Heavy anti-corrosion coating material

A coating material, heavy-duty anti-corrosion technology, used in anti-corrosion coatings, coatings, polyester coatings, etc., can solve the problems of unsatisfactory adhesion and toughness of coating materials, inability to use steel structure anti-corrosion repair, and difficult to complete anti-corrosion. requirements and other issues, to achieve good social and economic benefits, overcome technical difficulties in anti-corrosion, and achieve the effect of thick coating

Active Publication Date: 2016-03-23
QINGDAO UNIV OF SCI & TECH
View PDF5 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This kind of protective sleeve has high corrosion resistance, high plasticity and high weldability, and will not cause corrosion resistance and stress corrosion cracking. It has high stability in preventing the growth of microorganisms, but it is expensive and has fatal flaws: Once seawater seeps in, the corrosion becomes more serious
However, although these coating materials achieve environmental protection and long-term performance, the cost is too high when they are applied to the splash zone
At the same time, the material is too harsh on the construction requirements, and cannot be used for the anti-corrosion repair of the steel structure in the ocean splash area; It is found that the adhesion and toughness of the coating material are unsatisfactory, and it is easy to peel off after long-term washing in the ocean splash zone after coating, so it is difficult to meet the anti-corrosion requirements, so further improvement is needed

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Heavy anti-corrosion coating material
  • Heavy anti-corrosion coating material
  • Heavy anti-corrosion coating material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0039] A heavy-duty anti-corrosion coating material for steel structures in the ocean splash zone, including a main agent system and a curing agent system, in parts by weight:

[0040] (1) each component in the main agent system is: film-forming resin: bisphenol A type epoxy resin 45; Toughener: polycaprolactone 14; Rust stabilizer: zinc phosphate 8; rust conversion agent: diphenyl chromate 0.4; sub-nanometer flake filler: ceramic powder with a fineness of less than 1 micron 15; inorganic cementitious material: Portland cement: 35; adhesion enhancer: epoxy phosphate 4;

[0041] (II) The components in the curing agent system are: curing agent: cashew nut shell oil modified phenalkamine 40; high wear-resistant filler: quartz powder 25; antirust pigment: mica iron oxide 25; penetrating agent fatty alcohol polyoxyethylene Ether 2; Organic Chelating Agent: Organic Phosphite 3.

[0042] Wherein said polycaprolactone is graphene modified polycaprolactone, and its modification metho...

Embodiment 2

[0046] A heavy-duty anti-corrosion coating material for steel structures in the ocean splash zone, including a main agent system and a curing agent system, in parts by weight:

[0047] (1) Each component in the main agent system is: film-forming resin: bisphenol A type epoxy resin 43; Modified toughening agent: polycaprolactone 14; Defoamer: 0571.5 of BYK company; Leveling agent Peak’s 37771.5; rust stabilizer: zinc phosphate 6, zinc chromate 2; rust conversion agent: diphenyl chromate 0.8; sub-nano flaky filler: talcum powder 15 with a fineness of 0.7 microns; inorganic cementitious material: Aluminate cement 37; adhesion enhancer: 1211 adhesion enhancer 3;

[0048] (II) The components in the curing agent system are: curing agent: cashew nut shell oil modified phenalkamine 45; high wear-resistant filler: quartz powder 25; antirust pigment: iron phosphorus powder 25; penetrating agent: fatty alcohol polyoxygen Vinyl ether 2.5; organic chelating agent: organic phosphite 2.0. ...

Embodiment 3

[0053] A heavy-duty anti-corrosion coating material for steel structures in the ocean splash zone, including a main agent system and a curing agent system, in parts by weight:

[0054] (1) Each component in the main agent system is: film-forming resin: bisphenol A type epoxy resin 35; Modified toughening agent: polycaprolactone 12; Defoamer: 0571.3 of BYK company; Leveling agent : BYK 37771.2; Rust stabilizer: Zinc lattice 7; Rust conversion agent: Diphenyl chromate 0.6; Sub-nano flaky filler: Ceramic powder 12 with a fineness of less than 1 micron; Inorganic cementitious material: Sulfur aluminum Salt cement 30; adhesion enhancer: epoxy phosphate 4;

[0055] (II) The components in the curing agent system are: curing agent: Cardolite XN200735; high wear-resistant filler: quartz powder 25; anti-rust pigment: mica iron oxide 16, iron phosphorus powder 7; penetrating agent: fatty alcohol Polyoxyethylene ether: 1.5; organic chelating agent: organic phosphite 2.5.

[0056] Wherei...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Finenessaaaaaaaaaa
Finenessaaaaaaaaaa
Adhesionaaaaaaaaaa
Login to View More

Abstract

The invention relates to a heavy anti-corrosion coating material. The material does not need solvent and comprises a main agent system and a curing agent system; graphene-modified polycaprolactone is adopted as a toughening agent in the main agent system, and the anti-corrosion coating material can be directly applied in a waterless environment or water environment through a hand coating method, an apply coating method and a brush coating method. By adopting the material and a using method thereof, the zero-solvent content is achieved; meanwhile, the long effectiveness of the anti-corrosion effect and thick coating are achieved, the technical problem of steel structure corrosion prevention in a severe environment of a splash zone is effectively solved, the constructability and protective capability of ocean engineering corrosion prevention are greatly improved, and the technical progress in the coating field in China is promoted; in addition, the engineering construction cost is greatly lowered, the expensive repair and maintenance cost and precious fresh water resources are saved for the state, and the good social and economic benefits are achieved.

Description

technical field [0001] The invention relates to a heavy-duty anti-corrosion technology, in particular to a heavy-duty anti-corrosion coating material for steel structures in ocean splash zones. Background technique [0002] According to statistics, the annual loss caused by corrosion in the world accounts for 2%-4% of the gross national economic product, which is greater than the sum of losses caused by natural disasters such as fire, wind, flood and earthquake. The country attaches great importance to marine corrosion and protection research. my country is a large ocean country, with a coastline of more than 18,000 kilometers and a sea area of ​​more than 3 million kilometers under its jurisdiction 2 , Marine corrosion and protection is one of the key issues that need to be seriously resolved in my country's economic development. In terms of anti-corrosion of marine steel structures, the corrosion environment is different, and the anti-corrosion measures adopted are diffe...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C09D163/02C09D167/04C09D7/12C09D5/08
Inventor 李少香薛守伟李光俊黄永江仲华
Owner QINGDAO UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products