Ship hull rust-proof two-component epoxy coating

An epoxy coating, two-component technology, applied in epoxy resin coatings, anti-corrosion coatings, coatings and other directions, can solve the problems of adverse environmental impact of waste, poor resistance to cathodic disbonding that cannot meet the needs of practical use, and unfavorable environmental protection. Achieve the effect of improving anti-peeling performance, enhancing cathodic disbonding resistance and smooth coating film

Inactive Publication Date: 2016-03-09
ANHUI JINDUN PAINT
View PDF6 Cites 9 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The steel structure anticorrosion coatings in the prior art generally have poor cathodic disbonding resistance and cannot meet the needs of actual use, and the waste generated during the production process has a relatively large adverse impact on the environment, which is not conducive to environmental protection

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A kind of antirust two-component epoxy paint for hull, including A component and B component;

[0030] The raw materials of component A include by weight: 30 parts of bisphenol A type epoxy resin, 40 parts of modified bisphenol F type epoxy resin, 15 parts of amino resin, 35 parts of mixed solvent, 10 parts of nano silicon dioxide, filler 40 parts, 1 part of silane coupling agent, 2 parts of chlorinated paraffin, 1 part of dibutyl ester, 2 parts of anti-settling agent, 1 part of leveling agent, 2 parts of thixotropic agent, 1 part of dispersant, 2 parts of defoamer ;

[0031] The raw materials of component B include by weight: 10 parts of phenalkamine, 10 parts of 1,3-diaminohexylamine, 1 part of butanol, and 6 parts of xylene;

[0032] The weight ratio of A component to B component is 10:1.

Embodiment 2

[0034] A kind of antirust two-component epoxy paint for hull, including A component and B component;

[0035] The raw materials of component A include by weight: 60 parts of bisphenol A type epoxy resin, 20 parts of modified bisphenol F type epoxy resin, 30 parts of amino resin, 20 parts of mixed solvent, 20 parts of nano silicon dioxide, filler 20 parts, 3 parts of silane coupling agent, 1 part of chlorinated paraffin, 2 parts of dibutyl ester, 1 part of anti-settling agent, 2 parts of leveling agent, 1 part of thixotropic agent, 2 parts of dispersant, 1 part of defoamer ;

[0036] The raw materials of component B include by weight: 20 parts of phenalkamine, 5 parts of 1,3-diaminohexylamine, 3 parts of butanol, and 1 part of xylene;

[0037] The weight ratio of component A to component B is 10:1.5.

Embodiment 3

[0039] A kind of antirust two-component epoxy paint for hull, including A component and B component;

[0040] The raw materials of component A include: 56 parts of bisphenol A type epoxy resin, 30 parts of modified bisphenol F type epoxy resin, 26 parts of amino resin, 30 parts of mixed solvent, 38 parts of filler, 1.4 parts of chlorinated paraffin Parts, 1.6 parts of dibutyl ester, 1.2 parts of anti-settling agent, 1.8 parts of leveling agent, 1.3 parts of defoamer;

[0041] The raw materials of component B include by weight: 18 parts of phenalkamine, 1.5 parts of butanol, and 5 parts of xylene;

[0042] The weight ratio of A component to B component is 10:1.2.

[0043] The mixed solvent is composed of cyclohexanone, butanol and xylene in a weight ratio of 1:5:1.

[0044] The filler consists of talcum powder and barium sulfate.

[0045] The amino resin is composed of butanol modified melamine formaldehyde resin and isobutanol modified melamine formaldehyde resin.

[0046]...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Epoxy equivalentaaaaaaaaaa
Epoxy equivalentaaaaaaaaaa
Epoxy equivalentaaaaaaaaaa
Login to View More

Abstract

The invention discloses ship hull rust-proof two-component epoxy coating which comprises a component A and a component B, wherein the component A is prepared from the following raw materials in parts by weight: 30 to 60 parts of bisphenol A epoxy resin, 20 to 40 parts of modified bisphenol F epoxy resin, 15 to 30 parts of amino resin, 20 to 35 parts of mixed solvent, 10 to 20 parts of nano-silica, 20 to 40 parts of filler, 1 to 3 parts of silane coupling agent, 1 to 2 parts of chlorinated paraffin, 1 to 2 parts of dibutyl ester, 1 to 2 parts of anti-settling agent, 1 to 2 parts of flatting agent, 1 to 2 parts of thixotropic agent, 1 to 2 parts of dispersing agent and 1 to 2 parts of defoaming agent; the component B is prepared from the following raw materials in parts by weight: 10 to 20 parts of phenol-aldehyde amine, 5 to 10 parts of 1,3-diamido-hexylamine, 1 to 3 parts of butanol and 1 to 6 parts of xylene; the weight ratio of the component A and the component B is 10 to (1 to 1.5). The coating provided by the invention is environment-friendly, and is good in cathodic disbonding resistance.

Description

technical field [0001] The invention relates to the technical field of two-component epoxy coatings, in particular to an antirust two-component epoxy coating for ship hulls. Background technique [0002] In recent years, with the rapid development of the national economy and the sustained growth of the steel industry, the market demand for long-lasting steel structure anti-corrosion coatings is increasing day by day. Through the comprehensive evaluation of the anti-corrosion performance, construction process and later coating maintenance of epoxy coatings, it has higher cost performance and quality assurance as a heavy-duty anti-corrosion supporting system for domestic large-scale steel structure anti-corrosion projects, and has wide application value and prospects; Oxygen coatings are the development direction of anti-corrosion coatings. The anticorrosion coatings for steel structures in the prior art generally have poor cathodic disbonding resistance and cannot meet the n...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/00C09D161/32C09D5/08C09D7/12
Inventor 朱恒衡郭宝张国胜
Owner ANHUI JINDUN PAINT
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com