Modified waste PVC-based active carbon-loaded nano arsenic sulfide composite electrode material and preparation method thereof

A technology based on activated carbon and composite electrodes, which is applied in the manufacture of hybrid capacitor electrodes and hybrid/electric double layer capacitors. It can solve the problems of generating a large amount of harmful smoke, less waste disposal, and lower product quality, and achieve high specific capacitance. , fast charge and discharge rate, high conductivity

Inactive Publication Date: 2015-08-19
ANHUI JIANGWEI PRECISION IND
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The landfill method will occupy a large amount of arable land, the incineration method will produce a large amount of harmful smoke and HCl, and the recycled material method will reduce product quality, the application range is limited, and the amount of waste disposal is also small

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0011] specific implementation plan

[0012] The present invention will be described in detail below through specific examples.

[0013] A modified waste PVC-based activated carbon-loaded nano-arsenic sulfide composite electrode material, which is made of the following raw materials in parts by weight (kg): sodium pyrophosphate 2, polymethyl methacrylate resin 2, tetrahydrofuran 6, nano-arsenic sulfide 3, Nano Dysprosium Sulfide 2, Beryllium Oxide 1, Modified Waste PVC-based Activated Carbon 120, Dextrin 3, Distilled Water 15, Isopropyl Distearoyl Aluminate 2;

[0014] The modified waste PVC-based activated carbon is made of the following raw materials in parts by weight (kg): sodium sulfate 2, aluminum potassium sulfate 1, tourmaline 2, aminopropyltriethoxysilane 2, calcium stearate 1, Aluminum nitride powder 2, graphene oxide 2, waste PVC material 500, calcium hydroxide 20, 20% sulfuric acid 45; the preparation method is to crush and sieve the waste PVC material to obtain...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a modified waste PVC-based active carbon-loaded nano arsenic sulfide composite electrode material, and is characterized by being prepared from the following raw materials in parts by weight: 1 part to 2 parts of sodium pyrophosphate, 1 part to 3 parts of polymethyl methacrylate resin, 4 to 7 parts of tetrahydrofuran, 2 to 4 parts of nano arsenic sulfide, 1 part to 2 parts of nano dysprosium sulfide, 1 part to 2 parts of beryllia, 110 to 130 parts of modified waste PVC-based active carbon, 2 to 3 parts of dextrin, 10 to 15 parts of distilled water, and 1 part to 2 parts of distearoyl isopropoxy aluminate. The preparation method provided by the invention uses waste PVC to prepare electrode material active carbon which has the advantages of large specific surface area, high conductivity and the like, resources are utilized in a rationalized manner, the problem of environmental pollution is solved, the electrode material is doped with a metallic element having a conductive function and surface coating is performed with the nitrogen element, and a prepared supercapacitor has the advantages of high specific capacitance, high charge/discharge rate, good cycle stability and long usage time.

Description

technical field [0001] The invention relates to the field of chemical energy materials, in particular to a modified waste PVC-based activated carbon-loaded nano arsenic sulfide composite electrode material and a preparation method thereof. Background technique [0002] Chlorine-containing PVC waste is difficult to degrade at room temperature, and the main treatment methods are landfill, incineration and recycled materials. The landfill method will occupy a large amount of cultivated land, the incineration method will produce a large amount of harmful smoke and HCl, and the recycled material method will reduce the product quality, the application range is limited, and the amount of waste disposal is also small. The amount of discarded plastics in my country is about 2 million tons every year. The huge amount of polymer waste has caused serious environmental pollution and waste of natural resources. Therefore, the recycling and reuse of discarded PVC has significant economic ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): H01G11/32H01G11/86
CPCY02E60/13H01G11/30H01G11/34H01G11/38H01G11/44H01G11/86
Inventor 刘勇童翔熊文华
Owner ANHUI JIANGWEI PRECISION IND
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products