Turpentine-C9/C5 petroleum resin blend hydrogenation modification method and device

A technology of petroleum resin and rosin, which is applied in the field of blending and hydrogenation of rosin and C9/C5 petroleum resin, can solve the problem of poor thermal stability and oxidative stability of the resin, reduce the compatibility between the resin and the application object, and limit the application. Scope and other issues, to achieve the effect of being beneficial to manufacturing, reducing the thermal power conversion process, and improving thermal power efficiency

Active Publication Date: 2015-06-10
GUANGXI UNIV
View PDF2 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] The C9 / C5 petroleum resin obtained through thermal polymerization or catalytic polymerization will contain a certain amount of double bond unsaturated compounds, darker in color, low in softening degree, poor in stability, and prone to reactions under the action of ultraviolet rays, oxygen or other chemical substances , making the thermal stability and oxidation stability of the resin worse, and also reducing the compatibility between the resin and the application object; especially C9 / C5 petroleum resin contains a small amount of organic sulfur, which is easy to poison the catalyst and limit its application range

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Turpentine-C9/C5 petroleum resin blend hydrogenation modification method and device
  • Turpentine-C9/C5 petroleum resin blend hydrogenation modification method and device
  • Turpentine-C9/C5 petroleum resin blend hydrogenation modification method and device

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] like Figure 1-4 As shown, the device for blending hydrogenation modification of pine resin and C9 / C5 petroleum resin includes: dissolution kettle 1, hydrogenation reactor 2, expander 3, gas-liquid separator 4, absorption tower 5, turbine compression Machine 6, solvent pump 7.

[0041] The discharge port of the dissolution tank 1 is connected with the feed port of the hydrogenation reactor 2, and the dissolution tank 1 is used for dissolving raw materials required for production. The hydrogenation reactor 2 is cylindrical. The upper part of the hydrogenation reactor is provided with a feed inlet 21, a gas outlet 22, and the bottom is provided with a discharge outlet 23. The hydrogenation reactor 2 includes a heating pipe 24, which is a heating coil. It is arranged inside the hydrogenation reactor; the gas distributor 25 includes an air inlet 251 and a plurality of nozzles 252 for exhaust; the expander 3 is connected to the gas outlet of the hydrogenation reactor 2 . T...

Embodiment 2

[0050] The reaction unit that uses is identical with embodiment 1, a kind of method for rosin and C9 / C5 petroleum resin blending hydrogenation modification, comprises the following steps:

[0051] (1) Prepare raw materials, use turpentine and C9 / C5 petroleum resin as raw materials, mix its hydrogenated turpentine and modified bentonite loaded nickel, add turpentine, C9 / C5 petroleum resin and solvent in a mass ratio of 1:3:1, The amount of nickel loaded on the modified bentonite is 10% of the total mass of turpentine and C9 / C5, put it into the dissolution kettle 1, and heat to dissolve;

[0052] (2) Hydrogenation reaction, put the mixture prepared in step (1) into the hydrogenation reactor 2, then heat the temperature up to 150°C, and fill the hydrogenation reactor with a molar ratio of H 2 :CO 2 = 1:1 mixed gas until the pressure is 10.0MPa, continue to heat up to 250°C;

[0053] (3) Maintain the pressure in the hydrogenation reactor 2 to be 10.0MPa, open the gas outlet 22 o...

Embodiment 3

[0056] The reaction unit that uses is identical with embodiment 1, a kind of method for rosin and C9 / C5 petroleum resin blending hydrogenation modification, comprises the following steps:

[0057] (1) Prepare raw materials, take turpentine and C9 / C5 petroleum resin as raw materials, mix its hydrogenated turpentine and modified bentonite loaded nickel, add turpentine, C9 / C5 petroleum resin and solvent in a mass ratio of 10:10:1, The amount of nickel loaded on the modified bentonite is 30% of the total mass of turpentine and C9 / C5, put into the dissolution kettle 1, and heat to dissolve;

[0058] (2) Hydrogenation reaction, put the mixture prepared in step (1) into the hydrogenation reactor 2, then heat the temperature up to 150°C, and fill the hydrogenation reactor with a molar ratio of H 2 :CO 2 = 20:1 mixed gas until the pressure is 7.0MPa, continue to heat up to 250°C;

[0059] (3) Maintain the pressure in the hydrogenation reactor 2 at 7.0MPa, open the gas outlet 22 on th...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a turpentine-C9 / C5 petroleum resin blend hydrogenation modification method which comprises the following steps: (1) raw material preparation: mixing raw materials turpentine and C9 / C5 petroleum resin with a solvent and a catalyst, and dissolving by heating; (2) hydrogenation reaction: putting the mixture prepared in the step (1) into a hydrogenation reactor, charging a gas mixture of H2 and CO2 in a mole ratio of 1:1-20:1, and carrying out hydrogenation reaction at 150-400 DEG C under the pressure of 3.0-35.0 MPa; (3) taking out the reacted gas mixture in the hydrogenation reactor, passing the gas through an expander which is connected with a turbine compressor, supplementing the CO2-H2 gas mixture into the turbine compressor, and introducing the gas mixture into the hydrogenation reactor; and (4) after carrying out hydrogenation-desulfurization reaction for 1-10 hours, relieving the pressure, and discharging the blend hydrogenation modified turpentine-C9 / C5 petroleum resin product out of the hydrogenation reactor. The method enhances the hydrogenation-desulfurization reaction speed and equilibrium conversion rate, and implements coupling of the hydrogenation reaction and desulfurization separation.

Description

technical field [0001] The invention relates to the field of deep processing of rosin, in particular to a method and device for blending and hydrogenating modification of rosin and C9 / C5 petroleum resin. Background technique [0002] C9 / C5 petroleum resin is a thermoplastic hydrocarbon resin formed by pretreatment, polymerization and distillation of the C9 fraction of pyrolysis gasoline, a by-product in the process of pyrolysis of petroleum hydrocarbons to prepare ethylene. It has the characteristics of high resistance, cohesiveness and easy compatibility with other resins, and has low acid value, water resistance, alcohol resistance and chemical resistance, good chemical stability and thermal stability, and can adjust viscosity. It is widely used in paints, rubbers, inks , Hot melt, adhesive tape and adhesive industry. Adding C9 / C5 petroleum resin to the paint can increase the gloss of the paint, improve paint adhesion, hardness, acid resistance and alkali resistance; addi...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08F240/00C08F8/04C08L57/02C08L93/00C08L93/04C09F1/04B01J8/08
Inventor 陈小鹏王琳琳韦小杰梁杰珍周龙昌丁永辉唐伟超韦彩琴张鹏鹏
Owner GUANGXI UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com