Looking for breakthrough ideas for innovation challenges? Try Patsnap Eureka!

Thermosetting acrylic powder paint for ceramics

A powder coating and acrylic technology, applied in the field of coatings, can solve problems such as low gloss retention, low hardness, low temperature resistance and chemical corrosion resistance

Active Publication Date: 2015-01-21
盐城市盐龙水务有限公司
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Aiming at the above technical problems, the present application provides a thermosetting acrylic powder coating for ceramics, which solves the technical problems of the existing thermosetting acrylic powder coatings for ceramics such as low gloss retention and hardness, low temperature resistance and poor chemical corrosion resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0014] A kind of thermosetting acrylic powder coating for ceramics, its raw material ratio is as follows by weight: 100 parts of hydroxyethyl methacrylate; 1 part of benzoic acid; 5 parts of acrylic acid; 20 parts of butanol; 10 parts of cumene peroxide; 50 parts of modified polyethylene glycol phthalate glue; 5 parts of melamine resin; 70 parts of xylene; 10 parts of azobisisobutyronitrile; 1 part of ethanolamine; 1 part of DBP; 0.5 parts of manganese naphthenate; 20 parts of isocyanate ; 30 parts of titanium dioxide; 50 parts of styrene.

[0015] Put the above raw materials into the reaction kettle, raise the temperature to 80°C, keep warm for 2 hours and mix evenly, after cooling, pulverize with a pulverizer, and sieve with a 100mg sieve to prepare the coating.

[0016] Gloss is 130%, after artificial accelerated aging for 500 hours, the gloss retention rate is 92%; Shore hardness is 45, no blistering or falling off after soaking in water for 30 days, no abnormality after s...

Embodiment 2

[0018] A kind of thermosetting acrylic powder coating for ceramics, its raw material ratio is as follows by weight: 100 parts of hydroxyethyl methacrylate; 5 parts of benzoic acid; 15 parts of acrylic acid; 40 parts of butanol; 20 parts of cumene peroxide; 70 parts of modified polyethylene glycol phthalate glue; 15 parts of alkyl modified organosiloxane; 90 parts of xylene; 30 parts of azobisisobutyronitrile; 3 parts of ethanolamine; 10 parts of DBP; manganese naphthenate 1.5 parts; 30 parts of isocyanate; 40 parts of titanium dioxide; 60 parts of styrene.

[0019] Put the above raw materials into the reaction kettle, raise the temperature to 100°C, keep warm for 4 hours and mix evenly, after cooling, pulverize with a pulverizer, and sieve with a 150mg sieve to prepare the coating.

[0020] Gloss is 140%, after artificial accelerated aging for 500 hours, the gloss retention rate is 94%; Shore hardness is 55, no blistering or falling off after soaking in water for 45 days, no a...

Embodiment 3

[0022] A kind of thermosetting acrylic powder coating for ceramics, its raw material ratio by weight is as follows: 100 parts of hydroxyethyl methacrylate; 4 parts of benzoic acid; 25 parts of acrylic acid; 3 parts of butanol; 8 parts of cumene peroxide; 4 parts of modified polyethylene glycol phthalate glue; 10 parts of alkyl modified organosiloxane; 7 parts of xylene; 85 parts of azobisisobutyronitrile; 9 parts of ethanolamine; 5 parts of DOP; manganese naphthenate 5 parts; 2 parts of isocyanate; 35 parts of titanium dioxide; 30 parts of styrene.

[0023] Put the above raw materials into the reaction kettle, raise the temperature to 90°C, keep warm for 3 hours and mix evenly, after cooling, pulverize with a pulverizer, and sieve with a 125mg sieve to prepare a coating.

[0024] Gloss is 150%, after artificial accelerated aging for 500 hours, the gloss retention rate is 96%; Shore hardness is 65, no blistering or falling off after soaking in water for 60 days, no abnormality ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Melting pointaaaaaaaaaa
Densityaaaaaaaaaa
Melting pointaaaaaaaaaa
Login to View More

Abstract

The invention discloses thermosetting acrylic powder paint for ceramics. The thermosetting acrylic powder paint for ceramics is prepared from the following raw materials: hydroxyethyl methylacrylate, benzoic acid, acrylic acid, butanol, cumene peroxide, modified polyethylene terephthalate gum, a leveling agent, dimethyl benzene, azodiisobutyronitrile, ethanol amine, a plasticizer, manganese naphthenate, isocyanate, titanium dioxide and styrene. The thermosetting acrylic powder paint for ceramics has glossiness of 130%-150%, a gloss retention rate of 92-96% after manually accelerating ageing for 500 hours, shore hardness of 45-65, no bubbling and dropping phenomena after being soaked in water for 30-60 days, no abnormity after being soaked in 5% hydrochloric acid solution for 25-35 days, adhesion of levels 1-2, impact strength of 500-600N / cm, no bubbling and wrinkling phenomena after being soaked in saturated calcium hydroxide for 30-40 days, a product smelting point of 150-160 DEG C and density of 120-140g / cm<3>.

Description

technical field [0001] The application belongs to the field of coatings, in particular to a thermosetting acrylic powder coating for ceramics. Background technique [0002] Ceramics are various products made of natural clay and various natural minerals as the main raw materials through crushing, kneading, molding and calcination. In the past, people called ceramics made of clay and fired at high temperature in special kilns. Ceramics is the general term for pottery and porcelain. The traditional concept of ceramics refers to all artificial industrial products that use inorganic non-metallic minerals such as clay as raw materials. It includes various products made of clay or a mixture containing clay through kneading, shaping, and calcination. It ranges from the roughest earthenware to the finest fine pottery and porcelain. Its main raw material is silicate minerals (such as clay, quartz, etc.) taken from nature, so it belongs to the category of "silicate industry" togethe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D4/00C09D4/06C09D5/03C09D7/12C04B41/85
Inventor 马志明
Owner 盐城市盐龙水务有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com