Titanium chrome alloy lost-foam casting flame retardant coatings

A technology of lost foam casting and flame-retardant coatings, which is applied in the direction of fire-resistant coatings, casting molding equipment, coatings, etc. It can solve the problems of unsatisfactory coating effect and poor adhesion of coatings, and improve the smoothness, adhesion and property of castings. Good thermal insulation and low gas generation

Inactive Publication Date: 2009-06-10
大连核心铸造技术工程研究所
View PDF1 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

But the coating has poor adhesion

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0010] Embodiment 1: A kind of titanium-chromium alloy lost foam casting flame retardant coating, it is characterized in that the weight content of each component of said flame retardant coating is bentonite 50%, binder 10%, suspending agent 18%, flame retardant 15% %, silica sol 7%.

[0011] The binding agent of the present invention can be made of 45% of cornstarch; 5% of water-soluble cellulose ether poly; 4% of vinyl alcohol; 15% of solid organic acid; the remaining water is composed of 45% of phosphoric acid; %; boric acid 5%; citric acid 6% composition.

[0012] The suspending agent of the present invention is composed of 50-60% of artificial mica, 8-12% of sodium borate, 5-8% of phosphoric acid and the balance of ethyl acetate.

[0013] The flame retardant of the invention consists of 35-45% of cobalt aluminate, 28-36% of magnesium chloride and 24-29% of potassium chloride.

Embodiment 2

[0014] Embodiment 2: A kind of titanium-chromium alloy lost foam casting flame retardant coating, it is characterized in that the weight content of each component of said flame retardant coating is bentonite 46%, binder 13%, suspending agent 20%, flame retardant 17% %, silica sol 4%.

[0015] The binding agent of the present invention can be made up of 35% of cornstarch; 5% of water-soluble cellulose ether; 3% of vinyl alcohol; 25% of solid organic acid; the remaining water is composed of 45% of phosphoric acid; %; boric acid 7%; citric acid 8% composition.

[0016] The suspending agent of the present invention is composed of 60% of artificial mica, 12% of sodium borate, 8% of phosphoric acid and the balance of ethyl acetate.

[0017] The flame retardant of the invention consists of 35-45% of cobalt aluminate, 28-36% of magnesium chloride and 24-29% of potassium chloride.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a Ti-Cr alloy disappearance casting flame retardant coating, which is characterized in that weight contents of various composition of the flame retardant coating are: 46 to 58 percent of swell soil, 10 to 13 percent of binder, 13 to 22 percent of suspending agent, 12 to 17 percent of flame retardant agent and 3 to 9 percent of silica solution. The binder consists of 35 to 45 percent of corn starch; 3 to 5 percent of poly water-soluble cellulose ether, 0.5 to 4.5 percent of vinyl ethanol, 15 to 25 percent of solid organic acid, the residual water or 45 to 55 percent of phosphoric acid, 33 to 45 percent of aluminum dehydrogenate phosphate, 5 to 15 percent of boric acid and 6 to 12 percent of citric acid monohydrate. The suspending agent consists of 50 to 60 percent of artificial mica, 8 to 12 percent of sodium borate, 5 to 8 percent of phosphoric acid and the balance being water ethyl acetate. The flame retardant agent consists of 35 to 45 percent of cobalt aluminate, 28 to 36 percent of magnesium chloride and 24 to 29 percent of potassium chloride. The casting flame retardant coating can improve the surface quality of casting products effectively and the finish of the casting products, and has cohesive property and heat preservation property.

Description

technical field [0001] The invention relates to a flame-retardant coating for titanium-chromium alloy lost foam casting, which belongs to the technical field of metal casting coatings. Background technique [0002] In the prior art, in order to ensure good surface quality of castings and prevent voids or oxidized wrinkles on the surface of castings, it is the key to improve the quality of magnesium alloy castings to prevent magnesium alloys from burning in the mold during casting. For example, the patent application number is CN02110682.7, a magnesium alloy lost foam casting flame-retardant coating and its preparation method introduced in the publication specification of the invention patent application. The coating composition is 30-50% of magnesia powder, 20-40% of pearl powder, mica powder 15-30%, silica sol 3-9%, white latex 1-5%, polyacrylamide 0.1-0.8%, carboxymethyl cellulose sodium 0.1-0.8%, adsorbent 1-6%, flame retardant 0.3- 2%. When preparing, the adsorbent, so...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): B22C3/00C09D5/18
Inventor 刘弘
Owner 大连核心铸造技术工程研究所
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap