Preparation method of biomimetic mineralized collagen membrane in fibers that can promote osteogenic differentiation of cells

A biomimetic mineralization and osteogenic differentiation technology, applied in tissue regeneration, medical science, prostheses, etc., can solve problems such as bionics, achieve good cell adhesion, good biocompatibility, and promote cell osteogenic differentiation

Active Publication Date: 2022-01-07
THE FIRST AFFILIATED HOSPITAL ZHEJIANG UNIV COLLEGE OF MEDICINE +1
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Extrafibrous mineralization can biomime the chemical composition and a small part of the structure of the extracellular matrix of bone tissue, but the materials prepared by this method cannot achieve real biomimesis of the microstructure, formation process and microenvironment of the bone tissue matrix

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of biomimetic mineralized collagen membrane in fibers that can promote osteogenic differentiation of cells
  • Preparation method of biomimetic mineralized collagen membrane in fibers that can promote osteogenic differentiation of cells
  • Preparation method of biomimetic mineralized collagen membrane in fibers that can promote osteogenic differentiation of cells

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0037] The specific method for preparing the type I collagen film of biomimetic mineralization is:

[0038] Dissolve the lyophilized powder of calf epidermis in 0.1mol / L acetic acid solution (pH=2.5) to prepare a 3-5g / L collagen solution, store it at 4°C for 24 hours and use it within three months. Pour the collagen solution into a prefabricated mold and put it into a closed container containing 1% ammonia water. After neutralizing for 4 hours, remove it and put it in a 36-38°C incubator to continue culturing for 20 hours. During this process, the collagen completes self-assembly and becomes Gel-like. In order to stabilize the collagen structure, 0.025% glutaraldehyde was used for cross-linking for 1 h. At this point, the pure collagen gel was prepared. Put the pure collagen gel in the biomimetic mineralization solution and culture it at 37°C for 2 days to 4 days respectively to prepare collagen gels with different degrees of biomimetic mineralization, cool down the collagen ...

Embodiment 1

[0040] (1) The concrete method of synthesizing the biomimetic mineralization liquid containing amorphous calcium phosphate is:

[0041] 8g / L polyacrylic acid was used as a stabilizer for amorphous calcium phosphate, and 400mM glutamic acid solution was used as a remineralization accelerator. At 36°C, use 0.1M disodium hydrogen phosphate aqueous solution with a pH of 9.5±0.1 and 0.2M calcium chloride aqueous solution to make mother liquor; use a 50ml syringe to add calcium chloride aqueous solution at a volume ratio of 1:1 within 30 minutes In the disodium hydrogen phosphate aqueous solution, a magnetic stirrer was used to stir during the reaction, and a 0.1M sodium hydroxide solution was used to control the pH to maintain the interval of 9.5±0.5; so that the final concentration of calcium ions in the prepared biomimetic mineralization solution was 9.0mM , the final concentration of phosphorus ions was 5.0 mM, and the final concentration of glutamic acid was 10 mM. The final c...

Embodiment 2

[0045] (1) The concrete method of synthesizing the biomimetic mineralization liquid containing amorphous calcium phosphate is:

[0046] 9g / L polyacrylic acid was used as a stabilizer for amorphous calcium phosphate, and 400mM glutamic acid solution was used as a remineralization accelerator. At 37.5°C, use 0.17M disodium hydrogen phosphate aqueous solution with a pH of 9.5±0.1 and 0.28M calcium chloride aqueous solution to make mother liquor; use a 50ml syringe to add calcium chloride aqueous solution at a volume ratio of 1:1 within 37 minutes In the disodium hydrogen phosphate aqueous solution, a magnetic stirrer is used to stir during the reaction, and a 0.1M sodium hydroxide solution is used to control the pH to maintain the interval of 9.5±0.5; so that the final concentration of calcium ions in the prepared biomimetic mineralization solution is 10.0mM , the final concentration of phosphorus ions was 6.3 mM, and the final concentration of glutamic acid was 75 mM. The final...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a biomimetic mineralized collagen membrane in fibers that can promote osteogenic differentiation of cells. In the present invention, the preparation of the biomimetic mineralized collagen film in the fiber is specifically as follows: configure the collagen solution; pour the collagen solution into a prefabricated mold and put it into a closed container containing ammonia water, remove it after neutralization and put it into a constant temperature box to continue culturing, and complete the automatic Assemble and become a gel; cross-link the gel to obtain a pure collagen gel; place the pure collagen gel in a biomimetic mineralization solution for several days to obtain collagen gels with different degrees of biomimetic mineralization ; The collagen gel is cooled, and freeze-dried in a freeze dryer to obtain the final biomimetic mineralized collagen film in the fiber. The biomimetic mineralization of the present invention can form the intrafiber mineralization of collagen fibers, and retain and utilize the fiber network structure of the collagen film while utilizing the mechanical properties and biological properties of the hydroxyapatite crystals.

Description

technical field [0001] The invention relates to a preparation method of a collagen film, in particular to a preparation method of a biomimetic mineralized type I collagen film in fibers that can promote osteogenic differentiation of cells. Background technique [0002] Dental implants have now become a standard and commonly used procedure to restore missing teeth, but the lack of bone in the maxillofacial region due to factors such as trauma, tumors, and periodontal diseases has always been a challenge for oral implants and restorations. Therefore, there are many methods trying to solve this problem, including autologous bone grafting, alveolar ridge splitting and guided bone tissue regeneration (GBR) and so on. Among them, GBR is one of the most commonly used methods and is widely used in anterior implants. Bone substitute materials combined with barrier membranes are required in GBR to block the rapidly proliferating epithelium and connective tissue to ensure osteoblast g...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/12A61L27/24A61L27/50
CPCA61L27/12A61L27/24A61L27/50A61L2430/12
Inventor 顾新华王婧茅彩云陈超群孙健
Owner THE FIRST AFFILIATED HOSPITAL ZHEJIANG UNIV COLLEGE OF MEDICINE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com