Fluorescent compound with pyrochlore structure lanthanum titanate as matrix and preparation method and application

A fluorescent compound and pyrochlore structure technology, applied in the field of fluorescent compounds, can solve the problems of lack of red emission components, insufficient color rendering index, and insufficient luminous intensity, etc., and achieve the effect of stable chemical properties

Active Publication Date: 2017-01-25
NORTHEASTERN UNIV LIAONING
View PDF3 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, the emission of single-matrix white light-emitting fluorescent materials generally has problems such as lack or insufficient red emission components, insufficient color rendering index, and insufficient luminous intensity.
In the La-Ti-O ternary system, there are no fluorescent compounds based on pyrochlore-structured lanthanum titanate, which have been reported in related reports.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fluorescent compound with pyrochlore structure lanthanum titanate as matrix and preparation method and application
  • Fluorescent compound with pyrochlore structure lanthanum titanate as matrix and preparation method and application
  • Fluorescent compound with pyrochlore structure lanthanum titanate as matrix and preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0044] Pyrochlore structure lanthanum titanate-based fluorescent compound, the chemical formula is La 1.98 Dy 0.02 TiO 5 , made by the following steps:

[0045] (1) Weigh 1.98 mmol of lanthanum nitrate and 0.02 mmol of dysprosium acetate and dissolve them in deionized water to obtain solution A; weigh 1 mmol of tetrabutyl titanate and dissolve them in 50 mL of methanol to obtain solution B;

[0046] (2) Mix solution A and solution B, add 4 mmol acetic acid dropwise to make the pH<3, stir for 1 hour to obtain a clear solution C, raise the temperature of solution C to 50°C, and keep it in a water bath for 3 hours to obtain a precursor gel;

[0047] (3) Put the precursor gel in a corundum crucible, calcined in a muffle furnace, and calcined in an air atmosphere at a temperature of 1100° C., calcined for 4 hours, kept for 2 hours, and cooled to room temperature with the furnace to obtain a calcined product;

[0048] (4) The calcined product is pulverized, ground, passed through...

Embodiment 2

[0051] Pyrochlore structure lanthanum titanate-based fluorescent compound, the chemical formula is La 1.972 Dy 0.02 SM 0.008 TiO 5 , made by the following steps:

[0052] (1) Weigh 1.972mmol of lanthanum acetate, 0.02mmol of dysprosium carbonate and 0.008mmol of samarium acetate and dissolve them in deionized water to obtain solution A; weigh 1mmol of tetrabutyl titanate and dissolve them in 60mL of ethanol to obtain solution B;

[0053] (2) Mix solution A and solution B, add 30 mmol of carbonic acid dropwise to make the pH<3, stir for 2 hours to obtain a clear solution C, raise the temperature of solution C to 150°C, and keep it in a water bath for 6 hours to obtain a precursor gel;

[0054] (3) Put the precursor gel in a corundum crucible, calcined in a muffle furnace, and calcined in an air atmosphere at a temperature of 1200° C., calcined for 2 hours, kept for 3 hours, and cooled to room temperature with the furnace to obtain a calcined product;

[0055] (4) The calcin...

Embodiment 3

[0058] Pyrochlore structure lanthanum titanate-based fluorescent compound, the chemical formula is La 1.968 Dy 0.02 SM 0.012 TiO 5 , made by the following steps:

[0059] (1) Weigh 1.968 mmol of lanthanum carbonate, 0.02 mmol of dysprosium nitrate and 0.012 mmol of samarium nitrate and dissolve them in deionized water to obtain solution A; weigh 1 mmol of tetrabutyl titanate and dissolve them in 70 mL of propanol to obtain solution B;

[0060] (2) Mix solution A and solution B, add 25 mmol of nitric acid dropwise to make the pH<3, stir for 1.5 hours to obtain a clear solution C, raise the temperature of solution C to 60°C, keep it in a water bath for 4 hours, and obtain a precursor gel;

[0061] (3) Put the precursor gel in a corundum crucible, calcined in a muffle furnace, and calcined in an air atmosphere at a temperature of 900° C., calcined for 6 hours, kept for 4 hours, and cooled to room temperature with the furnace to obtain a calcined product;

[0062] (4) The calc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a fluorescent compound with pyrochlore structure lanthanum titanate as the matrix. The general formula of the fluorescent compound is La2(1-x)M2xTiO5, where M is Dy and / or Sm, 0.01≤x≤0.02, The preparation method includes the following steps: dissolve the soluble salt of La and the soluble salt of Sm and / or Dy in deionized water to obtain solution A; mix tetrabutyl titanate and alcohol to obtain solution B; mix solution A and solution B, and drip Add acid and stir to obtain solution C. Heat solution C to 50°C to 150°C and keep it warm to obtain a precursor gel; calcine the precursor gel to obtain a calcined product; crush, grind, wash, and dry the calcined product to obtain it, which can be used For preparing luminescent materials for white LEDs. The fluorescent compound of the present invention has good luminescence properties, high luminous intensity and good color rendering; the preparation method of the present invention has a low calcination temperature, a simple preparation method and low cost, and can meet the requirements in the field of white LED lighting.

Description

technical field [0001] The invention relates to a fluorescent compound with a pyrochlore structure lanthanum titanate as a matrix, a preparation method and an application, and belongs to the technical field of fluorescent compounds. Background technique [0002] White LED has the advantages of high energy efficiency, small size, long life, low pollution, etc., and is known as a new generation of "green lighting" light source. At present, white light LEDs are mainly realized through phosphor light conversion, including two types of light conversion, one is to effectively excite YAG:Ce through blue LED chips 3+ Yellow phosphor uses the combination of the blue light emitted by the chip and the yellow light emitted by the phosphor to form white light, but due to the lack of red light, the color rendering is poor, and the wavelength band of the phosphor doped with YAG is too narrow, concentrated in a certain range The other is to generate red, yellow, and blue colors into white ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C09K11/78H01L33/50
CPCY02B20/00
Inventor 刘宣文齐建全马振伟白永一和朝阳张杨郭瑞
Owner NORTHEASTERN UNIV LIAONING
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com