A low-cost cable sheathing material, applied in the direction of plastic/resin/wax insulators, organic insulators, etc., can solve the problems of threatening life and property safety, poor chemical stability, short service life, etc., to reduce production costs and mechanical properties Good, long-lasting effect

Active Publication Date: 2014-10-08
ZHEJIANG XINYUANHONG MACROMOLECULE MATERIAL
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0002] With the development of the economy, the places where cables need to be used have become diversified, and there are more stringent and diverse requirements for the performance indicators of cable sheath materials, such as insulation, tensile strength, service temperature, flame retardant performance and other indicators There are strict requirements, and continuous improvement of the performance of sheath materials is an urgent need for economic and social development. Traditional sheath materials often have poor flame retardancy, poor chemical stability, high temperature deformation, poor mechanical properties, and short service life. And other problems, bring a lot of inconvenience to the actual use, and even threaten the safety of people's lives and property. Therefore, it is urgent to change the original sheath material formula and improve the material performance to meet the diverse needs of the cable market.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment

[0009] This embodiment contains the following raw materials in parts by weight: waste PET bottle flake particles 34, polyvinylidene fluoride 25, EVA 15, calcium-zinc composite stabilizer 3, ammonium molybdate 2, copper oxide 5, ferric oxide 4, hexameta Sodium phosphate 3, 10-hydroxy-2-decenoic acid 2, acetyl tri-n-butyl citrate 18, epoxy octyl stearate 13, calcium sulfate 6, N330 carbon black 40, antimony trioxide 6, additives 15.

[0010] The auxiliary agent contains the following raw materials in parts by weight: lapis lazuli 24, 1,6-hexamethylene diisocyanate 4, tripropylene glycol diacrylate 3, accelerator DM 4, ferric oxide 2, polytetrafluoroethylene 4 , iron slag powder 8, aluminum hydroxide 10, jade 3, calcium stearate 2, vinyltriethoxysilane 3, pepper seed oil 2; the preparation method is to put lapis lazuli and jade into a calciner at 570 Calcined at ℃ for 4 hours, cooled, crushed into 100 mesh, soaked in 15% hydrochloric acid solution for 3 hours, filtered out lapis...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
elongation at breakaaaaaaaaaa
electrical resistivityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a cable material and particularly relates to an oil-resistant and temperature-resistant PET cable sheath material with low cost. The material is prepared from the following raw materials in parts by weight: 30-34 parts of waste PET bottle particles, 23-25 parts of polyvinylidene fluoride, 12-15 parts of EVA, 2-3 parts of a calcium and zinc compound stabilizer, 1-3 parts of ammonium molybdate, 4-5 parts of copper oxide, 3-4 parts of iron sesquioxide, 2-3 parts of sodium hexametaphosphate, 1-2 parts of 10-hydyroxyl-2-caproleic acid, 16-18 parts of acetyl tri-n-butyl citrate, 12-13 parts of epoxy ethylhexyl stearate, 3-6 parts of calcium sulfate, 30-40 parts of N330 carbon black, 5-6 parts of antimonous oxide and 14-16 parts of an assistant. The insulating material combines the advantages of raw materials such as PET, polyvinylidene fluoride and EVA. The prepared material is high in strength, good in mechanical performance, can resist oil and chemical corrosion, can resist high temperature and low temperature aging, can resist oxidization and ray radiation and has a long service life. PET in the formula is a recycled waste, so that the production cost is effectively lowered, and the material has an extremely huge market popularization and application value.

Description

technical field [0001] The invention relates to a cable material, in particular to a low-cost oil-resistant and temperature-resistant PET cable sheath material and a preparation method thereof. Background technique [0002] With the development of the economy, the places where cables need to be used have become diversified, and there are more stringent and diverse requirements for the performance indicators of cable sheath materials, such as insulation, tensile strength, service temperature, flame retardant performance and other indicators There are strict requirements, and continuous improvement of the performance of sheath materials is an urgent need for economic and social development. Traditional sheath materials often have poor flame retardancy, poor chemical stability, high temperature deformation, poor mechanical properties, and short service life. And other problems, bring a lot of inconvenience to the actual use, and even threaten people's life and property safety, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L67/02C08L27/16C08L23/08C08K13/06C08K9/02C08K3/34C08K3/28C08K3/22C08K3/32C08K5/09C08K5/11C08K5/1515C08K3/30C08K3/04C08K5/098C08K5/5425H01B3/42H01B3/44
Inventor 谢华谢罡张静束维武
Owner ZHEJIANG XINYUANHONG MACROMOLECULE MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products