Acrylic acid emulsion and functional acrylic acid emulsion for unshadowed protective film

An acrylic emulsion and acrylate technology, applied in the direction of film/sheet adhesive, adhesive type, adhesive additive, etc., can solve the problems of poor applicability, gel, restriction, etc., to improve heat resistance and Corrosion resistance, high crosslink density and cohesive strength, effect of reducing migration

Inactive Publication Date: 2011-08-31
南京夜视丽精细化工有限责任公司
View PDF7 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0007] Chinese patent CN1517422A discloses the composition and preparation method of a peelable emulsion pressure-sensitive adhesive, which adds a water-dispersible polyisocyanate crosslinking agent to the acrylic emulsion containing hydroxyl groups, and the adhesive products obtained have good Heat resistance, it can be used on a variety of substrates without any residual glue, but the reaction between a large amount of water and water-dispersible polyisocyanate in the emulsion reduces the cross-linking efficiency of the cross-linking agent, and it is very easy to add a cross-linking agent Gel phenomenon occurs during stirring and storage, poor applicability
[0009] Zhou Bo’s Nanjing Forestry University master’s thesis "Research and Application of Emulsion Pressure Sensitive Adhesive for Protective Film" studies the influence of various process conditions on the performance of acrylic emulsion adhesives, and uses internal crosslinking agents, external linking agents, reactive emulsifiers, etc. to improve acrylic emulsion, and studied the application of acrylic emulsion on the surface protective film of stainless steel plate and aluminum-plastic plate, but it did not analyze and solve the problem of water-resistant whitening of the protective film, and the prepared protective film can only withstand 80°C for four hours, making it The application on stainless steel mirror panels is limited, and the heat resistance and water whitening resistance need to be improved
[0010] In summary, there have been many reports on the patents of acrylic pressure-sensitive adhesives for protective films, but there have been no reports on the application of acrylic emulsion pressure-sensitive adhesives for shadow-free protective films on high-gloss stainless steel mirror panels.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Acrylic acid emulsion and functional acrylic acid emulsion for unshadowed protective film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0042] Weigh 35.2 parts of butyl acrylate, 39.8 parts of isooctyl acrylate, 6 parts of methyl methacrylate, 3 parts of hydroxyethyl acrylate, 10.1 parts of ethyl acrylate, 1.9 parts of methyl acrylate, 2 parts of maleic acid, 2 parts of N-methylolacrylamide, 0.5 parts of ammonium persulfate, 2.0 parts of 2-acrylamido-2-methyl-propenesulfonic acid, 40 parts of deionized water, deionized water, 2-acrylamido- Add 2-methyl-propene sulfonic acid and ammonium persulfate into the pre-emulsification tank, stir quickly and evenly; then add the weighed comonomer into the pre-emulsification tank, stir quickly for 0.5h to form a pre-emulsion, decelerate for later use, Add 85 parts of deionized water, 0.3 parts of 2-acrylamido-2-methyl-propenesulfonic acid, and 10% pre-emulsion into the reaction kettle, start stirring, raise the temperature to 82°C, keep it warm for 30 minutes, and react to form seeds Emulsion, then drop the remaining pre-emulsion in about 5 hours, keep it warm for 30 minu...

Embodiment 2

[0044] Weigh 38 parts of butyl acrylate, 31 parts of isooctyl acrylate, 8 parts of lauryl acrylate, 6 parts of methyl methacrylate, 8 parts of ethyl acrylate, 4 parts of methyl acrylate, and 5 parts of maleic acid. 0.3 parts of hydrogen oxide, 0.3 parts of sodium formaldehyde hyposulfite, 2.2 parts of allyloxynonylphenol polyoxyethylene ether bisphosphoric acid, 40 parts of deionized water, the deionized water, allyloxynonylphenol polyoxygen Add vinyl ether diphosphoric acid, hydrogen peroxide, and sodium formaldehyde oxysulfate into the pre-emulsification tank, and stir quickly; then add the weighed mixed monomers into the pre-emulsification tank, and stir quickly for 0.5h to form a pre-emulsion. Slow down for standby, add 85 parts of deionized water, 0.2 parts of allyloxy nonylphenol polyoxyethylene ether bisphosphoric acid, 8% pre-emulsion, start stirring, raise the temperature to 82 ° C, keep warm for 30 minutes, and react to form seeds Emulsion, then drop the remaining pr...

Embodiment 3

[0046] Weigh 10.3 parts of butyl acrylate, 40 parts of isooctyl acrylate, 8 parts of tridecyl acrylate, 9 parts of methyl methacrylate, 15 parts of hydroxypropyl acrylate, 8 parts of ethyl acrylate, butyl methacrylate 4.7 parts, 3.2 parts of maleic acid, 1 part of N-methylolacrylamide, 0.8 parts of acrylamide, 0.4 parts of tert-butyl hydroperoxide, 0.3 parts of sodium formaldehyde sulfoxylate, allyloxynonyl 1.8 parts of phenol polyoxyethylene ether ammonium sulfate, 40 parts of deionized water, deionized water, tert-butyl hydroperoxide, sodium formaldehyde sulfoxylate, and allyloxynonylphenol polyoxyethylene ether ammonium sulfate were added to In the pre-emulsification tank, stir quickly and evenly; then add the weighed mixed monomers into the pre-emulsification tank, stir quickly for 0.5h to form a pre-emulsion, decelerate for later use, add 85 parts of deionized water, 0.4 parts of emulsified agent, 7% pre-emulsion, start stirring, heat up to 82°C, keep warm for 30min, reac...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
peel strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to acrylic acid emulsion and functional acrylic acid emulsion for an unshadowed protective film comprising the same. The acrylic acid emulsion is compounded with an external cross-linking agent to obtain the functional acrylic acid emulsion for the unshadowed protective film which can be applied to a high-finish stainless steel mirror board to form the unshadowed protective film. A preparation method of the acrylic acid emulsion comprises the following steps of: 1) performing polymerization on a functional monomer and an acrylic ester monomer by pre-emulsification and seeding polymerization processes to prepare an acrylic ester polymer, wherein a comonomer comprises the following components in percentage by weight: 5 to 20 percent of the functional monomer, 5 to 10 percent of hard acrylic ester monomer, 10 to 20 percent of medium soft acrylic ester monomer and 50 to 80 percent of soft acrylic ester monomer; Tg of the hard acrylic ester monomer is more than or equal to 36 DEG C; Tg of the medium soft acrylic ester monomer is between 35 and -25 DEG C; and Tg of the soft acrylic ester monomer is less than or equal to -24 DEG C; and 2) adjusting the pH value of the polymer emulsion prepared in the step 1) to be alkalescent to obtain the acrylic acid emulsion.

Description

technical field [0001] The invention relates to an acrylic emulsion and a functional acrylic emulsion for a shadow-free protective film. Background technique [0002] Surface protection adhesive tape is a type of pressure-sensitive adhesive tape mainly used to protect the surface of materials to prevent the surface of materials from being scratched, polluted and corroded during processing, transportation, storage and use. Such as various plastic panels, soil panels, stainless steel panels and aluminum alloy materials. [0003] The surface protective film has the following requirements: easy to paste; can be peeled off repeatedly without leaving any glue marks and "shadows" of the pressure-sensitive adhesive on the metal surface; no corrosion or rust on the metal surface; excellent water whitening resistance , resistance to heat and humidity and aging properties, without any bad smell. [0004] Judging from the public reports on pressure-sensitive adhesives used for surface...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/18C08F220/14C08F220/28C08F222/02C08F220/58C08F2/24C08L33/08C09J133/08C09J11/06C09J7/02
Inventor 林中祥周波牛正发曹刚杨华新
Owner 南京夜视丽精细化工有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com