Corrosion resistant aluminum alloy surface treatment agent

A corrosion-resistant aluminum alloy and surface treatment agent technology, applied in anti-corrosion coatings, coatings, etc., can solve problems such as easy peeling off, serious environmental pollution, and uneven conversion film layer, and achieve the goal of enhancing corrosion resistance and reducing energy consumption Effect

Inactive Publication Date: 2014-10-22
RUIZHAN TONGLING TECH
View PDF6 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The commonly used method is anodic oxidation method, which forms a conversion film on the surface of aluminum alloy by electrochemical method. Although this method can improve the corrosion resistance of aluminum alloy, its ability to adapt to the environment is poor, and the conversion film layer is not uniform enough and easy to fall off. , the wear resistance has not been improved, and the traditional phosphate conversion and chromate passivation surface treatment technology can obtain good results, but the waste liquid discharged during the treatment process contains heavy metal ions such as zinc, manganese, nickel, chromium, etc. and sub-corrosion-resistant carcinogens, which pollute the environment very seriously, and the metal surface silanization treatment technology is considered to be expected to replace phosphate conversion treatment and chromium because it does not involve substances that are harmful to the environment, the production process has low energy consumption, and the technology has a wide range of applications. Salt passivation treatment is the latest development direction of metal surface protection alone

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0018] A corrosion-resistant aluminum alloy surface treatment agent, which is made up of the following raw materials in parts by weight:

[0019] Propyl gallate 0.7, sodium fluoroborate 4.2, calcium aluminate 1.6, sodium alginate 3.1, bauxite powder 0.4, xanthan gum 1.3, p-toluenesulfonic acid 3.1, hydroxypropyl methacrylate 0.4, trimethylol Propane diallyl ether 0.2, tetradecane dibasic acid 3.5, glycerin 4.1, film-forming aid 3, silane coupling agent KH560 20, deionized water 140;

[0020] Described film-forming aid is made up of the raw material of following weight part:

[0021] Polyethylene glycol 1000 26, sodium fluorosilicate 2, calcium acetylacetonate 0.3, ammonium molybdate 0.5, dipotassium glycyrrhizinate 2, Artemisia gum 1, polysorbate 80 1, silane coupling agent kh560 0.5, deionized water 80;

[0022] Sodium fluorosilicate, ammonium molybdate, and silane coupling agent kh560 are mixed and ball-milled evenly, and 20-30% of the weight of the above-mentioned deioniz...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a corrosion resistant aluminum alloy surface treatment agent, which is composed of the following raw materials by weight: 0.7-1 part of propyl gallate, 4.2-5 parts of fluoride sodium borate, 1-1.6 parts of calcium aluminate, 2-3.1 parts of sodium alginate, 0.2-0.4 parts of bauxite powder, 1-1.3 parts of xanthan gum, 2-3.1 parts of toluene-p-sulfonic acid, 0.2-0.4 part of methyl hydroxypropyl acrylate, 0.1-0.2 part of trimethylolpropane diallyl ether, 2-3.5 parts of tetradecanedioic acid, 3-4.1 parts of glycerol, 1-3 parts of a coalescent, 16-20 parts of a silane coupling agent KH560 and 110-140 parts of deionized water. The surface treatment agent provided by the invention can form a strong protective film on the aluminum alloy surface to enhance the corrosion resistance of the substrate; the surface treatment agent provided by the invention does not contain carcinogenic substances such as nitrate and nitrite; and waste liquid can be discharged through simple neutralization treatment, so as to reduce energy consumption.

Description

[0001] technical field [0002] The invention mainly relates to the field of surface treatment, in particular to a corrosion-resistant aluminum alloy surface treatment agent. Background technique [0003] There are many surface treatment methods for aluminum alloys, such as physical methods, chemical methods, physicochemical methods, and comprehensive methods. The commonly used method is anodic oxidation method, which forms a conversion film on the surface of aluminum alloy by electrochemical method. Although this method can improve the corrosion resistance of aluminum alloy, its ability to adapt to the environment is poor, and the conversion film layer is not uniform enough and easy to fall off. , the wear resistance has not been improved, and the traditional phosphate conversion and chromate passivation surface treatment technology can obtain good results, but the waste liquid discharged during the treatment process contains heavy metal ions such as zinc, manganese, nick...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D183/06C09D5/08C09D7/12
Inventor 徐泽军
Owner RUIZHAN TONGLING TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products