The mass ratio of granular powder and chopped carbon fiber granulated powder is 90:10, obtains modified mesophase car...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of an isotropic graphite material, specifically: after doping mesophase carbon microspheres with different particle sizes and chopped carbon fibers, undergoing liquid phase oxidation treatment, and then passing through secondary cold isostatic pressing Compression molding process, followed by carbonization and graphitization. The invention effectively overcomes the problem of low yield caused by product cracking in the existing ink preparation technology using mesocarbon microspheres as raw materials, and also improves the bending strength of graphite materials, improves compactness, reduces resistivity and Open porosity, thereby improving the performance of graphite materials.

Description

technical field [0001] The invention relates to the technical field of graphite materials, in particular to a preparation method of isotropic graphite materials. Background technique [0002] Graphite is an indispensable conductive material and structural material for the development of national economy such as metallurgy, chemical industry, electronics and nuclear industry. It has high thermal conductivity, low thermal expansion coefficient, good flexural strength, compressive strength and chemical stability. The graphite crystal structure is a mixed crystal structure: the atoms on the layer are arranged in a hexagonal grid, the atomic spacing is small, and the bonding force is strong; the spacing between the layers is large, and the bonding force is weak; so its plane direction and perpendicular to the plane direction The difference in properties is relatively large, which is the so-called "anisotropy". However, many special occasions have put forward the requirement of "...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B32/205C04B35/83C04B35/52C04B35/622
CPCC04B35/83C04B35/522C04B35/622C04B2235/602C04B2235/6562C04B2235/6567C04B2235/77C04B2235/96
Inventor 张海霞闫桂林闫萍胡春燕余萍王方丽谭程程
Owner SHANDONG CHENYANG NEW CARBON MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com