Dicyandiamide black slag resource utilization treatment process
A treatment process and technology of dicyandiamide, applied in the direction of carbide, calcium carbide, calcium/strontium/barium oxide/hydroxide, etc., can solve problems such as consumption, decrease in output of cement and non-sintered bricks, etc.
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0028] A dicyandiamide black slag resource utilization treatment process, the main scheme of which is:
[0029] According to the number of parts by mass, dry 1000kg of dicyandiamide black slag in the drying equipment until the moisture content is 0.8%, and the temperature is 80°C, then sieve the waste slag with a 150-mesh standard sieve, and keep the undersieve, and sieve The coarse slag is separated and enters the winnowing equipment, and the air volume of winnowing is controlled to be 62.1m 3 / h, collect the settled waste slag and combine it with the sieve; then add 6% binder and 5% quality improving agent to the obtained waste slag, mix it evenly and mold it under 8MPa, then place the formed waste slag in 800 ℃, carbonization at an atmosphere pressure of 0.1MPa for 20 hours, drying at 80 ℃ for 30 minutes after completion, and then calcining at 900 ℃ for 120 minutes, and the finished product of activated calcium oxide can be obtained after completion.
[0030] Described bin...
Embodiment 2
[0039] A dicyandiamide black slag resource utilization treatment process, the main scheme of which is:
[0040] According to the number of parts by mass, 1100kg of dicyandiamide black slag is dried in a drying equipment until the moisture content is 1.5%, and the temperature is 90°C, and then the waste residue is sieved with a 200-mesh standard sieve, and the sieved material is retained. The coarse slag is separated and enters the winnowing equipment, and the air volume of winnowing is controlled to be 65.5m 3 / h, collect the settled waste slag and combine it with the sieve; then add 9% binder and 7% quality improving agent to the obtained waste slag, mix it evenly and mold it under 10MPa, then place the formed waste slag in 100 ℃, carbonization under the pressure of 0.5MPa for 15 hours, after completion, dry at 100 ℃ for 45 minutes, and then calcinate at 960 ℃ for 180 minutes, and the finished product of activated calcium oxide can be obtained after completion.
[0041] Desc...
Embodiment 3
[0050] A dicyandiamide black slag resource utilization treatment process, the main scheme of which is:
[0051] According to the number of parts by mass, dry 1200kg of dicyandiamide black slag in the drying equipment until the moisture content is 2.3%, and the temperature is 100°C, then sieve the waste slag with a 250-mesh standard sieve, and keep the undersieve, and sieve The coarse slag is separated and enters the winnowing equipment, and the air volume of winnowing is controlled to be 68.7m 3 / h, collect the settled waste slag and combine it with the sieve; then add 11% binder and 8% quality improving agent to the obtained waste slag, mix well and mold it under 13MPa, then place the formed waste slag at 120 ℃, carbonization under the pressure of 1 MPa for 10 hours, after completion, dry at 120 ℃ for 60 minutes, and then calcinate at 980 ℃ for 240 minutes, and the finished product of activated calcium oxide can be obtained after completion.
[0052] Described binder is a ki...
PUM
Property | Measurement | Unit |
---|---|---|
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
diameter | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com