High-performance chlorinated polyvinyl chloride plastic

A technology of chlorinated polyvinyl chloride and polyvinyl chloride, which is applied to the physical and chemical parameters of materials and the field of modified plastics of chlorinated polyvinyl chloride, can solve the problems of high low-temperature brittleness, increased processing difficulty, and poor impact resistance, and achieves High impact strength, good physical and chemical properties, good chemical stability

Inactive Publication Date: 2002-01-23
张小文
View PDF0 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, its disadvantage is that its melt viscosity is at least twice that of polyvinyl chloride, which increases the friction between it and processing equipment, and the friction heat generated increases. Due to thermal decomposition, a large amount of hydrogen chloride gas is produced, which makes processing and molding difficult. And seriously corrode the proc

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Embodiment 1: Vicat softening reaches 120 ℃ component (weight ratio)

[0043] Chlorinated polyvinyl chloride 100

[0044] Polyvinyl chloride 11.1

[0045] Lead complex with lubrication system 8.89

[0046] Methacrylate impact modifier 8.89

[0047] Partially oxidized polyethylene wax 0.02

[0048] Active light CaCo 3 3.33 The above components are made into pipes through the following process:

[0049] Component raw materials→high-speed mixing→low-speed cold mixing→extrusion by twin-screw extruder→head mold forming→vacuum cooling and shaping→spray cooling→traction→cutting to length→flaring→inspection→packing and storage.

[0050] Its process parameters are:

[0051] 1. Temperature control range (°C):

[0052] 1. High speed mixing 110~130

[0053] 2. Low speed cold mixing 40~50

[0054] 3. Twin-screw extruder barrel:

[0055](I) District 180~205

[0056] (II) District 175~200

[0057] (III) District 170~195

[0058] (IV) District 170~195

[0059] ...

Embodiment 2

[0074] Embodiment 2: Vicat softening point is 110 ℃ of components (weight ratio)

[0075] Chlorinated polyvinyl chloride 100

[0076] PVC 25

[0077] Lead complex with lubrication system 7.75

[0078] Methacrylate Impact Modifier 10

[0079] Partially oxidized polyethylene wax 0.375

[0080] Active light CaCo 3 12.5

[0081] Other process flow and process parameter control are identical to embodiment 1.

Embodiment 3

[0082] Embodiment 3: Vicat softening point is 105 ℃ of components (weight ratio)

[0083] Chlorinated polyvinyl chloride 100

[0084] PVC 50

[0085] Lead complex with lubrication system 12.8

[0086] Methacrylate Impact Modifier 12

[0087] Partially oxidized polyethylene wax 0.9

[0088] Active light CaCo 3 46 Other process flow and process parameter control are identical to embodiment 1.

[0089] Generally speaking, when the ratio of polyvinyl chloride increases the temperature of its Vicat softening point and reduces, but the physicochemical index of its product can reach impact strength (KJ / m 2 )≥12, Vicat softening point (°C) 90-120, oxygen index (%) 50-60.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Vicat softening pointaaaaaaaaaa
Vicat softening pointaaaaaaaaaa
Login to view more

Abstract

The present invention relates to a polymer material, modified chlorinated polyvinyl chloride plastic. It consists of in weight ratio chlorinated polyvinyl chloride 100, polyvinyl chloride 2-160, composite lead stabilizer 4-12, methyl acrylate as shock modifier 2-14, partially oxidized polyethylene wax 0.05-0.9, active light CaCO3 0.05-80. It has excellent physical and chemical performance including chemical stability, heat resistance, corrosion resistance, fireproofing, shock strength, weather resistance and ultraviolet resistance. In addition, it has relatively lower cost, and may be used widely in producing various plastic products.

Description

technical field [0001] The invention belongs to polymer plastic materials, especially modified plastics of chlorinated polyvinyl chloride, and relates to its composition, process control parameters and physical and chemical parameters of materials. Background technique [0002] In industry, agriculture, mining, communication, electric power, construction, environmental protection and human daily life, the use of plastics and their products has been widely used. For example, plastic pipes are widely used to transport liquids and gases. Plastic pipes have light weight, With the advantages of corrosion resistance and easy installation, its application has been developed rapidly. The current plastics are mainly polyvinyl chloride (PVC), polyethylene (PE), ABS, etc. However, the main defect of polyvinyl chloride is that the heat-resistant temperature is not high, and the long-term working temperature cannot exceed 60°C, and as the temperature increases, its o...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08K5/09C08L27/06C08L27/24
Inventor 张小文
Owner 张小文
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap