Modified vinyl ester resin and preparation method thereof, toughened modified vinyl ester resin with good air-drying property, preparation method and application thereof

A vinyl ester resin, toughening modification technology, applied in the field of vinyl ester resin and its preparation, to achieve the effects of improving air-drying property, increasing molecular weight, and accelerating the overall reaction rate

Active Publication Date: 2022-01-21
SOUTH CHINA AGRI UNIV +1
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There is still a lack of a vinyl ester resin with good toughness and air-drying properties in the prior art

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modified vinyl ester resin and preparation method thereof, toughened modified vinyl ester resin with good air-drying property, preparation method and application thereof
  • Modified vinyl ester resin and preparation method thereof, toughened modified vinyl ester resin with good air-drying property, preparation method and application thereof
  • Modified vinyl ester resin and preparation method thereof, toughened modified vinyl ester resin with good air-drying property, preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] The preparation method of the modified vinyl ester resin of the present embodiment may further comprise the steps:

[0032] In the reactor, drop into 47g bisphenol A type epoxy resin E-44 (epoxy equivalent 227.27), 16g acrylic acid, the polymerization inhibitor hydroquinone of raw material gross mass 0.028%, stir at 45 ℃, then slowly Drop into 7g toluene diisocyanate, the catalyst dibutyltin dilaurate of 0.1% of raw material gross mass, be heated up to 70 ℃ and react, react 2h, add the catalyst benzyltriethylammonium chloride of raw raw material gross mass 0.6% afterwards, and heat up to React at 110°C until the acid value drops below 15mgKOH / g, then lower the temperature to 80°C, add 30g of active diluent styrene, until the mixture is uniform, and a light yellow transparent vinyl ester resin is obtained.

[0033] The Nicolet iS10 Fourier Transform Infrared Spectrometer of Thermo Fisher was used to monitor and analyze the functional groups in real time during the synthe...

Embodiment 2

[0036] The preparation method of the modified vinyl ester resin of the present embodiment may further comprise the steps:

[0037] (1) In the reactor, drop into 49g bisphenol A type epoxy resin E-44 (epoxy equivalent 227.27), 15g acrylic acid, the polymerization inhibitor hydroquinone of raw material gross mass 0.028%, stir at 45 ℃ , then slowly drop into 5g toluene diisocyanate, catalyzer dibutyltin dilaurate of 0.1% of the total mass of raw materials, be warming up to 70°C for reaction, react for 2h, then add benzyltriethylammonium chloride and benzyltriethylammonium chloride of 0.6% of the total mass of raw materials 1g of fumaric acid, stir until fully dissolved, heat up to 110°C for reaction until the acid value drops below 15mgKOH / g, then lower the temperature to 80°C, add 30g of reactive diluent styrene, until the mixture is uniform, and a light yellow color is obtained Transparent vinyl ester resin.

[0038] The same analysis method as in Example 1 was used to monitor a...

Embodiment 3

[0040] The preparation method of the toughened and modified vinyl ester resin with good air-drying property of the present embodiment comprises the following steps:

[0041] (1) Under the environment of nitrogen protection, drop into 30g of toluene diisocyanate and 45g of castor oil in the reactor and mix evenly, heat up to 45°C for 3h, then add 25g of hydroxyethyl acrylate, 0.1% of the total mass of raw materials Catalyst II Dibutyltin laurate and 0.1% of the total mass of raw materials as a polymerization inhibitor hydroquinone were heated up to 78° C. for 4 hours and stirred evenly to obtain a clear and transparent castor oil-based urethane acrylate resin.

[0042] (2) In another reactor, drop into 47g bisphenol A type epoxy resin E-44 (epoxy equivalent 227.27), 16g acrylic acid, the stopper hydroquinone of raw material gross mass 0.028%, at 45 ℃ Stir evenly, then slowly add 7g of toluene diisocyanate, a catalyst of 0.1% of the total mass of raw materials, dibutyltin dilaur...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
Login to View More

Abstract

The invention belongs to the technical field of polymer materials, and in particular relates to a modified vinyl ester resin and a preparation method thereof, a toughened modified vinyl ester resin with good air-drying property, a preparation method and application thereof. In the present invention, after the epoxy resin and the diisocyanate are chain-extended under the catalyst, the unsaturated monobasic acid is used to react with the epoxy group, and after the reaction is completed, an active diluent is added to obtain the modified vinyl ester resin; the vegetable oil-based oligomer and The modified vinyl ester resin is mixed in proportion to obtain a toughened modified vinyl ester resin with good air-drying properties. The modified vinyl ester resin and the toughened and modified vinyl ester resin with good air-drying properties not only have good air-drying properties and fast curing speed, but also have excellent mechanical properties and corrosion resistance.

Description

technical field [0001] The invention belongs to the technical field of polymer materials, and in particular relates to a modified vinyl ester resin and a preparation method thereof, a toughened modified vinyl ester resin with good air-drying property, a preparation method and an application thereof. Background technique [0002] Vinyl ester resin is usually obtained by ring-opening addition reaction of epoxy resin and monobasic unsaturated carboxylic acid, and then dissolved in unsaturated active monomer. From the structural point of view, since the double bond participating in free radical curing is located at the end of the molecular chain segment, its curing activity is high and it is easy to form a mold; secondly, the commonly used epoxy resin has a bisphenol A structure, and the main chain has more rigidity. Benzene ring structure, so its cured film has high tensile strength. However, the vinyl ester resin prepared by the above method has brittleness problems, low elon...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08G59/17C08G18/58C08L63/10C08L75/14C08L91/00
CPCC08G59/1466C08G18/58C08L63/10C08L75/14C08L91/00
Inventor 杨卓鸿李贵东方亨杨绍恒吴海华
Owner SOUTH CHINA AGRI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com