A kind of graphene/silicon dioxide/nano zero-valent iron composite material and its preparation method and application

A technology of nano-zero-valent iron and silicon dioxide, which is applied in chemical instruments and methods, water/sludge/sewage treatment, and other chemical processes, can solve the problems of losing specific surface area and limiting the application of graphene, and achieve a higher ratio The effects of surface area and stability, abundant reserves, and simple and easy preparation process

Active Publication Date: 2018-02-27
SOUTH CHINA UNIV OF TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, during the preparation process, graphene flakes will undergo irreversible re-stacking and agglomeration, causing them to lose most of their specific surface area, thus limiting the application of graphene as an adsorbent in water pollution control.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of graphene/silicon dioxide/nano zero-valent iron composite material and its preparation method and application
  • A kind of graphene/silicon dioxide/nano zero-valent iron composite material and its preparation method and application
  • A kind of graphene/silicon dioxide/nano zero-valent iron composite material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] (1) Add 0.3 g of graphite oxide solid, 1.5 g of cetyltrimethylammonium bromide and 0.9 g of sodium hydroxide into water, and after ultrasonic treatment at 180 W for 2 h, a modified graphite oxide with a concentration of 0.3 g / L was obtained alkene suspension;

[0041]Graphite oxide in this example is prepared by the improved Hummers method, and the specific steps are: slowly add 120 ml of concentrated sulfuric acid to a 1000 mL beaker and place it in a mixture of ice and water, stir it slowly with an electric stirrer, and when the temperature When the temperature drops to about 5°C, add 5 g of graphite and 2.5 g of sodium nitrate, stir for 30 minutes, then slowly add 15 g of potassium permanganate, keep the temperature of the reaction system not higher than 15°C during the process, and continue the reaction for 90 minutes; Place the beaker in a constant temperature water bath at 35°C, and when the temperature of the system rises to 35°C, continue to stir for 30 minutes;...

Embodiment 2

[0047] (1) Add 0.2 g of graphite oxide solid, 1.0 g of cetyltrimethylammonium bromide and 0.6 g of sodium hydroxide into water, and obtain modified graphite oxide with a concentration of 0.2 g / L after ultrasonic treatment at 190 W for 2 h alkene suspension;

[0048] (2) After the modified graphene oxide suspension obtained in step (1) was magnetically stirred for 2 h, 14 mL of ethyl orthosilicate was added, and the mass ratio of graphene oxide to ethyl orthosilicate was 1:13 ;Continue stirring for 36 hours, and keep the temperature at 40°C. After fully reacting, the product is centrifugally washed with deionized water until the product does not contain bromide ions, and the graphene oxide / silica solid is obtained after drying;

[0049] (3) Put the solid obtained in step (2) into a tube furnace and feed it with nitrogen for calcination, the nitrogen flow rate is controlled at 40 mL / min, the calcination temperature of the tube furnace is 550 ° C, and the calcination time is 180 ...

Embodiment 3

[0054] (1) Add 0.4 g of graphite oxide solid, 2 g of cetyltrimethylammonium bromide and 1.2 g of sodium hydroxide into water, and after ultrasonic treatment at 200 W for 2 h, a modified graphite oxide with a concentration of 0.4 g / L was obtained alkene suspension;

[0055] (2) After the modified graphene oxide suspension obtained in step (1) was magnetically stirred for 2 h, 20 mL of ethyl orthosilicate was added, and the mass ratio of graphene oxide to ethyl orthosilicate was 1:17 ;Continue stirring for 40 h, and keep the temperature at 40°C. After sufficient reaction, the product is centrifugally washed with deionized water until the product does not contain bromide ions, and the graphene oxide / silicon dioxide solid is obtained after drying;

[0056] (3) Put the solid obtained in step (2) into a tube furnace and feed it with nitrogen for calcination, the nitrogen flow rate is controlled at 60 mL / min, the calcination temperature of the tube furnace is 550 ° C, and the calcina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
pore sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a graphene / silicon dioxide / nano zero-valent iron composite as well as a preparation method and application thereof. The preparation method comprises the following steps: after the graphene oxide is subjected to ultrasonic dispersion, adding tetraethyl orthosilicate, drying after magnetic stirring is carried out completely, introducing nitrogen in a tubular furnace for calcination, adding deionized water into the solids obtained through calcination, after ultrasonic dispersion, introducing nitrogen and adding ferrous sulfate heptahydrate, after uniform stirring, and adding a reducing agent for reducing so as to obtain black flocculent precipitates after complete reaction, washing, carrying out suction filtration, drying, grinding and screening through a sieve so as to obtain the graphene / silicon dioxide / nano zero-valent iron composite. The graphene / silicon dioxide / nano zero-valent iron composite prepared according to the preparation method can be applied to the field of water pollution control as an adsorbent, particularly adsorption removal of arsenic pollutants in waste water, and has the advantages of simple and convenient preparation process, high adsorption speed and the like, and in addition, the required raw materials are wide in source, low in cost and high in practical application value.

Description

technical field [0001] The invention relates to the technical field of water pollution control, in particular to a graphene / silicon dioxide / nano zero-valent iron composite material and its preparation method and application. Background technique [0002] With the rapid development of industrial economy and the increase of industrial production intensity, more and more arsenic-containing wastewater is discharged into natural water bodies, and water is an essential resource for human beings. A large amount of arsenic discharge seriously endangers the ecological environment and human health. The treatment of arsenic-containing wastewater is urgent. Arsenic-containing wastewater has the characteristics of high toxicity, refractory degradation, and easy bioaccumulation, and has great potential harm to the natural environment and human beings. Arsenic pollutants have been listed as one of the priority pollutants. Therefore, the removal of arsenic-containing wastewater has always b...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B01J20/20B01J20/30C02F1/28C02F1/58
CPCB01J20/0229B01J20/103B01J20/20C02F1/281C02F1/288
Inventor 罗汉金刘佩佩
Owner SOUTH CHINA UNIV OF TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com