Novel wood plastic composite decorative building material and manufacturing method thereof

A wood-plastic composite and manufacturing method technology, applied in the field of wood-plastic composite decorative building materials and its manufacturing, can solve the problems of rough appearance of products, poor dispersion of wood powder, small filling amount of wood powder, etc., and achieve excellent environmental protection characteristics, diverse patterns, Full color effect

Inactive Publication Date: 2012-09-05
CHENGDU AOKINGTH TECH
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This method has the disadvantages of small wood powder filling (generally less than 50 parts by mass), poor dispersion of wood powder in PVC, difficult melt flow, poor processability, and rough product appearance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Novel wood plastic composite decorative building material and manufacturing method thereof
  • Novel wood plastic composite decorative building material and manufacturing method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0019] Three different fillers are used to make wood-plastic products, namely wood powder, bran powder and bamboo powder. And test the physical properties of three different products. Batching by weight, wherein the consumption of PVC resin powder is 100 parts, and the consumption of wood powder or bran powder or bamboo powder is 30 parts, and the consumption of calcium powder is 30 parts, and the consumption of chlorinated polyethylene is 10 parts, The consumption of rare earth composite stabilizer is 5.0 parts, the consumption of polyethylene wax is 1.0 parts, the consumption of stearic acid is 3.0 parts, the consumption of foaming agent is 1.0 parts, and the consumption of acrylic foaming aid is 8 parts , the consumption of antioxidant is 0.5 part, the consumption of toner is 1.0 part, and the consumption of weather resistance agent is 0.5 part. Put the above materials into a high-temperature mixer, mix and dry them, and then put them into a twin-screw extruder for extrusi...

Embodiment 2

[0023] The products are extruded from three different plastics, namely high-density polyethylene (HDPE), polypropylene (PP), and polyvinyl chloride (PVC), and the physical properties of the three wood-plastic products are tested. Ingredients by weight, wherein the consumption of PVC or HDPE or PP resin powder is 100 parts, the consumption of wood powder (more than 80 orders) is 50 parts, the consumption of calcium powder is 30 parts, and the consumption of chlorinated polyethylene is 50 parts. 10 parts, the consumption of rare earth composite stabilizer is 4.0 parts, the consumption of polyethylene wax is 0.5 part, the consumption of stearic acid is 1.0 part, the consumption of blowing agent is 0.8 part, the consumption of the foaming auxiliary agent of acrylate 6 parts, the consumption of the reinforcing agent is 1.0 parts, the consumption of the toner is 1.2 parts, and the consumption of the weather resistance agent is 0.5 parts. Put the above materials into a high-temperatu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
decomposition temperatureaaaaaaaaaa
sizeaaaaaaaaaa
Login to View More

Abstract

The invention relates to a novel wood plastic composite decorative building material and a manufacturing method thereof. The novel wood plastic composite decorative building material comprises the following components in part by weight: 100 parts of polyvinyl chloride (PVC) resin powder, 30 parts of mixture formed by mixing one or more of wood powder, bamboo powder, rice bran powder and crop straw powder in an arbitrary ratio, 30 parts of calcium powder, 5 to 10 parts of chlorinated polyethylene or MBS resin, 2 to 6 parts of rear earth compound stabilizer, 0.5 to 3 parts of polyethylene wax or oxidized polyethlene wax, 0.5 to 3 parts of stearic acid, 0.5 to 2.0 parts of a composite foaming agent with the decomposition temperature thereof within 110 DEG-190 DEG, 5 to 10 parts of acrylic ester-like foaming promoter, 0.5 to 1 part of 4-(b-(3, 5-tert-butyl -4-hydroxyphenyl ) propionate ) pentaerythritol ester or b-(3, 5-tert-butyl -4-hydroxyphenyl ) propionic octadecyl alcohol ester, 0.5 to 1 part of titanic acid ester or silane coupling agent, 1 to3 parts of toner and 0.5 to 1 part of weather resistant agent. PVC plastic is modified by adding the auxiliaries, and the influence of unstable components (such as a vinyl chloride monomer, hydrogen chloride gas and the like) in the PVC on the performance of the building material is eliminated, so that the building material has better performance and environmental protection characteristics on the basis of keeping the original performance.

Description

technical field [0001] The invention relates to a wood-plastic composite decorative building material and a manufacturing method thereof. Background technique [0002] Wood-plastic composite material is a new type of composite material made of wood powder, bamboo powder, bran powder or crop straw powder and PVC, PE resin as the main raw materials through mixing and molding. It has the following characteristics: (1) can be processed and installed like wood, and can be painted; (2) durable, long life, similar to wood appearance, high hardness; (3) has excellent physical and mechanical properties, dimensional stability than wood Good, there will be no cracks and warping, no knot marks and twill lines of wood, and various colorful products can be made by adding colorants or composite surfaces; (4) Easy to shape, and can be shaped and processed with general plastic processing equipment (5) Not afraid of insect bites, aging resistance, corrosion resistance, low water absorption, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L97/02C08K13/02C08K3/26C08J9/06
Inventor 马兴
Owner CHENGDU AOKINGTH TECH