Recyclable oil absorbing composite material and preparation method therefor
What is Al technical title?
Al technical title is built by PatSnap Al team. It summarizes the technical point description of the patent document.
A technology of composite materials and sodium-based bentonite, which is applied in the field of oil-absorbing composite materials and its preparation, can solve problems such as the inability to suppress the volatility of highly volatile liquids, unsatisfactory chemical treatment effects, and large specific surface area, so as to improve adsorption speed and Adsorption range, enhanced hydrophobicity and lipophilicity, good dispersion effect
Inactive Publication Date: 2015-10-28
ANHUI CHENGFANG NEW MATERIAL TECH
View PDF1 Cites 2 Cited by
Summary
Abstract
Description
Claims
Application Information
AI Technical Summary
This helps you quickly interpret patents by identifying the three key elements:
Problems solved by technology
Method used
Benefits of technology
Problems solved by technology
However, as an adsorption material, this material has some disadvantages, namely, oil absorption and water absorption, and leakage after absorption after extrusion. Due to the porous structure, the specific surface area is large, and the volatility of the absorbed highly volatile liquid cannot be suppressed, which is harmful to toxic and explosive chemicals. Product processing effect is not ideal
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0011] specific implementation plan
[0012] The present invention will be described in detail below through specific examples.
[0013] A recyclable oil-absorbing composite material and its preparation method are prepared from the following raw materials in parts by weight (kg): sodium bentonite 5, cetyltrimethylammonium bromide 0.5, methacrylate 6, Styrene 4, 1,6-hexanediol diacrylate 0.4, ethyl acetate 4, polyvinyl alcohol 2, organic phosphate 1.2, potassium persulfate 0.04, sodium bicarbonate 0.7, polyethylene wax 4, stearic acid 2. Calcium sulfate 2, polypropylene 90, antioxidant 10100.2, azodicarbonamide 13, silane coupling agent kh5500.7, peat 3, lanthanum nitrate 0.7, silicon acrylic emulsion 2, appropriate amount of water;
[0014] A recyclable oil-absorbing composite material and its preparation method described in the present invention are prepared by the following specific steps:
[0015] (1) Put the sodium-based bentonite in a beaker and ultrasonically treat it ...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
PUM
Login to view more
Abstract
The present invention discloses a recyclable oil absorbing composite material and a preparation method therefor. The ecyclable oil absorbing composite material is characterized by being prepared by using the following raw materials in parts by weight: 3-5 parts of sodium bentonite, 0.3-0.5 parts of cetyl trimethyl ammonium bromide (CTAB), 4-6 parts of methacrylate, 3-5 parts of styrene, 0.1-0.5 parts of 1,6-hexanediol diacrylate, 3-4 parts of ethyl acetate, 1-3 parts of polyvinyl alcohol, 0.8-1.2 parts of organophosphorus ester, 0.01-0.05 parts of potassium persulfate, 0.5-1 parts of sodium bicarbonate, 2-5 parts of polyethylene wax, 2-3 parts of stearic acid, 1-2 parts of calcium sulfate, 80-95 parts of polypropylene, 0.1-0.3 parts of antioxidant 1010, 10-15 pats of azodicarbonamide, 0.5-1 parts of silane coupling agent KH550, 2-3 parts of peat, 0.5-1 parts of lanthanum nitrate, 1-2 parts of silicone acrylic emulsion and an appropriate amount of water. The recyclable oil absorption composite material provided by the present invention has characteristics of high oil absorption multiple, fast oil absorption speed, good oil-water selectivity, high oil retention, reusability and the like, and can be widely used in treating pollution of oil on water surface and recycling oil in sewage.
Description
technical field [0001] The invention relates to the technical field of polymer materials, in particular to a recyclable oil-absorbing composite material and a preparation method thereof. Background technique [0002] With the development of industry and the improvement of people's living standards, the environmental pollution caused by the discharge of oily waste water and waste gas and the increase in leakage accidents of oil tankers and oil tanks has become increasingly serious, which has already constituted a threat to the ocean and people's lives. As a new type of functional polymer material, super oil-absorbing resin material is different from ordinary oil-absorbing materials in the past. It can not only achieve the purpose of high-efficiency oil absorption, but also has the characteristics of various types of oil absorption, fast oil absorption rate, high oil absorption ratio, oil absorption but not water absorption, etc. Not only can it replace traditional oil-absorbi...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more
Application Information
Patent Timeline
Application Date:The date an application was filed.
Publication Date:The date a patent or application was officially published.
First Publication Date:The earliest publication date of a patent with the same application number.
Issue Date:Publication date of the patent grant document.
PCT Entry Date:The Entry date of PCT National Phase.
Estimated Expiry Date:The statutory expiry date of a patent right according to the Patent Law, and it is the longest term of protection that the patent right can achieve without the termination of the patent right due to other reasons(Term extension factor has been taken into account ).
Invalid Date:Actual expiry date is based on effective date or publication date of legal transaction data of invalid patent.