Middle temperature sealant and closing process for aluminum anodized film
An oxide film and sealer technology, applied in electrolytic coatings, surface reaction electrolytic coatings, coatings, etc., can solve the problems of ecological damage, slow degradation, long-term use accumulation, etc., to extend service life, easy to obtain, maintain stable effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0050] Example 1
[0051] 1. After the aluminum and aluminum alloy samples are subjected to the anodic oxidation film formation treatment in the above steps ①-⑧, the oxide film is immediately subjected to the following sealing treatment.
[0052] 1. Oxide film sealing treatment:
[0053] (1) The composition of the blocking agent: magnesium acetate tetrahydrate 6.7g / L, triethanolamine 10mL / L, ammonium acetate 0.5g / L, and the pH value is adjusted to 5.6 with acetic acid.
[0054] (2) Sealing process: 80℃, immersion for 30min.
[0055] (3), secondary running tap water washing.
[0056] (4) Dry in the air at room temperature.
[0057] (5), inspection
[0058] The surface of the sample is clean, no "powder frost", phosphoric acid-chromic acid corrosion weight loss 25.7mg / dm 2 , Closed qualified.
Example Embodiment
[0059] Example 2
[0060] 1. After the aluminum and aluminum alloy samples are subjected to the anodic oxidation film formation treatment in the above steps ①-⑧, the oxide film is immediately subjected to the following sealing treatment.
[0061] 2. Oxide film sealing treatment:
[0062] (1) The composition of the blocking agent: 6.7 g / L magnesium acetate tetrahydrate, hydrazine hydrate (85%), 1 g / L ammonium acetate, and adjust the pH value to 5.85 with acetic acid.
[0063] (2) Sealing process: 80℃, immersion for 30min.
[0064] (3), secondary running tap water washing.
[0065] (4) Dry in the air at room temperature.
[0066] (5), inspection
[0067] The surface of the sample is clean and free of “powder frost”, and the weight loss of phosphoric acid-chromic acid corrosion is 24.1mg / dm 2 , Closed qualified.
Example Embodiment
[0068] Example 3
[0069] 1. After the aluminum and aluminum alloy samples are subjected to the anodic oxidation film formation treatment in the above steps ①-⑧, the oxide film is immediately subjected to the following sealing treatment.
[0070] 2. Oxide film sealing treatment:
[0071] (1) The composition of the blocking agent: lithium hydroxide 10g / L, triethanolamine 10mL / L, sodium acetate 0.5g / L, and the pH value is adjusted to 6.6 with acetic acid.
[0072] (2) Sealing process: 85℃, immersion for 30min.
[0073] (3), secondary running tap water washing.
[0074] (4) Dry in the air at room temperature.
[0075] (5), inspection
[0076] The surface of the sample is clean, no "powder frost", phosphoric acid-chromic acid corrosion weight loss 22.4mg / dm 2 , Closed qualified.
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap