Diblock copolymer containing full-fluorine cyclobutyl aryl aether block and uses thereof

A technology of perfluorocyclobutyl aryl ether and block copolymer, which is applied in the field of two-block polymers and can solve the problems of difficulty in preparing block copolymers, limitations in design and synthesis, etc.

Inactive Publication Date: 2009-07-29
SHANGHAI INST OF ORGANIC CHEMISTRY - CHINESE ACAD OF SCI
View PDF0 Cites 40 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The above method for synthesizing block copolymers containing perfluorocyclobutyl polymer blocks uses thermal cyclopolymerization of trifluorovinyl aryl ether monomers, due to the relatively high polymerization temperatur

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Diblock copolymer containing full-fluorine cyclobutyl aryl aether block and uses thereof
  • Diblock copolymer containing full-fluorine cyclobutyl aryl aether block and uses thereof
  • Diblock copolymer containing full-fluorine cyclobutyl aryl aether block and uses thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0055] The synthesis of embodiment 1.poly-tert-butyl acrylate 3

[0056]

[0057] After the reaction tube was baked dry with gas fire and the nitrogen was replaced, cuprous bromide (39.2 mg, 0.28 mmol) was added, and the nitrogen was replaced three times. After tert-butyl acrylate (4.0 mL, 27.6 mmol), PMDETA (0.06 mL, 0.28 mmol) and anisole (1 mL) were added to the reaction tube, the reaction system was frozen with liquid nitrogen, vacuumized for 5 minutes, and thawed with nitrogen gas. After repeating three times, methyl 2-bromopropionate (0.06mL, 0.55mmol) was added, frozen again-vacuumized-nitrogen-filled thawed three times, put into an oil bath at 70°C and stirred for 2h. Put the reaction tube into liquid nitrogen to freeze and quench the reaction, add THF to dissolve, and pass through a neutral alumina column to remove copper salt. After the solvent was removed by rotary evaporation, 5 mL of THF was added to dissolve, precipitated in cold n-hexane, and filtered by suc...

Embodiment 2

[0061] Example 2. Polytert-butyl acrylate-b-polymethacrylic acid

[0062] Synthesis of (4-((2-(4-methylphenoxy))hexafluorocyclobutoxy))phenyl ester diblock polymer 5

[0063]

[0064] After drying the reaction tube with gas fire and replacing the nitrogen, polymer 3 (525mg, 0.04mmol, M n = 12,500 g / mol, M w / M n =1.10), monomer 4 (0.7mL, 2.1mmol) and CuBr (6mg, 0.04mmol) were added to the reaction tube, and the nitrogen was replaced three times. After adding 1 mL of anisole, freeze with liquid nitrogen, vacuumize for 5 minutes, and fill with nitrogen to thaw. After repeating three times, PMDETA (0.017mL, 0.084mmol) was added, and then frozen-pumped-nitrogen gas was thawed three times, and then placed in an oil bath at 70°C and stirred for 24h. Put the reaction tube into liquid nitrogen to freeze and quench the reaction, add THF to dissolve, and pass through a neutral alumina column to remove copper salt. After the solvent was removed by rotary evaporation, 1 mL THF was...

Embodiment 3

[0069] Embodiment 3. the synthesis of polyethylene oxide macroinitiator 6

[0070]

[0071] Polyethylene oxide (5g, 2.5mmol, M n =2,000g / mol) into a dry three-necked flask, dissolved in freshly distilled dichloromethane (150mL), added triethylamine (1.5mL, 12.5mmol), and placed in an ice-water bath. 2-Bromopropionyl chloride (1.3 mL, 12.5 mmol) was slowly added dropwise, and stirred for 2 h after the addition was complete. The generated salt was removed by suction filtration, the solvent was removed by rotary evaporation, dissolved in 20 mL of THF, precipitated three times in cold ether, and dried in vacuum to obtain 4.23 g of a white powdery polymer.

[0072] FT-IR (KBr): v (cm -1 ) 2929, 1751, 1610, 1503, 1318, 1197, 1104, 962, 818.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a bi-block polymer containing perfluorocyclobutyl aryl ether-based polymer, a preparation method thereof and application thereof. The preparation method comprises two reaction steps: firstly, a macroinitiator formed through atom transfer radical polymerization is prepared; and then the macroinitiator is used for initiating an acrylic ester monomer and a metacrylic acid ester monomer, which contain perfluorocyclobutyl aryl ether structures, to carry out the atom transfer radical polymerization, thus obtaining the diblock polymer containing the perfluorocyclobutyl aryl ether-based polymer. The obtained diblock polymer can be used for preparing an aggregate with microscopic shape and can be potentially applied to such fields as a pollution-resistant reagent, a surfactant, an emulsifier, a drug carrier, photoconductive materials, photonic crystals, etc.

Description

technical field [0001] The invention relates to a two-block polymer containing a perfluorocyclobutyl aryl ether polymer block, a preparation method and an application. Background technique [0002] Perfluorocyclobutyl aryl ether polymers are a new class of fluoropolymers developed by researchers at Dow Chemical Co. in 1993. Polymers of perfluorocyclobutyl aryl ether not only improve the processing performance of fluoropolymers, but also have traditional excellent properties of fluoropolymers, such as low dielectric constant, low hygroscopicity, high thermal stability, high oxidation resistance, High dn / dT value, low birefringence and excellent optical transparency have potential application prospects in the fields of optical fibers, polymer light-emitting diodes, nonlinear optical materials, liquid crystals, aerospace coatings, and proton exchange membranes for fuel cells. In recent years, the preparation of perfluorocyclobutyl aryl ether polymers with specific structures t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C08F297/00C08F220/30B01F17/52A61K47/32G02B1/04
Inventor 黄晓宇张森李永军陆国林童亮
Owner SHANGHAI INST OF ORGANIC CHEMISTRY - CHINESE ACAD OF SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap