A concrete release agent, high stability technology, applied in lubricating compositions, petroleum industry and other directions, can solve the problems of difficulty in cleaning the release agent, small application area, time-consuming and labor-intensive, etc., to improve the release effect, prolong the Service life, the effect of solving environmental pollution problems

Inactive Publication Date: 2021-12-31
湖南加美乐素新材料股份有限公司
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It is difficult to clean the release agent, and a special solvent must be used, which is time-consuming and labor-intensive;
[0007] Resin: The mold release agent made of methyl silicone resin, unsaturated polyester resin, epoxy resin and solvent has good mold release effect and can be reused many times, but it is expensive, toxic, and difficult to clean, etc. Disadvantages, it is not widely used in China

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A high-stable concrete mold release agent, made of the following components in weight percentage: 30% of oil raw materials, 2% of emulsifier, 1% of auxiliary agent, 0.2% of stabilizer, 0.1% of high molecular polymer, water quantity.

[0041] Among them, the oil raw material is vegetable oil, specifically rapeseed oil; the emulsifier is a combination of sodium dodecylbenzenesulfonate and polyoxyethylene octylphenol ether; the auxiliary agent is triethanolamine, antifreeze, and defoamer; The stabilizer is a combination of sodium polyphosphate and xanthan gum; the high molecular polymer is polyacrylamide.

[0042] A kind of preparation method of high stability concrete release agent, comprises the steps:

[0043] (1) Weigh the oil raw material by weight percentage, adjust the pH value of the oil raw material to 4 with an acid-base reagent, raise the temperature to 50°C, add sliding substances, stir for 1h, then cool down to react below 35°C, and filter through the filter ...

Embodiment 2

[0048] A high-stable concrete release agent, made of the following components by weight: 35% oily raw material, 3% emulsifier, 2% auxiliary agent, 0.4% stabilizer, 0.2% high molecular polymer, water residue quantity.

[0049] Among them, the oil raw material is waste oil; the emulsifier is a combination of Span and Tween; the auxiliary agent is sodium borate; the stabilizer is hydroxymethyl cellulose and carboxymethyl cellulose sodium; diol.

[0050] A kind of preparation method of high stability concrete release agent, comprises the steps:

[0051] (1) Weigh the oil raw material according to the weight percentage, adjust the pH value of the oil raw material to 5 with an acid-base reagent, raise the temperature to 60°C, add sliding substances, stir for 1.5h, then cool down and react to below 35°C, pass through the filter device Filter out impurities to obtain an oily solution;

[0052] (2) Weigh the emulsifier and a small amount of water according to weight percentage, mix ...

Embodiment 3

[0056] A high-stable concrete release agent, made of the following components in weight percentage: 38% of oil raw materials, 4% of emulsifier, 2% of auxiliary agent, 0.7% of stabilizer, 0.2% of high molecular polymer, water residue quantity.

[0057] Among them, the oil raw materials include vegetable oil and waste engine oil; the emulsifier is a combination of sodium dodecylbenzenesulfonate, Span, and Tween; the auxiliary agent is triethanolamine, antifreeze, and defoamer; the stabilizer is polymer Sodium phosphate, methylcellulose and sodium carboxymethylcellulose; polymers are polyacrylamide and polyethylene glycol.

[0058] A kind of preparation method of high stability concrete release agent, comprises the steps:

[0059] (1) Weigh the oil raw material according to the weight percentage, adjust the pH value of the oil raw material to 5 with an acid-base reagent, raise the temperature to 70°C, add sliding substances, stir for 1.5h, then cool down and react to below 35°C, p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-stability concrete release agent which is prepared from the following components in percentage by weight: 30-40% of an oil raw material, 2-5% of an emulsifier, 1-3% of an auxiliary agent, 0.2-1% of a stabilizer, 0.1-0.3% of a high-molecular polymer and the balance of water. Vegetable oil or waste grease is adopted as base oil, the waste grease is a mixture of vegetable oil and animal oil, both the vegetable oil and the waste grease are renewable substances, and in addition, the problem of environmental pollution can be further solved by adopting the waste grease. The emulsifier added in the concrete release agent has efficient stability, the added triethanolamine can effectively prevent rust, and the added high-molecular polymer can improve the release effect. The concrete release agent has the advantages of being environmentally friendly, high in stability and capable of being repeatedly used after being applied once. Moreover, the surface strength of concrete can be improved, the weather resistance of concrete is effectively improved, and the service life of a concrete member is prolonged.

Description

technical field [0001] The invention relates to the technical field of construction engineering, in particular to a high-stability concrete release agent. Background technique [0002] Concrete release agent, also known as concrete release agent or release lubricant, is a kind of coating or spraying on the inner surface of the formwork, which can produce a layer of isolation film to lubricate and isolate, and can effectively reduce the adhesion between concrete and formwork The substance or material that enables the concrete to be demoulded smoothly when the formwork is removed, and keeps the shape of the concrete intact and clean. [0003] With the rapid development of concrete, the use of concrete release agents is becoming more and more extensive. At present, there are many types of concrete on the market. Different types of release agents have different effects on the release between concrete and formwork. Release agents The main types are as follows: [0004] Emulsifi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C10M173/00C10N40/36
CPCC10M173/00C10M2207/401C10M2219/044C10M2209/104C10M2209/108C10M2215/06C10M2201/085C10M2217/024C10M2209/12C10M2209/103C10M2207/283C10M2209/109C10M2201/087C10M2209/04
Inventor 王伟龙威
Owner 湖南加美乐素新材料股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap