hatcn and its construction of cu(i) complex as an organic ultraviolet photodetector with an anode buffer layer

An anode buffer layer, organic ultraviolet light technology, applied in the direction of electric solid device, semiconductor device, semiconductor/solid state device manufacturing, etc., to achieve the effect of good film formation, prevent device aging, and facilitate hole transport

Inactive Publication Date: 2017-02-08
JILIN NORMAL UNIV
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] In order to solve the device aging of the organic ultraviolet light detection device in the above-mentioned background technology, improve the stability of the device, the working life and the detection performance, etc., the purpose of the present invention is to combine a class of HATCN with higher electron mobility and low LUMO energy level The Cu(I) complex constructed by it is used in organic ultraviolet photodetection devices to improve device performance and life, etc., and the synthesis method of the copper complex is simple, and the device is easy to prepare

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • hatcn and its construction of cu(i) complex as an organic ultraviolet photodetector with an anode buffer layer
  • hatcn and its construction of cu(i) complex as an organic ultraviolet photodetector with an anode buffer layer
  • hatcn and its construction of cu(i) complex as an organic ultraviolet photodetector with an anode buffer layer

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0053] ②. Preparation of Cu(I) complex Ⅰ (preparation of Cu(I) complex CuDH):

[0054] With 538.6mg (1.0mmol) two (2-diphenylphosphino) phenyl ether, 314.0mg (1.0mmol) [Cu (CH 3 EN) 4 ] BF 4 Dissolve in 10ml of dichloromethane, stir at room temperature for about 30 minutes, then add 384.3mg (1.0mmol) HATCN, and continue stirring for one hour. The final solution was rotary evaporated, and the obtained solid powder was CuDH.

[0055] ③. Preparation of Cu(I) complex II (preparation of Cu(I) complex CuBH):

[0056] With 446.5mg (1.0mmol) 1,2-bis (diphenylphosphino) benzene, 314.0mg (1.0mmol) [Cu (CH 3 EN) 4 ] BF 4 Dissolve in 10ml of dichloromethane, stir at room temperature for about 30 minutes, then add 384.3mg (1.0mmol) HATCN, and continue stirring for one hour. The final solution was rotary evaporated, and the obtained solid powder was CuBH.

Embodiment 1

[0058] select figure 1 The device structure shown, in the present embodiment, at first on the ITO anode 1, the anode buffer layer HATCN with a thickness of 7nm is vacuum-deposited, then an electron donor layer 3 of 30nm is deposited on the anode buffer layer 2, and then on the electron donor A mixed layer 4 of electron donor and electron acceptor with a weight ratio of 1:1 and a thickness of 40 nm is deposited on layer 3, and then a 40 nm electron acceptor layer 5 is deposited on the mixed layer 4, followed by a 1 nm electron injection layer 6 , and finally deposited a 200nm metallic Al cathode. All the above films are deposited by vacuum coating process, the thickness of the film is monitored by a film thickness monitor, and the external circuit is detected by KEITHLEY2601.

[0059] Effect: at a light intensity of 1.05mW / cm 2 , Under the irradiation of ultraviolet light with a center wavelength of 365nm and an external reverse bias of -12V, the photocurrent response value o...

Embodiment 2

[0061] On the basis of Example 1, the thickness of the anode buffer layer 2 was changed to 9 nm, and other manufacturing conditions remained unchanged.

[0062] Effect: at light intensity 1.05mW / cm 2 , Under the irradiation of light with a central wavelength of 365nm and an external reverse bias of -12V, the photocurrent response value of the device is 508mA / W (see figure 2 ), the current density is 0.53mA / cm 2 .

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention belongs to the field of organic photoelectric materials and organic ultraviolet light detection devices, and relates to a class of organic ultraviolet light detection devices with HATCN with high electron transport performance and the Cu(I) complex constructed therewith as an anode buffer layer. The structure of the device is: ITO anode, anode buffer layer, electron donor layer, donor acceptor mixed layer, electron acceptor layer, electron injection layer, cathode. It is characterized in that: HATCN and its monovalent copper complexes have high electron mobility, good film-forming properties and stability. Moreover, its very low LUMO energy level is beneficial for electrons to shuttle between the anode and the HOMO energy level of the donor, and can quickly recombine with the holes formed by the dissociation of excitons, which is conducive to hole transport through the charge recombination mechanism, thereby improving device performance. The use of the anode buffer layer material in the present invention greatly improves the performance of the organic ultraviolet light detection device, slows down the aging of the device, and improves the stability of the device.

Description

technical field [0001] The invention belongs to the field of materials and devices for organic ultraviolet photodetection devices, and specifically relates to a class of HATCN with high electron transport performance and Cu(I) complexes (monovalent copper complexes) constructed therefrom as anode buffer layer materials Organic UV photodetectors. Background technique [0002] Ultraviolet light detection device is a device that converts ultraviolet light into electrical signals, and has important applications in various fields such as military affairs, medical treatment, and the environment. Before the 1980s, the research on ultraviolet light detection devices mainly focused on inorganic semiconductors with wide band gaps such as GaN and SiC. The fabrication process of such ultraviolet light detection devices was complicated and costly. In recent years, ultraviolet light detection devices based on organic semiconductors have attracted widespread attention due to their wide se...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01L51/46H01L51/42
CPCH10K85/371H10K30/20Y02E10/549
Inventor 车广波刘敏刘春波苏斌徐占林孔治国
Owner JILIN NORMAL UNIV