High-performance modified styrene butadiene rubber composition

A technology of styrene-butadiene rubber and composition, applied in the field of high-performance modified styrene-butadiene rubber composition, can solve problems such as inability to meet and social requirements, and achieve the effects of improving tensile stress, good wear resistance and improving dispersion

Inactive Publication Date: 2015-12-02
合肥市再德高分子材料有限公司
View PDF5 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

With the development of society, people put forward higher requirements for the quantity and quality of rubber products, and because the use environment of rubber products is relatively changeable, the strength, wear resistance and aging resistance of existing rubber products cannot meet the requirements of rapid The requirements of the developing society require improvement

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0017] The high-performance modified styrene-butadiene rubber composition of the present invention, its raw material comprises the following components by weight: 70 parts of styrene-butadiene rubber, 10 parts of epoxidized natural rubber, 25 parts of carbon nanotubes, 12 parts of modified montmorillonite 3 parts of nano-aluminum nitride, 20 parts of precipitated white carbon black, 5 parts of modified boehmite, 5 parts of nano-aluminum hydroxide, 2 parts of nano-magnesium hydroxide, 3 parts of stearic acid, 0.5 parts of sulfur, oxidation 3 parts of zinc, 1.2 parts of silicone peroxide, 1.5 parts of polyvinyl alcohol, 1 part of diphenyl phosphate, 2.5 parts of lanthanum stearate, 0.3 parts of anti-aging agent RD, 1.5 parts of anti-aging agent NBC, anti-aging agent 4010NA0 .5 parts, 1 part of zinc diethyl dithiocarbamate, 0.8 part of cerium glutamic acid dithiocarbamate, 2 parts of accelerator DM, 1 part of triethyl citrate;

[0018] Wherein, the modifying agent for modifying b...

Embodiment 2

[0020] The high-performance modified styrene-butadiene rubber composition of the present invention, its raw material comprises the following components by weight: 90 parts of styrene-butadiene rubber, 3 parts of epoxidized natural rubber, 10 parts of carbon nanotubes, 3 parts of modified montmorillonite 20 parts of nano-aluminum nitride, 10 parts of precipitated silica, 25 parts of modified boehmite, 1 part of nano-aluminum hydroxide, 5 parts of nano-magnesium hydroxide, 1 part of stearic acid, 1 part of sulfur, oxidation 1.5 parts of zinc, 2 parts of silicone peroxide, 0.5 parts of polyvinyl alcohol, 2.5 parts of diphenyl phosphate, 1.2 parts of lanthanum stearate, 1.2 parts of anti-aging agent RD, 0.7 parts of anti-aging agent NBC, anti-aging agent 4010NA1 .8 parts, 0.5 parts of zinc diethyl dithiocarbamate, 2 parts of cerium glutamic acid dithiocarbamate, 0.5 parts of accelerator DM, 5 parts of triethyl citrate;

[0021] Wherein, the modifying agent of the modified boehmite i...

Embodiment 3

[0023] The high-performance modified styrene-butadiene rubber composition of the present invention, its raw material comprises the following components by weight: 84 parts of styrene-butadiene rubber, 6 parts of epoxidized natural rubber, 20 parts of carbon nanotubes, 6 parts of modified montmorillonite 18 parts of nano-aluminum nitride, 14 parts of precipitated silica, 20 parts of modified boehmite, 3.4 parts of nano-aluminum hydroxide, 3.8 parts of nano-magnesium hydroxide, 1.6 parts of stearic acid, 0.75 parts of sulfur, oxidation 2.1 parts of zinc, 1.78 parts of silicone peroxide, 0.9 parts of polyvinyl alcohol, 2.1 parts of diphenyl phosphate, 1.9 parts of lanthanum stearate, 1.0 parts of anti-aging agent RD, 0.9 parts of anti-aging agent NBC, anti-aging agent 4010NA1 .5 parts, 0.68 parts of zinc diethyl dithiocarbamate, 1.78 parts of cerium glutamic acid dithiocarbamate, 0.8 parts of accelerator DM, 3.5 parts of triethyl citrate;

[0024] Wherein, the modifying agent of ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The present invention discloses a high performance modified styrene butadiene rubber composition. The high performance modified styrene butadiene rubber composition is prepared from the following raw materials: styrene butadiene rubber, epoxidized natural rubber, a carbon nano-tube, modified montmorillonite, nano aluminium nitride, precipitation-method white carbon black, modified boehmite, nano aluminium hydroxide, nano magnesium hydroxide, stearic acid, sulfur, zinc oxide, organic silicon peroxide, polyvinyl alcohol, diphenyl phosphate, lanthanum stearate, an anti-aging agent RD, an anti-aging agent NBC, an anti-aging agent 4010NA, diethyl dithiocarbamate zinc, dithiocarbamate cerium formate glutamate, an accelerant DM and triethyl citrate. wherein a modifier of the modified boehmite is a mixture comprising one or more of methacrylic acid, itaconic acid, sorbic acid, maleic acid, arachidonic acid and linoleic acid. The high-performance modified styrene butadiene rubber composition provided by the present invention has high strength, good abrasion resistance, and excellent heat resistance and weather resistance.

Description

technical field [0001] The invention relates to the technical field of rubber materials, in particular to a high-performance modified styrene-butadiene rubber composition. Background technique [0002] Styrene-butadiene rubber, also known as polystyrene butadiene copolymer, has better wear resistance, heat resistance, aging resistance and vulcanization speed than natural rubber. It has been widely used in tires, tapes, hoses, wires and cables, and medical appliances. It is the largest general-purpose synthetic rubber variety and one of the earliest rubber varieties to realize industrial production. With the development of society, people put forward higher requirements for the quantity and quality of rubber products, and because the use environment of rubber products is relatively changeable, the strength, wear resistance and aging resistance of existing rubber products cannot meet the requirements of rapid The demands of the developing society require improvements. Conte...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08L9/06C08L15/00C08L29/04C08K13/06C08K9/04C08K7/24C08K3/34C08K3/36C08K3/28C08K3/22C08K5/09C08K5/526
Inventor 邱再明
Owner 合肥市再德高分子材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap