Waterproof antibacterial marine coating

A coating and marine technology, applied in the field of waterproof and antibacterial marine coatings, can solve the problems of shortening the service life of marine coatings, poor waterproof and antibacterial performance, and limiting the application of marine coatings, so as to shorten the surface drying time, improve hardness, and prevent penetration Effects inside the coating

Inactive Publication Date: 2015-09-30
WUHU SHUANGBAO BUILDING MATERIAL
View PDF4 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the hardness of the existing marine coatings is not very ideal. During the sailing process of the ship, it is easy to be scratched and loses its performance. In addition, its water resistance and antibacterial properties are not good, which shortens the service life of the marine coatings and limits them. Application of Marine Coatings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] A kind of waterproof and antibacterial marine coating proposed by the present invention, its raw material comprises the following components by weight: 45 parts of fluorosilicon modified acrylic acid emulsion, 45 parts of vinyl acetate emulsion, 4 parts of polypropylene fiber, 15 parts of silicon nitride, graphite oxide 1 part, 35 parts of liquid petroleum resin, 1 part of ethylene glycol dimethacrylate, 5 parts of 3-methacryloxypropyl trimethoxysilane, 0.5 parts of tri-n-butyl phosphate, 8 parts of oxidized starch, 5 parts of polyvinyl alcohol, 3 parts of ethylene glycol, 1 part of dipropylene glycol butyl ether, 1 part of hydroxypropyl distarch phosphate, 0.3 parts of sodium gluconate, 1.5 parts of 2-furan-dimethylsilanol, 5 parts of additives parts, 35 parts of water;

[0018] Wherein, the fluorosilicon-modified acrylic emulsion is prepared according to the following process: 40 parts by weight of dodecafluoroheptyl methacrylate, 16 parts of methacryloyloxypropyl tri...

Embodiment 2

[0020] A waterproof and antibacterial marine coating proposed by the present invention, its raw materials include the following components by weight: 60 parts of fluorosilicon modified acrylic emulsion, 30 parts of vinyl acetate emulsion, 10 parts of polypropylene fiber, 5 parts of silicon nitride, graphite oxide 5 parts, 20 parts of liquid petroleum resin, 3 parts of ethylene glycol dimethacrylate, 2 parts of 3-methacryloxypropyl trimethoxysilane, 2 parts of tri-n-butyl phosphate, 3 parts of oxidized starch, 10 parts of polyvinyl alcohol, 1 part of ethylene glycol, 4 parts of dipropylene glycol butyl ether, 0.3 parts of hydroxypropyl distarch phosphate, 1.5 parts of sodium gluconate, 0.3 parts of 2-furan-dimethylsilanol, corrosion inhibitor 10 parts, 20 parts of water;

[0021]Wherein, the fluorosilicon-modified acrylic emulsion is prepared according to the following process: 50 parts by weight of dodecafluoroheptyl methacrylate, 10 parts of methacryloyloxypropyl tris(trimeth...

Embodiment 3

[0023] A kind of waterproof and antibacterial marine coating proposed by the present invention, its raw material comprises the following components by weight: 55 parts of fluorosilicon modified acrylic acid emulsion, 39 parts of vinyl acetate emulsion, 6.7 parts of polypropylene fiber, 10 parts of silicon nitride, graphite oxide 3.8 parts, 30 parts of liquid petroleum resin, 2 parts of ethylene glycol dimethacrylate, 4 parts of 3-methacryloxypropyl trimethoxysilane, 1.4 parts of tri-n-butyl phosphate, 5.6 parts of oxidized starch, 7.5 parts of polyvinyl alcohol, 2 parts of ethylene glycol, 2.3 parts of dipropylene glycol butyl ether, 0.58 parts of hydroxypropyl distarch phosphate, 1 part of sodium gluconate, 1 part of 2-furan-dimethylsilanol, defoamer 3.5 parts, 5.2 parts of thickener, 28 parts of water;

[0024] Wherein, the fluorosilicon-modified acrylic emulsion is prepared according to the following process: 20 parts by weight of dodecafluoroheptyl methacrylate, 25 parts o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a waterproof antibacterial marine coating. Raw materials of the marine coating comprise the following ingredients, by weight, 45-60 parts of a fluorine-silicon modified acrylic emulsion, 30-45 parts of a vinyl acetate emulsion, 4-10 parts of polypropylene fiber, 5-15 parts of silicon nitride, 1-5 parts of graphite oxide, 20-35 parts of liquid petroleum resin, 1-3 parts of ethylene dimethacrylate, 2-5 parts of 3-methacryloxy propyl trimethoxy silane, 0.5-2 parts of tri-n-butyl phosphate, 3-8 parts of oxidized starch, 5-10 parts of polyvinyl alcohol, 1-3 parts of glycol, 1-4 parts of dipropylene glycol mono butyl ether, 0.3-1 part of hydroxy propyl distarch phosphate, 0.3-1.5 parts of sodium gluconate, 0.3-1.5 parts of 2-furan-dimethyl silanol, 5-10 parts of an auxiliary agent and 20-35 parts of water. The waterproof antibacterial marine coating brought forward in the invention has advantages of high hardness, excellent waterproofness and antibacterial property, good comprehensive performance and long service life.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a waterproof and antibacterial marine coating. Background technique [0002] Marine coatings are a general term for coatings used in various parts of ships and marine engineering structures to meet the special requirements of preventing seawater, marine atmospheric corrosion, marine organisms, and other special requirements. Coatings used for ships are required to have good adhesion, good water resistance, chemical resistance and abrasion resistance; they can be used under harsh conditions such as the ocean, and have a long-term anti-rust life. It can be used for up to 10 or 15 years. However, the hardness of the existing marine coatings is not very ideal. During the sailing process of the ship, it is easy to be scratched and loses its performance. In addition, its water resistance and antibacterial properties are not good, which shortens the service life of the marine coatings...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D4/02C09D4/06C09D5/14C09D5/16C09D7/12C09D7/00C08F220/22C08F230/08C08F220/18
Inventor 胡昌悌
Owner WUHU SHUANGBAO BUILDING MATERIAL
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com