Single-component water-borne pressure sensitive adhesive for sun-proof and heat-insulating film

A single-component, pressure-sensitive adhesive technology, applied in adhesive types, ester copolymer adhesives, etc., can solve the problems of shortened glue pot life, reduced cross-linking efficiency, lack of water resistance, etc., to achieve glue pot life Long, simple process route, reducing the possibility of water absorption and whitening

Active Publication Date: 2013-05-01
广东创阳新材料科技有限公司
View PDF5 Cites 11 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The conventional method of adding a cross-linking agent has the disadvantages of short pot life of glue, large waste, or the toxicity of the cross-linking agent, and poor environmental protection. The one-component type can overcome the above shortcomings, and is easy to use and basically no waste
[0009] There are patents related to water-based pressure-sensitive adhesives related to surface protection films, such as "Peelable Emulsion Pressure-Sensitive Adhesive and Pressure-Sensitive Adhesive Sheet" (Patent Publication No. CN1517422A) describes the composition and preparation of a peelable emulsion PSA method, which includes an acrylate emulsion polymer and an external crosslinking agent containing a water-dispersible polyisocyanate, but the reaction of the water-dispersible polyisocyanate with water in the emulsion reduces the crosslinking efficiency, thereby reducing the water resistance, and also leads to The pot life of the glue is significantly shortened
"Preparation Method of Emulsion Pressure Sensitive Adhesive for Moisture and Heat Resistance Surface Protection Film and Surface Protection Film" (Patent Publication No. CN101153208A) describes an emulsion pressure sensitive adhesive for moisture and heat resistance protection film. Reactive emulsifier, without fluorine modification method, still lacks in water resistance, and is not a one-component type

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Single-component water-borne pressure sensitive adhesive for sun-proof and heat-insulating film

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Follow the specific steps below to prepare a one-component water-based pressure-sensitive adhesive for the adhesive layer of the sunscreen and heat insulation film:

[0033] 1. Preparation of seed emulsion: Mix 100 parts by weight of deionized water and 1.5 parts by weight of 2-acrylamido-2-methylpropane sulfonate sodium (AMPS-NA), and stir at a stirring speed of 250 rpm Evenly, then slowly drop 25 parts by weight of methyl methacrylate, 15 parts by weight of butyl acrylate, 1 part by weight of acrylic acid, 0.5 parts by weight of hydroxyethyl acrylate, and 0.5 parts by weight of acrylamide, and stir for 20 minutes , heating up to 82°C, passing nitrogen, removing oxygen, then adding 0.2 parts by weight of ammonium persulfate, and reacting for 3 hours to obtain a seed emulsion;

[0034] 2. Preparation of pre-emulsion A: 30 parts by weight of deionized water, 0.3 parts by weight of 2-acrylamido-2-methylpropane sulfonate sodium (AMPS-NA), 0.3 parts by weight of sodium viny...

Embodiment 2

[0045] Follow the specific steps below to prepare a one-component water-based pressure-sensitive adhesive for the adhesive layer of the sunscreen and heat insulation film:

[0046] 1. Preparation of seed emulsion: Mix 100 parts by weight of deionized water and 1 part by weight of allyloxy fatty alcohol polyoxyethylene ether ammonium sulfate (SR-10), and stir evenly at a stirring speed of 500 rpm. Then slowly the ethyl methacrylate of 5 parts by weight, the butyl methacrylate of 5 parts by weight, the isooctyl acrylate of 20 parts by weight, the butyl acrylate of 9 parts by weight, the methacrylic acid of 2 parts by weight, 1 weight part part of hydroxyethyl methacrylate, stirred for 30 minutes, heated up to 78°C, passed through nitrogen, deoxygenated, then added 0.1 parts by weight of potassium persulfate, and reacted for 2 hours to obtain a seed emulsion;

[0047] 2. Preparation of pre-emulsion A: Mix 30 parts by weight of deionized water, 0.3 parts by weight of allyloxy fatt...

Embodiment 3

[0058] Follow the specific steps below to prepare a one-component water-based pressure-sensitive adhesive for the adhesive layer of the sunscreen and heat insulation film:

[0059] 1. Preparation of seed emulsion: 100 parts by weight of deionized water, 0.7 parts by weight of sodium alkylamide ethylene sulfonate (DNS-86), 0.8 parts by weight of allyloxy nonylphenol polyoxyethylene ether ammonium sulfate (SE-10) mixing, using 200 rpm stirring speed to stir evenly, and then slowly mix 10 parts by weight of octyl methacrylate, 15 parts by weight of lauryl acrylate, 2 parts by weight of methyl acrylate, 5 parts by weight ethyl acrylate, 10 parts by weight of butyl acrylate, and 0.2 parts by weight of methacrylic acid, stirred for 10 minutes, heated up to 82°C, passed nitrogen, deoxygenated, and then added 0.30 parts by weight of ammonium persulfate, reacted for 2.5 hours, Obtain seed emulsion;

[0060] 2. Preparation of pre-emulsion A: 30 parts by weight of deionized water, 0.3 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a single-component water-borne pressure sensitive adhesive for a sun-proof and heat-insulating film. A fluorine-containing ethylene monomer is introduced in the polymerization process to carry out the modification by copolymerization, and the single-component water-borne pressure sensitive adhesive for the sun-proof and heat-insulating film, which consumes fewer emulsifiers and has excellent performance, is synthetized through a seed emulsion polymerization method by a reaction-type emulsifier. The invention further provides a preparation method of a sun-proof and heat-insulating film viscous layer. The prepared protective film viscous layer has favorable water resistance and weather resistance, can ensure no foaming, no swelling, no wrinkling and no flanging after being used for a long time as required.

Description

technical field [0001] The invention belongs to the field of chemical industry, and in particular relates to a single-component water-based pressure-sensitive adhesive for a sunscreen and heat-insulating film. Background technique [0002] Sunscreen and heat insulation film is a new type of surface protection material developed to prevent ultraviolet / infrared radiation. The sunscreen and heat insulation film is based on polyester film, which has high transparency, high ultraviolet / infrared ray blocking rate, strong impact resistance and tear resistance, adjustable adhesion performance, and good adhesion to various surfaces. The time changes are small. Paste it on the surface of various car window glass, building materials, instruments, electronic products and other materials to avoid damage caused by ultraviolet / infrared radiation. The application of sunscreen and heat insulation film can not only effectively block the heat of solar radiation, reduce a lot of heat in the h...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J133/08C08F220/18C08F220/14C08F220/28C08F220/56C08F220/22C08F220/68
Inventor 柯跃虎张刚江家钧
Owner 广东创阳新材料科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap