TK-JH mineral interface active material, and preparation method and application method thereof

An interface active material, TK-JH technology, applied in the field of TK-JH mineral interface active material and its preparation, can solve problems such as high pollution, high energy consumption, and impact on the durability of structures, and achieve high hydration heat and early The effect of demoulding and saving rental fees

Active Publication Date: 2015-04-08
苏笮斌
View PDF5 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the production of cement is not only a product of high energy consumption and high pollution, but also affects the durability of the structure after use.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • TK-JH mineral interface active material, and preparation method and application method thereof
  • TK-JH mineral interface active material, and preparation method and application method thereof
  • TK-JH mineral interface active material, and preparation method and application method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0035] Take the preparation of 10,000 liters of product as an example

[0036] Prepare the liquid product and solid product of the TK-JHTK-JH type mineral interfacial active (agent) material combination, and its proportioning is calculated according to the weight percentage, puts 5000 kilograms of sulfuric acid into the reactor, heats up to 80 ℃, under the situation of stirring , put in 3000 kg of fly ash, 1000 kg of silica fume, and 1000 kg of phosphorus slag in turn. After 6 hours of extraction reaction, through precipitation, separation, and pressure filtration, a mixture containing sulfur, aluminum, silicon, and phosphate is obtained. The solid content is 40-45%, put the mixed solution evenly into the dissolved polyether plasticizer with a solid content of 40% by dropping, the ratio is: 50% of the mixed solution is 5000 kg, polyether plasticized The agent liquid is 4800 kg. After fully stirring and polymerizing for 4 hours at a temperature of 35 ° C, add 200 kg of triisopr...

Embodiment 2

[0038] Take the preparation of 10,000 liters of product as an example

[0039] Prepare the liquid and solid product of TK-JHTK-JH type mineral interfacial active (agent) material composition, calculate by weight percent, add solid content and be 5000 kilograms of polycarboxylate water-reducing plasticizers of 45% in reactor, Then add 1,500 kg of tap water, stir well, and control the temperature at 45°C, then add 1,500 kg of aluminum sulfate, 1,000 kg of ferrous sulfate, 500 kg of water glass, 300 kg of sodium phosphate, and 200 kg of triethanolamine to fully dissolve After 6 hours of polymerization reaction, cool down to normal temperature, then detect, discharge, measure, pack, store, and obtain TK-JH type mineral interface active (agent) material composition liquid product. Further spray and dry to obtain a solid product of TK-JH type mineral interface active (agent) material composition.

Embodiment 3

[0041] Take the preparation of 10,000 liters of product as an example

[0042] Prepare the liquid and solid products of the TK-JH type mineral interface active (agent) material composition, calculated by weight percentage, add 3000 kilograms of solid low-iron aluminum sulfate, 2200 kilograms of aluminum potassium sulfate, and 2000 kilograms of ultrafine silicon micropowder in the reactor , 1,500 kilograms of melamine water-reducing plasticizer, 500 kilograms of sodium sulfonate, and 500 kilograms of sodium tripolyphosphate were mixed and matured for 4 hours at 60°C, and 300 kilograms of diethanolamine was sprayed into it, and then stirred and matured for 1 hour. Hour, be cooled to normal temperature, discharge, detect, measure, put in storage, obtain solid TK-JH type mineral interface active (agent) material, further calculate according to weight percentage, add equivalent tap water, promptly join with 5000 kilograms of solid products 5000 kg of tap water, fully stirred and di...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a TK-JH mineral interface active material, and a preparation method and application method thereof. The TK-JH mineral interface active material is composed of the following components in percentage by weight: 30-60% of sulfate, 20-30% of silicate, 20-30% of plasticizing and water reducing agent, 3-6% of phosphate and 1-3% of alkylol amine salt. The TK-JH mineral interface active material can perform green revolution on the cementing material and foundation work, can make great contribution to energy saving and environmental protection, protection of mine resources, utilization of waste resources, sustainable development of circular economy and great exploits of centuries, and can become historical transitions in sunrise industry of cementing material and application of construction industry new materials in construction industry.

Description

technical field [0001] The invention relates to a TK-JH type mineral interface active material, a preparation method and an application method thereof. Background technique [0002] The basic engineering in buildings (and structures) requires cementitious materials as components for bonding, solidification and strengthening. Calcined limestone and cement become the main cementitious materials in construction engineering to configure cement concrete and mortar, that is, to manufacture artificial stone. Therefore, cement and lime and other cementitious materials have already become indispensable, necessary and important structure components in the concrete and mortar of the foundation engineering of the construction industry. From 2005 to now, my country's annual cement production and sales have reached 2.3 billion tons for ten consecutive years, ranking first in the world, accounting for more than 35% of the global cement production and sales. [0003] With the acceleration ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C04B24/32C04B24/24C04B24/18C04B24/20
CPCC04B28/04C04B28/26C04B28/34C04B20/1077C04B14/06C04B12/04C04B14/042C04B14/043C04B22/14C04B22/143C04B22/147C04B22/148C04B22/149C04B22/16C04B22/165C04B24/10C04B24/121C04B24/122C04B24/18C04B24/223C04B24/226C04B24/24C04B24/2647C04B24/38C04B24/383C04B2103/302C04B2103/61C04B7/02
Inventor 苏笮斌梁玉祥成子桥陈钒苏琳
Owner 苏笮斌
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More