Casting method of high-hardness and erosion-resistant combined stop valve body
A technology of anti-scour and globe valve, applied in casting molding equipment, casting mold, casting mold composition, etc., can solve the problems affecting the appearance quality and service life of the valve body, the uneven thickness of slag inclusion and surface composite layer, and the quality of casting infiltration layer. Poor stability and other problems, to achieve good surface protection, appearance quality, good performance and high hardness
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0013] A method for casting a valve body of a high-hardness and erosion-resistant composite globe valve includes the following steps:
[0014] (1) Prepare pouring liquid, in which the chemical composition weight percentage of the pouring liquid is as follows: C: 0.22%, Si: 0.25%, Mn: 0.60%, Ni: 0.50%, Cu: 0.25%, B: 0.15%, P: 0.03 %, S: 0.02%, the balance is Fe, each raw material is smelted in an intermediate frequency induction furnace at 1580℃, and the chemical composition is adjusted to obtain the pouring liquid;
[0015] (2) Preparing cast-infiltrating coatings, where cast-infiltrating coatings are made of the following weight (kg) raw materials: 200 mesh titanium iron powder 40, 200 mesh titanium nitride 5, polyvinyl alcohol 0.5, rosin 0.1, acrylic acid 0.1, persulfuric acid Ammonium 0.01, Lithium Silicate 2, Sodium Fluoride 1, Carbon Nanotube 1, Carboxymethyl Cellulose 0.1, Silane Coupling Agent KH-550 0.5; The method for preparing the cast-infiltrated coating is to first comb...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap