Polar monomer graft-modified amorphous poly-alpha-olefin and preparation method thereof
A polar monomer, graft modification technology, applied in the direction of graft polymer adhesives, adhesive types, adhesives, etc., can solve the problems of inconvenient materials, short storage period, etc. Processing fluidity, good fluidity effect
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0030] Example 1:
[0031] After dissolving 30g of maleic anhydride with 30g of acetone, it was mixed with 3kg of APAO792 (Degussa), 3g of 2,5-dimethyl-2,5-bis(tert-butylperoxy)hexane, 3g of (3) Ethoxylated trimethylolpropane triacrylate, 15g of tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl)propionic acid]pentaerythritol ester are mixed uniformly with a high-speed mixer, and wait for the solvent After volatilization, reactive extrusion is carried out on a twin-screw extruder with a screw length-to-diameter ratio of 40:1. The temperature of each zone of the extruder is 80, 120, 150, 190, 190, 190, 190, 190, 180 ℃, and the material is at The reaction time of the twin-screw extruder is 0.03h. The light-colored graft particles are obtained by using underwater pelletizing equipment. The grafting rate of maleic anhydride after acid-base titration is 0.63%. After testing, the storage period is one year.
Example Embodiment
[0032] Example 2:
[0033] Add 100kg of ΑPAO703 (Degussa) into the reaction kettle, fully melt it at 160°C, add maleic anhydride and stir evenly, the maleic anhydride added is 3% of the weight of Α-PA-O, add dropwise with liquid feeding equipment Initiator tert-butyl cumene peroxide, the amount of initiator is 0.5% of the weight of APAO, and the grafting aid is added dropwise at the same time. The addition amount of the grafting aid is 5% of the weight of A-PA-O. The branching agent is a mixture of styrene and diethylene glycol diacrylate in a weight ratio of 3:2. Adjust the liquid feeding speed so that the initiator and the grafting aid are added dropwise within 2 hours, and then continue to react for 2 hours, then Add antioxidant β-(3,5-di-tert-butyl-4-hydroxyphenyl) n-octadecyl propionate, the amount of antioxidant added is 0.5% of the weight of APAO, stir evenly and then vacuum The unreacted maleic anhydride is removed, and after cooling, a light yellow maleic anhydride graf...
Example Embodiment
[0034] Example 3:
[0035] Add 100kg of ΑPAO508 (Degussa) into the reactor, fully melt at 190°C, add glycidyl methacrylate and stir evenly, the added glycidyl methacrylate is 6% of the weight of ΑPAO, use liquid feeding equipment Drop the initiator dicumyl acetone peroxide solution (dicumyl peroxide is dissolved in the same mass of acetone), the amount of the initiator is 0.75% of the weight of APAO, and at the same time, the grafting aid is added dropwise to aid the grafting The addition amount of the grafting agent is 2% of the weight of APAO, and the co-grafting agent is a mixture of polyethylene glycol diacrylate and pentaerythritol tetraacrylate with a weight ratio of 9:1. The liquid feeding rate is adjusted to enable the initiator and the co-grafting The branching agent was added dropwise within 1.5 hours, after which the reaction was continued for 2 hours, and then the antioxidant tetra[β-(3,5-di-tert-butyl-4-hydroxyphenyl) propionic acid] pentaerythritol ester and tri(2) ...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap