Manufacturing technology of plant fiber synthetic resin powder and plant fiber product

A plant fiber powder and plant fiber technology, applied in the field of chemical materials, can solve the problems of waste water pollution, high cost, environmental pollution, etc., and achieve the effects of low cost, long service life and broad market prospects

Active Publication Date: 2013-03-20
XIAMEN HUSKS NEW MATERIAL TECH CO LTD
View PDF4 Cites 15 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] The existing tableware, furniture, kitchen utensils and other daily necessities on the market are made of plastic, wood, bamboo and other products. It destroys the water permeability of the soil, and wood products require deforestation and waste water pollution in the manufacturing process, which is not a very good environmental protection material
[0003] In particular, most of the existing disposable tableware uses foamed plastics, and its foaming agent is Freon, which will destroy the ozone layer of the atmosphere, and it is extremely difficult to degrade. The invention patent publication CN1212312A discloses a degradable disposable tableware. Non-toxic tableware and a manufacturing method thereof, the method uses crop shells or rods as raw materials, and adds urea-formaldehyde resin and melamine to make it by hot pressing. The melamine used in the method is expensive, and the material will cause environmental pollution after degradation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] Grind 60g of tea leaves into 60-mesh tiny tea powder; put the tea powder into a high-speed mixer, add 10g of rice bran wax and 30g of amylopectin and mix evenly, then put it into the reaction kettle, add 20g of water and stir evenly to form a Then add 35g of gum arabic powder and heat at 80°C to form a paste; inject the paste directly into the flash dryer, the temperature of the hot air during the drying process is 100°C, and the material is discharged when the moisture content is 8%. Make tea fiber synthetic resin powder, pack and store after cooling.

[0018] Start the high-temperature molding machine, heat the mold temperature to 130°C, and adjust its pressure to 18MPa, then inject 30g of the above-mentioned tea synthetic resin powder into the spoon mold and then mold it. After the product is formed, take it out, and then put the The product is ground with an edge grinder, and then polished into a soup spoon with a polishing machine.

Embodiment 2

[0020] Grind 100g of pitaya peel into 100 mesh tiny particles of pitaya peel powder; then put the pitaya peel powder into a high-speed mixer, add 25g of rice bran wax and 45g of waxy corn starch and mix evenly, then put it into the reaction kettle, add 25g of water Stir evenly to form a slurry, then add 50g of gelatin, and heat at 120°C to form a paste; inject the paste directly into the flash dryer, during the drying process, the temperature of the hot air is 120°C, and the material is discharged when the moisture content is 10%. , make pitaya peel synthetic resin powder, pack and store after cooling.

[0021] Start the high-temperature molding machine, heat the mold temperature to 200°C, and adjust its pressure to 21MPa, then inject 80g of the above-mentioned dragon fruit peel synthetic resin powder into the dish mold and then carry out molding. After the product is formed, take it out, and then put the The product is deburred with an edge grinder, and then polished into a d...

Embodiment 3

[0023] Grind 40g of tea stalks into 300-mesh tea stalk powder; then put the tea stalk powder into a high-speed mixer, add 5g of rice bran wax and 16g of tapioca starch and mix evenly, then put it into the reaction kettle, add 10g of water and stir Make a slurry evenly, then add 18g of hydrogenated rosin, and heat at 150°C to form a paste; inject the paste directly into the flash dryer, during the drying process, the temperature of the hot air is 80°C, and the material is discharged when the moisture content is 5%. , make tea stem synthetic resin powder, pack and store after cooling.

[0024] Start the high-temperature molding machine, heat the mold temperature to 250°C, and adjust its pressure to 10MPa, then inject 100g of the above-mentioned tea stalk synthetic resin powder into the cup mold and then mold it. After the product is formed, take it out, and then put the The product is ground with an edge grinder, and then polished into a cup with a polisher.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention relates to the field of chemical materials, in particular to a manufacturing technology of plant fiber synthetic resin powder and a plant fiber product. The manufacturing technology comprises the following steps: grinding plant fiber into plant fiber powder with molecules, putting the plant fiber powder into a high-speed mixer, adding rice bran wax and starch, evenly mixing, putting into a reaction kettle, evenly stirring into pulp by added water, heating up by adding natural resin powder into pasty materials, and injecting into a flash streaming drier to prepare into the plant fiber synthetic resin powder. The manufacturing technology is the recycle derived from the plant fiber residue. The product of the manufacturing technology has the natural color and fragrance of the plant fiber per se, has super-strong water resisting property, further has the characteristics of being hard, high-density, smooth, non-toxic, low-cost, environment-friendly and the like, and can be automatically degraded into organic fertilizer in the natural world, and can return to nature, and the product produced by the manufacturing technology is freezing-resistant, high temperature-resistant, good in intensity, density and hardness, and long in service life, thereby being an environment-friendly material, and wide in market prospect.

Description

technical field [0001] The invention relates to the field of chemical materials, in particular to a manufacturing process of plant fiber synthetic resin powder and plant fiber products. Background technique [0002] The existing tableware, furniture, kitchen utensils and other daily necessities on the market are made of plastic, wood, bamboo and other products. It destroys the water permeability of the soil, and wood products require deforestation and waste water pollution during the manufacturing process, so they are not very good environmental protection materials. [0003] In particular, most of the existing disposable tableware uses foamed plastics, and its foaming agent is Freon, which will destroy the ozone layer of the atmosphere, and it is extremely difficult to degrade. The invention patent publication CN1212312A discloses a degradable disposable tableware. Disclosed is permanent tableware and a manufacturing method thereof. The method uses crop husks or rods as ra...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L97/02C08L91/06C08L3/02C08L3/12C08L89/00C08L93/04C08L93/00
Inventor 庄展鹏
Owner XIAMEN HUSKS NEW MATERIAL TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap