A kind of bone tissue repair material and preparation method and application thereof

A technology for repairing materials and bone tissue, which is applied in the field of bone tissue repairing materials and their preparation, can solve the problems of high partial or complete shedding of mineralized silk protein particles, single product obtaining method, non-constant temperature, etc., and achieves low requirements for reaction equipment, Avoid scattering or leaking, the effect of the method is simple

Active Publication Date: 2022-07-01
HUBEI SAILUO BIOLOGICAL MATERIAL CO LTD
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The Chinese patent "Mineralized Silk Protein Material and Its Preparation Method" (publication number CN1241654A) discloses a mineralized silk protein material and its preparation method, wherein the organic component is degummed silk protein, and the minerals are calcium phosphorus salt crystals. The specific method It is to add calcium ion-containing solution and phosphate ion-containing solution to the water-soluble degummed silk protein solution under stirring, adjust the pH value of the reaction system, keep stirring for a while, let the system stand still, repeat centrifugation, wash the precipitate, and then put Precipitation is vacuum-dried to obtain the product; the system has the problems of non-constant temperature, large capacity, pH deviation from the most stable value of hydroxyapatite, and a single method for obtaining the product
At the same time, there is a higher risk of partial or complete detachment of fine mineralized silk protein particles from the bone graft during use

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of bone tissue repair material and preparation method and application thereof
  • A kind of bone tissue repair material and preparation method and application thereof
  • A kind of bone tissue repair material and preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0033] The preparation method of the bone tissue repair material provided by the present invention comprises the following steps:

[0034] (1) In the liquid phase system of pH=10~12, the soluble calcium salt and soluble phosphate (or phosphoric acid) with the molar ratio of Ca and P of 5:3 undergo in situ co-precipitation reaction on the natural polymer A, and the precipitation reaction occurs. After cleaning, drying, grinding and sieving, the hydroxyapatite-natural polymer A nanocomposite particles of different specifications are formed;

[0035] (2) The hydroxyapatite-natural polymer A nanocomposite particles and the natural polymer B are uniformly mixed in a liquid phase system, then placed in a mold for vacuum freeze-drying, and then soaked and dried in absolute ethanol to obtain Bone tissue repair material with fixed morphology;

[0036] Among them, the natural polymer A and the natural polymer B are the same or different.

[0037] Specifically include the following ste...

Embodiment 1

[0049] (1) Weigh 75.3 g of soluble silk fibroin, put it into 3L of purified water at a constant temperature of 40°C, and dissolve for 10 minutes under stirring at 150-1500 rpm to obtain a silk fibroin solution.

[0050] (2) Weigh 342.1 g of trisodium phosphate dodecahydrate, put it into the silk fibroin solution obtained in step (1) at one time, stir at 150 to 1500 rpm until the solution is clear, put in 354.2 g of calcium nitrate tetrahydrate at one time, and continue to stir;

[0051] (3) after a large amount of milky white precipitation appears in the reaction system, add 1.5L of concentrated ammonia water (NH 3 The concentration is 25-28 wt%), ensure that the pH value of the system is about 11, and stir for 3 hours to make it fully react.

[0052] (4) After the completion of the reaction, the stirring was stopped, and the reaction product was aged for 20 hours at a constant temperature of 40°C in the reaction vessel.

[0053] (5) Pour out the aged reaction product.

[0...

Embodiment 2

[0062] (1) Weigh 60.5 g of soluble silk fibroin, put it into 3 L of purified water at a constant temperature of 37°C, and dissolve for 10 minutes under stirring at 1000 rpm to obtain a silk fibroin solution.

[0063] (2) put 342.1g potassium dihydrogen phosphate into the silk fibroin solution prepared in step (2) at one time, stir at a rotating speed of 500~1000rpm until the solution is clear, and then put 354.2g anhydrous calcium chloride into it at one time, Continue to stir the reaction.

[0064] (3) After a large amount of milky white precipitation appears in the reaction system, sodium hydroxide solution (concentration is 3M) is added in batches to ensure that the pH value of the system is about 11, and the stirring is continued for 3 hours to make it fully react.

[0065] (4) After the reaction is completed, the stirring is stopped, and the reaction product is aged for 16 hours under the constant temperature condition of 37°C in the reaction vessel.

[0066] (5) Pour ou...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
densityaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a bone tissue repair material and a preparation method and application thereof. In a liquid phase system of pH=10-12, a soluble calcium salt with a molar ratio of Ca to P of 5:3 and a soluble phosphate or phosphoric acid are naturally An in-situ co-precipitation reaction occurs on the polymer A, and the precipitate is dried and ground to form hydroxyapatite-natural polymer A nanocomposite particles; the hydroxyapatite-natural polymer A nanocomposite particles are mixed with natural high The solution of molecule B is evenly mixed and then placed in a mold for vacuum freeze drying, and then soaked in absolute ethanol and dried to obtain a bone tissue repair material. The bone tissue repair material is loose and porous, hydroxyapatite is not easily leaked from the bone tissue repair material, has good water absorption, is soft and elastic after water absorption, and can be used for common bone defects in oral implantology, prosthodontics, orthopedics and other surgeries Repair; the preparation method is easy to operate, easy to automate, clean reagents, and low cost.

Description

technical field [0001] The invention relates to the field of bone tissue engineering materials, in particular to a bone tissue repair material and a preparation method and application thereof. Background technique [0002] At present, bone tissue substitute materials are a hot spot in the research and application of biomedical materials due to the huge market demand. Endogenous bone tissue repair has a good effect, but the popularization of this therapy is limited due to the shortage of alternative material sources; while exogenous bone tissue repair has obvious immune rejection, and may also introduce potential pathogens and other toxic side effects. It can be seen that it is of great practical significance to study and prepare an efficient and safe artificial bionic bone tissue replacement material. [0003] Natural bone tissue is a uniform and ordered biological complex composed of inorganic minerals (mainly nano-hydroxyapatite) and natural macromolecules (mainly collage...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A61L27/46C01B25/32A61L27/56
CPCC01B25/325A61L27/46A61L27/56C01P2002/72C01P2004/03C01P2006/10C01P2006/17A61L2430/02A61L2430/12
Inventor 邓红兵蒋朝俊
Owner HUBEI SAILUO BIOLOGICAL MATERIAL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com