Method for coating titanium dioxide by using chloride by-product hydrochloric acid
A technology for by-producing hydrochloric acid and titanium dioxide is applied in chemical instruments and methods, dyeing low-molecular-weight organic compounds treatment, inorganic pigment treatment, etc. Competition and other issues, to achieve the effect of improving chalking resistance, reducing photochemical activity, and improving chalking resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0026] Example 1
[0027] (1) Dilute the crude hydrochloric acid with pure water to a mass concentration of 5% to 10% for use;
[0028] (2) To the titanium dioxide suspension with a concentration of 10wt%, add 0.02% of the titanium dioxide powder mass of sodium hexametaphosphate, adjust the pH to 8 with sodium hydroxide, and stir for 2 hours to obtain a titanium dioxide slurry;
[0029] (3). Add hydrochloric acid to the titanium dioxide slurry obtained in step (2) to adjust the pH to 9, raise the temperature to 60°C, then slowly add zirconium sulfate, which accounts for 0.5% of the weight of the titanium dioxide powder, and then mature for 30 minutes , Adjust the pH to 7 again with hydrochloric acid, and then mature for 50 minutes;
[0030] (4). In the mixed powder slurry obtained in step (3), heat up to 70°C, add sodium silicate (with SiO 2 Calculated) is 0.5% of the mass of the titanium dioxide powder to obtain a mixed slurry, adjust the pH to 7.5 with hydrochloric acid, and let the...
Example Embodiment
[0035] Example 2
[0036] (1) Dilute the crude hydrochloric acid with pure water to a mass concentration of 5% to 10% for use;
[0037] (2) To a titanium dioxide suspension with a concentration of 20 wt%, add 0.2% of the titanium dioxide powder mass of sodium hexametaphosphate, adjust the pH to 10 with sodium hydroxide, and stir for 3 hours to obtain a titanium dioxide slurry;
[0038] (3) In the titanium dioxide slurry obtained in step (2), the temperature is raised to 80°C, hydrochloric acid is added to adjust the pH to 8, and then zirconium oxychloride is slowly added. The added amount of zirconium oxychloride accounts for the mass of the titanium dioxide powder 1%, then mature for 60 minutes, adjust the pH to 8 again with hydrochloric acid, and then mature for 60 minutes;
[0039] (4). Cool the mixed slurry obtained in the above step (3) to 70℃, and add sodium metasilicate (with SiO 2 (Calculated) is 3% of the mass of the titanium dioxide powder, adjust the pH to 8.2 with hydrochl...
Example Embodiment
[0044] Example 3
[0045] (1) Dilute the crude hydrochloric acid with pure water to a mass concentration of 5% to 10% for use;
[0046] (2) To the titanium dioxide suspension with a concentration of 30wt%, add 0.3% of the titanium dioxide powder mass of sodium hexametaphosphate, adjust the pH to 12 with sodium hydroxide, and stir for 4 hours to obtain a titanium dioxide slurry;
[0047] (3). To the titanium dioxide slurry obtained in step (2), heat up to 85°C, add hydrochloric acid to adjust the pH to 9, and then slowly add zirconium chloride, the amount of zirconium chloride added accounts for 2% of the mass of the titanium dioxide powder , Then mature for 30-100min, adjust the pH to 9 with hydrochloric acid again, and mature for 90min;
[0048] (4). In the mixed slurry obtained in the above step (3), the temperature is reduced to 70°C, and the amount of sodium silicate added (in SiO 2 (Calculated) is 2% of the mass of the titanium dioxide powder, adjust the pH to 8.6 with hydrochlor...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap