Anticorrosion aerated brick and making method thereof
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A production method and technology of aerated bricks, applied in the field of aerated bricks, can solve the problems of slow development of aerated bricks technology and inability to meet diversified markets, and achieve reduced energy consumption, finished product pass rate, excellent compressive strength, and durability Good grinding performance
Inactive Publication Date: 2014-06-04
重庆市霖垚诚首环保建材有限公司
View PDF3 Cites 4 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, at present, the production technology of aerated bricks in my country is not mature enough, which makes the development of aerated bricks technology slow and cannot meet the needs of diversified markets.
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0014] The anti-corrosion aerated brick is characterized in that it is made of the following raw materials in parts by weight: quicklime 14, fluorite slag 26, hydrogen peroxide 1, cement 8, ammonium bisulfite 0.4, Glauber's salt 0.6, urban road waste cement Road slag 11, zirconia 2, fly ash 6, acrylic fiber 5, aluminum magnesium metasilicate 1, dibenzylidene sorbitol 7, perfluoroalkyl ethyl acrylate 4, N-vinylpyrrolidone 0.3, olive Oil 8, lemongrass 0.35, Artemisia argyi 0.26, auxiliary agent 3, appropriate amount of water; the auxiliary agent is made of the following raw materials in parts by weight: polyphenylene ether 0.03, carbon nanotube 0.1, polyoxyethylene ether 0.02, sodium silicate 0.25 , triethylamine 1.4, wollastonite powder 3, urotropine 0.01, camphor 0.1, cedarwood oil 1, peanut shell 4, trichloroethyl phosphate 1.2, the preparation method is to pulverize and mix each material, and heat to 70- 80 ℃, stirring reaction for 30-40 minutes, that is.
[0015] The prepa...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Property
Measurement
Unit
density
aaaaa
aaaaa
compressive strength
aaaaa
aaaaa
Login to view more
Abstract
The invention discloses an anticorrosion aerated brick, which is characterized by being made of the following raw materials by weight part: 14-16 of quicklime, 24-26 of fluorite slag, 1-2 of hydrogen peroxide, 8-9 of cement, 0.2-0.4 of ammonium bisulfite, 0.4-0.6 of salt cake, 10-12 of urban road waste cement road slag, 2-4 of zirconia, 6-8 of fly ash, 5-8 of acrylic fiber, 1-3 of magnesium aluminometasilicate, 7-9 of dibenzylidene sorbitol, 4-7 of perfluoroalkylethyl acrylate, 0.3-0.7 of N-vinyl pyrrolidone, 6-8 of olive oil, 0.3-0.5 of citronella grass, 0.2-0.6 of folium artemisiae argyi, 3-5 of an additive, and a proper amount of water. The aerated brick made by the invention has good anticorrosion effect and good wear resistance, can effectively prevent external force and internal stress damage and resist acid liquor corrosion or flue gas scouring, can effectively prolonging the service life of the matrix, and reduces energy consumption. Meanwhile, by optimizing the formula materials, cracks on a green body are reduced, the qualified rate and the compressive strength of the finished product are excellent.
Description
technical field [0001] The invention relates to the technical field of aerated bricks, in particular to an anti-corrosion aerated brick and a manufacturing method thereof. Background technique [0002] In recent years, with the acceleration of the industrialization process and the improvement of the level of urbanization, various environmental pressures and problems have also been brought about. Various solid wastes generated in the industrial production process and solid wastes caused by urban construction demolition and reconstruction have been troubled. In order to meet the living environment of residents, the present invention adds solid waste as a raw material to the aerated bricks, realizes waste recycling, reduces environmental pollution, and meets the strategic requirements of sustainable development. [0003] Aerated bricks are aerated concrete blocks produced by high-temperature autoclaved equipment. The aerated concrete block is a solid block made of cement, sla...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.
Login to view more