Preparation method of Pb oxide nano powder for recovery and manufacture of lead acid battery

A lead-acid battery and nano-powder technology, which is applied in battery recycling, lead oxide, nanotechnology, etc., can solve the problems that are not suitable for lead-acid battery recycling and manufacturing process, the manufacturing process requirements do not meet, and it is difficult to commercialize production and application and other issues to achieve the effect of shortening the production cycle, simplifying the process and related logistics steps, and reducing production costs

Active Publication Date: 2012-09-26
杨春晓
View PDF5 Cites 24 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Chinese patent No. is 02100264.9 (authorization announcement number CN 1171797C) invention patent also discloses a kind of method of synthesizing α, β type lead dioxide nanocrystal and trilead tetraoxide nanocrystal, but the prepared Pb oxide is different from existing Mature lead-acid battery manufacturing process requirements do not meet
[0005] In the above method for preparing Pb oxide powder, either the process cost is too high, or it is not suitable for the recovery and manufacturing process of the existing lead-acid battery, and it is difficult to be applied in commercial production.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of Pb oxide nano powder for recovery and manufacture of lead acid battery
  • Preparation method of Pb oxide nano powder for recovery and manufacture of lead acid battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] The preparation method of the Pb oxide nano-powder that is used for lead-acid storage battery recovery and manufacture of the present invention, its schematic flow sheet, as shown in the accompanying drawings of description, its steps comprise:

[0033] (1) Place 0.1kg (0.308mol) of lead acetate in 0.9kg of water, then pass 0.136kg (3.08mol) of CO into the water 2 To form a carbonic acid solution, react with lead acetate at the same time to generate a precipitate, the reaction is carried out at room temperature, the reaction time is controlled until no precipitation continues to occur, and precipitate A is generated;

[0034] In addition, the above-mentioned 1kg lead acetate solution was also prepared, and 0.02kg (0.0308mol) of surfactant Triton X-100 was added thereto, and then the same CO 2 The operation, and the reaction system was supplemented with 30s ultrasound at intervals of 2 minutes during the process, resulting in precipitate B;

[0035] (2) Filter the above...

Embodiment 2

[0037] The preparation method of the Pb oxide nanopowder that is used for lead-acid storage battery recovery and manufacture of the present invention, its steps comprise:

[0038] (1) Mix 0.1kg of lead sulfate (0.33mol) with 1 liter of Na with a concentration of 1.65mol / L 2 CO 3 The aqueous solution is reacted, and the solution is removed after the reaction, and then the precipitate is mixed with 1 liter of Na with a concentration of 1.65mol / L 2 CO 3 The aqueous solution is reacted, so repeated 200 times, that is, 0.1kg of lead sulfate (0.33mol) is mixed with 333mol of Na in total 2 CO 3 Interact, fully remove sulfur, and obtain precipitate A;

[0039] In addition, the same preparation of the above Na 2 CO 3 solution, and 0.007kg (0.0165mol) of surfactant Tween-80 was added thereto, and then the same repeated operation was performed, and the reaction system was supplemented with 30s ultrasound during the interaction (reaction). 2 CO 3 In addition to the interaction, 0....

Embodiment 3

[0042] The preparation method of the Pb oxide nanopowder that is used for lead-acid storage battery recovery and manufacture of the present invention, its steps comprise:

[0043] (1) Place 0.1kg (0.303mol) of lead nitrate in 3kg of water, and then continuously feed 13.33kg (303mol) of CO into the water 2 To form a carbonic acid solution, react with lead nitrate at the same time to generate a precipitate, the reaction is carried out at room temperature, the reaction time is controlled until no precipitation continues to occur, and precipitate A is generated;

[0044] In addition, prepare above-mentioned 0.1kg (0.302mol) lead nitrate solution equally, and add the surfactant lauric acid of 3.02mol (0.6kg) wherein (or it and a certain amount, such as 1kg, ethanol solvent add together), stir simultaneously The reaction system was supplemented with ultrasound, and then the same CO 2 The operation produces precipitate B;

[0045] (2) Filter the above solution or / and oily liquid to...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparation method of a Pb oxide nano powder for recovery and manufacture of a lead acid battery. The method comprises the steps of: (1) reacting lead salt or waste lead acid battery lead paste with an organic or inorganic compound capable of complexing with Pb atom / ion, so as to realize desulphurization or reloading of acid radical; and (2) carrying out treatment processes of filtering, drying for removing water and heating for decomposition, so as to obtain the Pb oxide nano powder. The method of the invention realizes an environment-friendly and energy-efficient recovery and production process with substantially reduced production cost; meanwhile, the prepared Pb oxide powder is beneficial for enhancement of product performance.

Description

technical field [0001] The invention relates to the preparation of a Pb (lead) oxide nanopowder, in particular to a method for preparing the Pb oxide nanopowder used in the recovery and manufacture of lead-acid storage batteries. Background technique [0002] Compared with other commercialized batteries, lead-acid batteries show good cycle characteristics. This is because lead, the main raw material for batteries, has been better recycled. The early methods of lead recovery mainly include earth-fire method, that is, using reverberatory furnace, blast furnace, etc. to smelt the lead paste of waste batteries. PbSO in general lead paste 4 Its content is more than 50%, its melting point is high, and the temperature of complete decomposition is above 1000°C [Yang Jiakuan. Research progress of waste lead-acid battery lead paste recycling technology [J]. Modern Chemical Industry, 2009, 29 (3)]. In order to overcome the high energy consumption of pyrotechnics, high pollution emis...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C01G21/02C01G21/06H01M10/54B82Y40/00
CPCY02E60/12Y02W30/84
Inventor 杨春晓徐志国
Owner 杨春晓
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com