Insulative products having bio-based binders

a bio-based, binder-based technology, applied in the direction of synthetic resin layered products, protein coatings, pipes, etc., can solve the problems of inability to use formaldehyde scavengers in general, unstable urea-extended resoles, and inability to meet the needs of workers, etc., to achieve convenient use, low cost, and save time and money

Inactive Publication Date: 2011-09-15
OWENS CORNING INTELLECTUAL CAPITAL LLC
View PDF102 Cites 69 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Benefits of technology

[0013]It is an advantage of the present invention that the carbohydrate is natural in origin and derived from renewable resources.
[0014]It is yet another advantage of the present invention that maltodextrin is readily available and is low in cost.
[0015]It is a further advantage of the present invention that insulation products and non-woven mats utilizing the inventive binder composition can be manufactured using current manufacturing lines, to make a variety of product shapes, densities and uses, thereby saving time and money.
[0016]It is another advantage of the present invention that the binder composition has no add

Problems solved by technology

Unfortunately, the urea-extended resoles are unstable, and because of this instability, the urea-extended resoles must be prepared on site.
In addition, the binder inventory must be carefully monitored to avoid processing problems caused by undesired crystalline precipitates of dimer species that may form during storage Ammonia is not a particularly desirable alternative to urea as a formaldehyde scavenger because ammonia generates an unpleasant odor and may cause throat and nose irritation to workers.
Further, the use of a formaldehyde scavenger in general is undesirable d

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Insulative products having bio-based binders
  • Insulative products having bio-based binders
  • Insulative products having bio-based binders

Examples

Experimental program
Comparison scheme
Effect test

example 1

[0095]The binder formulations set forth in Table 4 were utilized to form handsheets in the manner described in detail below. The nonwoven fiberglass handsheets were dried and cured for three minutes at 400° F. The tensile strength, the Loss on Ignition (LOI), and the tensile strength divided by the LOI (tensile strength / LOI) for each sample was determined under ambient and steam conditions. The tensile strength was measured using Instron. The loss on ignition (LOI) of the reinforcing fibers is the reduction in weight experienced by the fibers after heating them to a temperature sufficient to burn or pyrolyze the organic size from the fibers. The loss on ignition was measured according to the procedure set forth in TAPPI T-1013 OM06, Loss on Ignition of Fiberglass Mats (2006). To place the handsheet in a steam environment, the handsheets were placed in an autoclave at 240° F. at a pressure between 400 and 500 psi for 30 minutes.

[0096]The handsheets were made according to the followin...

example 2

[0099]The binder formulations set forth in Table 6 were utilized to form handsheets according to the procedure set forth in Example 1. The nonwoven fiberglass handsheets were dried and cured for three minutes at 400° F. The tensile strength, the loss on ignition (LOI), and the tensile strength divided by the LOI (tensile strength / LOI) for each sample was determined under ambient and steam conditions. The steam conditions were identical to that set forth in Example 1. In addition, the loss on ignition and tensile strength of each the samples were measured according to the procedures described in Example 1. The results are set forth in Table 7. It is to be noted that the weights in Table 6 are expressed in grams (g).

TABLE 6Sample 1Sample 3Sample 410%20%20%Citric AcidSample 2Citric AcidCitric AcidComponent5% SHPControl5% SHP5% SHPMaltodextrin79.9(DE 11.0)Maltodextrin79.9(DE 18.0)Maltodextrin89.8(DE 7.5)gamma-amino-13.713.713.713.7propyltri-hydroxy-silane (1.24%solution)Citric9.619.219....

example 3

[0101]The binder formulations set forth in Table 8 were utilized to form handsheets according to the procedure set forth in Example 1. The nonwoven fiberglass handsheets were dried and cured for three minutes at 400° F. The tensile strength, the LOI, and the tensile strength / LOI for each sample were determined under ambient and steam conditions. The steam conditions were identical to that set forth in Example 1. In addition, the loss on ignition and tensile strength of each the samples were measured according to the procedures described in Example 1. The results are set forth in Table 9. It is to be noted that the weights in Table 8 are expressed in grams (g).

TABLE 8Sample 270:30Sample 5Sample 1MD-CASample 3Sample 470:3070:30w / 5% SHP70:3070:30MD-CAMD-CAand 10%MD-CAMD-CAw / 3% Li-Componentw / 5% SHPH3PO4w / 4% H3PO2w / 5% AlCl3CarboxylateMaltodextrin45.142.646.045.152.0(DE 11.0)Citric Acid19.314.219.219.323.3gamma-10.211.210.310.211.5aminopropyl-trihydroxy-silane (1.24%solution)Catalyst4.14....

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Fractionaaaaaaaaaa
Fractionaaaaaaaaaa
Fractionaaaaaaaaaa
Login to view more

Abstract

Fibrous insulation products have an aqueous binder composition that includes a carbohydrate and a crosslinking agent. In exemplary embodiments, the carbohydrate-based binder composition may also include a catalyst, a coupling agent, a process aid, a crosslinking density enhancer, an extender, a moisture resistant agent, a dedusting oil, a colorant, a corrosion inhibitor, a surfactant, a pH adjuster, and combinations thereof. The carbohydrate may be natural in origin and derived from renewable resources. Additionally, the carbohydrate polymer may have a dextrose equivalent (DE) number from 2 to 20. In at least one exemplary embodiment, the carbohydrate is a water-soluble polysaccharide such as dextrin or maltodextrin and the crosslinking agent is citric acid. Advantageously, the carbohydrates have a low viscosity and cure at moderate temperatures. The environmentally friendly, formaldehyde-free binder may be used in the formation of insulation materials and non-woven chopped strand mats. A method of making fibrous insulation products is also provided.

Description

CROSS REFERENCE TO RELATED APPLICATIONS[0001]This application is a continuation in part of U.S. patent application Ser. No. 12 / 900,540, filed Oct. 8, 2010, which claims priority benefits from U.S. Provisional Patent Application Ser. No. 61 / 250,187 entitled “Bio-Based Binders For Insulation And Non-Woven Mats” filed Oct. 9, 2009, the entire contents of which are expressly incorporated herein by reference.TECHNICAL FIELD AND INDUSTRIAL APPLICABILITY OF THE INVENTION[0002]The present invention relates generally to fibrous insulation products and non-woven mats, and more particularly, to fibrous insulation products that contain a bio-based binder that contains no added formaldehyde and is environmentally friendly.BACKGROUND OF THE INVENTION[0003]Conventional fibers are useful in a variety of applications including reinforcements, textiles, and acoustical and thermal insulation materials. Although mineral fibers (e.g., glass fibers) are typically used in insulation products and non-woven...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D04H1/58C03C14/00B32B1/08B32B27/42B32B27/04
CPCC03C25/1095C09J103/02C09J103/04C09J105/06C03C25/32C03C25/321Y10T428/1314C08L2312/00C08L2666/44C09D105/00C09D133/02C09D189/00C09D191/00C03C25/24C03C25/20Y10T428/249924Y10T442/2959Y10T442/2992Y10T442/60D06M15/01D06M15/11D06M15/263D06M15/507D06N2201/082D06N2209/065
Inventor HAWKINS, CHRISTOPHER M.HERNANDEZ-TORRES, JESUS MANUELCHEN, LIANGMARTINE, EDWARD ALANCHACKO, JACOB
Owner OWENS CORNING INTELLECTUAL CAPITAL LLC
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap