Phosphogypsum sintered brick and production process thereof
A technology of sintered bricks and phosphogypsum, applied in the field of sintered bricks, can solve problems such as environmental pollution, sulfur dioxide pollutants, and inability to achieve industrialization, and achieve the effects of saving land resources, protecting cultivated land, and widening sources
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0037] Example 1
[0038] Phosphogypsum sintered brick, its sintering raw materials, based on absolute dry weight, include the following components by weight:
[0039] 25.5 parts by weight of phosphogypsum;
[0040] 32.2 parts by weight of coal gangue;
[0041] 26.5 parts by weight of river silt;
[0042] Dry powder additives 8 parts by weight.
[0043] The particle size of the coal gangue is 0.1-0.3 mm, and the particle size of the dry powder additive is 0.1-0.3 mm.
[0044] Preparation method of phosphogypsum fired brick (such as figure 1 The process flow chart shown in which the machine used is conventional equipment in the prior art) is:
[0045] Add phosphogypsum with a water content of 5% to a water content of 13-18%; grind coal gangue and finished sintered bricks to a particle size of 0.1-0.3mm; pass a river sludge with a water content of 20-40% Aging, dehydration and drying to a moisture content of 13-18%; according to the proportion of coal gangue, river sludge and dry powder add...
Example Embodiment
[0049] Example 2
[0050] Phosphogypsum sintered brick, its sintering raw materials, based on absolute dry weight, include the following components by weight:
[0051] 25.5 parts by weight of phosphogypsum;
[0052] 32.2 parts by weight of cinder;
[0053] 30 parts by weight of river silt;
[0054] Dry powder additives 8 parts by weight.
[0055] The particle size of the coal gangue is 0.1-0.3 mm, and the particle size of the dry powder additive is 0.1-0.3 mm.
[0056] The preparation method of phosphogypsum sintered brick is:
[0057] Add phosphogypsum with 5% water content to 13-18% water content; pulverize coal slag and finished sintered bricks to a particle size of 0.1-3mm; age and dehydrate river sludge with 40% water content Drying to a moisture content of 13-18%; adding coal slag, river sludge and dry powder additives to the phosphogypsum according to the ratio, and adding water to adjust the moisture content of the mixture to 13-18%, and aging for 5-7 days. After aging, fully agi...
Example Embodiment
[0060] Example 3
[0061] Phosphogypsum sintered brick, its sintering raw materials, based on absolute dry weight, include the following components by weight:
[0062] 20 parts by weight of phosphogypsum;
[0063] 27.6 parts by weight of coal gangue;
[0064] 22.5 parts by weight of river silt;
[0065] Dry powder additive 5 parts by weight.
[0066] The particle size of the coal gangue is 0.1-0.3 mm, and the particle size of the dry powder additive is 0.1-0.3 mm.
[0067] The preparation method of phosphogypsum sintered brick is:
[0068] Add phosphogypsum with a water content of 5% to a water content of 13-18%; grind coal gangue and finished sintered bricks to a particle size of 0.1-0.3mm; age river sludge with a water content of 25% , Dehydrate and dry to a moisture content of 13-18%; add coal gangue, river sludge and dry powder additives to the phosphogypsum according to the ratio, mix and add water to adjust the moisture content of the mixture to 13-18%, and age for 7 days. After ag...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap