Anti-peeling heat-dissipation paint and preparation method therefor

A heat-dissipating coating and anti-stripping technology, applied in anti-corrosion coatings, coatings, etc., can solve the problems of performance degradation, high specific surface energy, and large specific surface area, and achieve enhanced dispersion, good dispersion, and high graft density. Effect

Inactive Publication Date: 2015-12-02
BENGBU TIMES ELECTRONICS
View PDF8 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Nano-silica has a large specific surface area and high specific surface energy. It is easy to agglomerate in the coating to form secondary particles, resulting in a decrease in the performance of strengthening and toughening. At the same time, the hydroxyl groups on the surface also strengthen this phenomenon.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0024] A kind of anti-peeling heat-dissipating coating, it is made up of the raw material of following weight part:

[0025] Didecyldimethylammonium bromide 0.6, epoxy butyl oleate 2, phytic acid 1, polyvinyl formal 2, diethanolamine 0.4, styrene maleic anhydride copolymer 12, propynyl alcohol 6, Tetrahydrofuran 90, graphene 4, nano-silica 16, silane coupling agent KH5600.2, dimethylformamide 700, sodium nitride 4, aluminum chloride 0.04, 2% sodium ascorbate solution 1.6, 2% copper sulfate Solution 1.8, high density polyethylene 120, montmorillonite powder 5, calcium oxide 0.7.

[0026] A kind of preparation method of described anti-peeling heat dissipation coating, comprises the following steps:

[0027] (1) Add the above-mentioned calcium oxide to 14 times the water, stir evenly, add phytic acid, raise the temperature to 60°C, add graphene, heat and stir until the water is dry, mix with nano-silica, and ball mill for 30 minutes;

[0028] (2) Mix styrene-maleic anhydride co...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Thermal conductivityaaaaaaaaaa
Login to View More

Abstract

The present invention discloses anti-peeling heat-dissipation paint. The anti-peeling heat-dissipation paintconsists of the following raw materials in parts by weight: 0.6-1 part of didecyldimethylammonium bromide, 2-4 parts of epoxy butyl oleate, 1-2 parts of phytic acid, 2-3 parts of polyvinyl formal, 0.4-1 part of diethanolamine, 12-15 parts of styrene-maleic anhydride copolymer, 6-10 parts of propargyl alcohol, 90-100 parts of tetrahydrofuran, 4-7 parts of graphene, 16-20 parts of nano silica, 0.2-0.3 part of a silane coupling agent KH560, 700-800 parts of dimethylformamide, 4-5 parts of sodium nitride, 0.04-0.05 parts of aluminium trichloride, 1.6-2 parts of a 2-3% sodium ascorbate solution, 1.8-2 parts of a 2-3% copper sulfate solution, 120-130 parts of high-density polyethylene, 5-7 parts of montmorillonite powder, and 0.7-1 part of calcium oxide. The paint provided by the present invention is strong in adhesion with a base material, high in peeling resistance, not liable to come off and to be destroyed, and is lasting in protective effect.

Description

technical field [0001] The invention relates to the technical field of heat dissipation coatings, in particular to an anti-peeling heat dissipation coating and a preparation method thereof. Background technique [0002] With the rapid development of modern science and technology, the high frequency and high speed of electronic devices and the density and miniaturization of integrated circuits have greatly increased the total power density and calorific value of electronic devices per unit volume, thus making the cooling of electronic devices more difficult. increasingly prominent. However, the cooling capacity achieved by conventional cooling systems is greatly challenged, especially in the fields of energy, automobiles, air conditioning, agriculture, chemicals, heating, aerospace, microelectronics, information, etc. put forward higher requirements. The heat dissipation paint is a special paint that improves the heat dissipation efficiency of the surface of the object and ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D123/06C09D5/08C09D7/12
Inventor 朱兴堂朱亮亮陈军彦
Owner BENGBU TIMES ELECTRONICS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com