A kind of 6,6-dimethyl-6h-benzo[cd]pyrene derivative and its application

A pyrene derivative, dimethyl technology, applied in the field of 6,6-dimethyl-6H-benzo[cd]pyrene derivatives, can solve the problems of low power efficiency, poor stability, low electron mobility, etc. Achieve the effect of high glass transition temperature, thermal stability guarantee, and high electron mobility

Active Publication Date: 2016-03-09
KUNSHAN VISIONOX DISPLAY TECH +2
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, CBP still has obvious defects: the glass transition temperature Tg is very low, only 62°C, and as a hole-type transport material, the corresponding electron transport ability of CBP is not balanced enough, which affects the efficiency and life of the device.
[0006] The traditional electron transport material is 8-trihydroxyquinoline aluminum (AlQ 3 ), but AlQ 3 Has many disadvantages: (1) Electron mobility is relatively low (about 10 -6 cm / Vs), which leads to higher voltage and thus lower power efficiency; (2) poor stability and partially decomposes at sublimation temperature; (3) has high hygroscopicity, which affects the lifetime of the device ; (4) It has color, and the color shift is caused by reabsorption and re-emission phenomenon, which affects the color purity of the device
Devices based on this hybrid electron transport layer have improved efficiency and lifetime, but increase the complexity of the device manufacturing process, which is not conducive to reducing the cost of OLEDs

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of 6,6-dimethyl-6h-benzo[cd]pyrene derivative and its application
  • A kind of 6,6-dimethyl-6h-benzo[cd]pyrene derivative and its application
  • A kind of 6,6-dimethyl-6h-benzo[cd]pyrene derivative and its application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0070] This embodiment is the precursor S11 of the synthetic intermediate S1:

[0071]

[0072] The synthetic route is shown in the following formula:

[0073]

[0074] The synthesis method is:

[0075] S11-2: Add 150ml of fuming nitric acid into a 500ml three-neck flask, cool it to about 5°C with an ice-water bath, add 22.2g of 10,10-dimethylanthrone (0.1mol) in batches under stirring, and control the feeding speed so that the reaction solution The temperature is not higher than 10°C. After the reactants are added, keep the temperature of the reaction solution at 5°C for about 30 minutes. The reactant was poured into 400ml of ice water, stirred vigorously, and then suction filtered. The filter cake was washed with water, dried, and recrystallized with ethanol-petroleum ether mixed solvent to obtain 25 g of light yellow solid with a yield of 80%.

[0076] S11-3: Corey-Fuchs dibromoalkenylation reaction: Add 25g S11-2 (80mmol) and 53g carbon tetrabromide (160mmol) to a...

Embodiment 2

[0083] This embodiment is the precursor S21 of the synthetic intermediate S2:

[0084]

[0085] The synthetic route is shown in the following formula:

[0086]

[0087] The synthesis method is:

[0088]S21-2: Corey-Fuchs dibromoalkenylation reaction: In a 500ml dry pressure-resistant reactor, add 22.2g (80mmol) of 10,10-dimethylanthrone, 53g of carbon tetrabromide ( 160mmol), the reaction system was evacuated three times - nitrogen circulation, added 250ml dry benzene, the mixture was stirred for 5 minutes, and 83.7g triphenylphosphine (320mmol) was added. The reaction mixture was vigorously stirred at 150° C. for 48 h, and the temperature of the system was cooled to room temperature, and an appropriate amount of CH2Cl2 was added to dissolve the reaction mixture. The crude product was separated by column chromatography (pure petroleum ether) to obtain 24.5 g of white solid S21-2, with a yield of 65%.

[0089] S21-3: Under N2 protection, add 2.6g of zinc powder (0.04mo...

Embodiment 3

[0095] This embodiment is the precursor S31 of the synthetic intermediate S3:

[0096]

[0097] The synthetic route is shown in the following formula:

[0098]

[0099] The synthesis method is:

[0100] Weigh 1.4g (97.7mmol) of S114 synthesized in Example 1, 55.1g (195.4mmol) of p-bromoiodobenzene, Pd(dba) 2 1.69g (2.93mmol), and NaO-t-Bu22.5g (234.5mmol) were placed in a 2000mL three-necked round-bottomed flask, and 1000mL of toluene (potassium hydroxide was dried for 3 days) was added, ventilated and inert gas protected, oil Warm up the bath to 90°C, add 5.9 mL of LP(t-Bu) 3 (10%, cyclohexane solution) was slowly heated to 115°C and refluxed for 2 hours, cooled, the reaction solution was washed 3 times with an appropriate amount of water, separated, the organic phase was spin-dried, and recrystallized from ethyl acetate to obtain 33.8g of the product, with a yield of 60% .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The present invention relates to a 6,6-dimethyl-6H-benzo[cd]pyrene derivative, a class of compounds shown in formula (1), wherein: n is 1 or 2; R1-R5 are The five substituents at different positions are the same or different from each other, and are independently selected from H atoms, C1-C20 aliphatic straight-chain or branched hydrocarbon groups, and C1-C20 aromatic groups; Ar is an aromatic group ; A is an N atom or CH; L is a single bond, selected from a C6-C10 aromatic ring or aromatic heterocyclic ring. The present invention also protects the application of such compounds in organic electroluminescent devices, especially as electron transport materials and / or light-emitting host materials of OLEDs.

Description

technical field [0001] The present invention relates to an organic compound, in particular to a 6,6-dimethyl-6H-benzo[cd]pyrene derivative used in an organic electroluminescence device, a preparation method and its application in an organic electroluminescence device applications. Background technique [0002] Electroluminescence (Electroluminescence, EL) refers to the phenomenon that luminescent materials are excited by current and electric field under the action of an electric field to emit light. It is a luminescence process that directly converts electrical energy into light energy. There are many solid materials that can produce electroluminescence, and those that have been studied more and can reach the level of use are mainly inorganic semiconductor materials. However, the production cost of inorganic EL devices is high, the processing is difficult, the efficiency is low, the luminous color is not easy to adjust, it is difficult to realize full-color display, and it ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C07D403/14C07D251/18C07D251/24C07D241/20C07D241/12C07D239/42C07D239/26C07F5/02H01L51/54
CPCC07D239/26C07D239/42C07D241/12C07D241/20C07D251/18C07D251/24C07D403/14C07F5/025H10K85/623H10K85/636H10K85/615H10K85/654H10K85/6572
Inventor 邱勇汤金明范洪涛段炼任雪艳
Owner KUNSHAN VISIONOX DISPLAY TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com