Solar glass panel with honeycomb colored tempered coating and production method thereof, colored solar photovoltaic module

A technology of solar glass and production method, applied in the field of solar photovoltaic, can solve the problems of unsuitable glass outer surface of photovoltaic modules, no practical application value, low light transmittance of inorganic coatings, etc., so as to reduce the probability of burning photovoltaic modules, Excellent outdoor weather resistance, the effect of broadening the range of color choices

Active Publication Date: 2022-06-07
杭州玻美文化艺术有限公司
View PDF12 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The disadvantage of low-temperature color coating is that the hardness of the coating is low, the weather resistance is poor, and the friction resistance is poor. It cannot be used on the outer surface of the glass of photovoltaic modules. surface decoration
[0010] Traditional high-temperature tempered glass coatings are mainly composed of inorganic pigments and glass fluxes, both of which are inorganic components, with outstanding advantages and obvious disadvantages
The advantages are strong hiding power, good weather resistance, good decoration, the same high hardness as tempered glass, the surface coating cannot be scraped off by a knife, and excellent impact resistance. It is suitable for the outer surface decoration of photovoltaic glass and can withstand wind, sand and The impact of objects such as hail; the disadvantage is that the light transmittance of the inorganic coating is very low, and some tempered coatings are not transparent at all, and the light transmittance is only a few percent at the highest. When used for the decoration of colored solar glass panels, the photoelectricity of photovoltaic modules Conversion efficiency is almost zero, no practical application value

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Solar glass panel with honeycomb colored tempered coating and production method thereof, colored solar photovoltaic module
  • Solar glass panel with honeycomb colored tempered coating and production method thereof, colored solar photovoltaic module
  • Solar glass panel with honeycomb colored tempered coating and production method thereof, colored solar photovoltaic module

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0061] Golden honeycomb tempered UV coating formula (raw material mass percentage):

[0062]

[0063]

[0064] The B-3310 and IBOA in the above formula are stirred and dissolved into a uniform liquid at 60-80 ° C, mixed with the remaining components to obtain a color UV coating, and the above UV coating is printed with a 200-mesh screen to obtain a thickness of 20. Micron color coating; UV light curing, irradiating energy 600 mJ / cm2; green laser with a wavelength of 532 nm and a power of 10 watts, punched at an angle of 45 degrees to the glass, the aperture is 15 microns, and the area of ​​the hole and the coating is 15 microns. The ratio is 10%; the perforated glass is directly sent to a tempering furnace for tempering (780-820° C. / 220 seconds), that is, a golden honeycomb tempered glass coating is obtained. When viewed from a distance, it is a golden glass with uniform color. When viewed from a distance, there are many oblique light-transmitting small holes distributed...

Embodiment 2

[0066] Blue honeycomb tempered UV coating formula (raw material mass percentage):

[0067]

[0068] The B-3131 polymer and HDDA in the above formula are stirred and dissolved into a uniform liquid at 60-80 ° C, mixed with the remaining components to obtain a color UV coating, and the above UV coating is printed with a 200-mesh screen to obtain a 18 microns thick blue coating. The UV light curing energy is 1100 mJ / cm 2 , and a green laser with a wavelength of 532 nm and a power of 10 watts is used to make holes at an angle of 45 degrees to the glass, the aperture is 15 microns, and the ratio of the hole to the coating area is 20%. The glass is directly sent to the tempering furnace for tempering (780-820 ℃ / 220 seconds), that is, the blue honeycomb tempered glass coating is obtained, which is uniform blue glass when viewed from a distance, and there are many oblique light transmittances distributed on the surface when viewed from a close distance. Small holes, measurement of...

Embodiment 3

[0070] White honeycomb tempered UV coating formula (raw material mass percentage):

[0071]

[0072] The B-3131 polymer and IBOMA in the above formula are stirred and dissolved into a uniform liquid at 60-80 ° C, and mixed with the other components to obtain a color UV coating; 200 mesh screen The above UV coating is obtained with a thickness of 20 microns Color coating. UV light curing, irradiation energy 1500 mJ / cm2. A green laser with a wavelength of 532 nanometers and a power of 10 watts was used to drill holes at a 45-degree angle to the glass, with a hole diameter of 15 microns and a ratio of the hole to the coating area of ​​25%. The perforated glass is directly sent to the tempering furnace for tempering (780-820°C / 220 seconds), that is, a white honeycomb colored tempered glass panel is obtained, which is a white glass with uniform color when viewed from a distance. For the light transmission holes, the physical and chemical indicators such as light transmittance ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
acid valueaaaaaaaaaa
glass transition temperatureaaaaaaaaaa
densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses a solar glass panel with a honeycomb colored tempered coating, a production method thereof, and a colored solar photovoltaic module. The production method includes the following steps: coating a UV colored tempered coating on the photovoltaic glass panel, and coating the photovoltaic glass The panel is preheated; after preheating, the UV color tempered coating is irradiated with ultraviolet light; the laser beam is used to obliquely punch or scribe the UV color tempered coating after the initial curing, so that the UV color tempered coating forms a honeycomb structure; Carry out high-temperature tempering to the UV color tempered coating after punching to form a solar glass panel with a honeycomb color tempered coating; in terms of mass percentage of raw materials, the UV color tempered coating includes: thermoplastic polymer 8‑25% ; Low-viscosity photoactive diluent 10-25%; Photosensitizer 1-3%; Transparent glass flux 50-65%; Inorganic pigment 0.1-15%; Leveling agent 0.01-3%. The coating of the solar glass panel of the invention has excellent impact resistance and high light transmittance.

Description

technical field [0001] The invention relates to the field of solar photovoltaic, in particular to a solar glass panel with a honeycomb colored tempered coating, a production method thereof, and a colored solar photovoltaic assembly. Background technique [0002] Vigorously developing solar photovoltaic power generation is one of the important paths to reduce carbon emissions and achieve carbon neutrality. [0003] Silicon solar photovoltaic cells dominate the market. The traditional structure of silicon solar photovoltaic cells is composed of photovoltaic glass, photovoltaic film, monocrystalline silicon or polycrystalline silicon solar cells, photovoltaic film and photovoltaic backplane from the outside to the inside, and is fixed by an aluminum alloy frame. [0004] Since monocrystalline or polycrystalline silicon solar cells are dark blue or black, silicon crystalline solar photovoltaic cells are also dark. [0005] Distributed solar energy is mainly installed on the ro...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L31/0216C09D4/06C09D4/02C09D5/36C03C17/00C03C17/32
CPCC09D4/06C09D5/36C03C17/009C03C17/32H01L31/02168Y02E10/50
Inventor 何平
Owner 杭州玻美文化艺术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com