A corrosion-resistant, aluminum pigment technology, applied in anti-corrosion coatings, inorganic pigment treatment, fibrous fillers, etc., can solve the problems of potential safety hazards, limited corrosion inhibition effect, and reduced metallic luster, achieving good gloss and improving corrosion resistance The effect of good performance and dispersibility

Inactive Publication Date: 2016-11-09
HEFEI SUNRISE PIGMENTS
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although the method of adding inhibitors to the aluminum pigment system can inhibit the corrosion rate of aluminum, the corrosion inhibition effect is limited. Prolonged contact with water-based system coatings, inks, etc. will still cause certain corrosion to the aluminum pigments, reducing the metallic luster and at the same time There are security risks

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0015] A high-brightness, high-stability, corrosion-resistant water-based aluminum pigment prepared from the following parts by weight (kg) of raw materials: flake aluminum powder 40, isopropanol 100, copper sulfate crystal 0.3, deionized water, phenol ether type phosphoric acid Ester 4, appropriate amount of absolute ethanol, ethyl orthosilicate 9, vinyl triethoxy silane 6, ammonia water with a concentration of 20 wt% 9, butyl acetate 200, acrylic acid 5, methacrylic acid 5, diphenyl methyl peroxide Acyl 0.6, propylene glycol monomethyl ether 13, polyvinyl alcohol 1.2, sodium polyacrylate 0.3, nano tin oxide antimony 6, dimethyl silicone oil 1.2, polydimethylsiloxane 0.8.

[0016] The high-brightness, high-stability, corrosion-resistant water-based aluminum pigment is produced by the following specific steps:

[0017] (1) Put the flake aluminum powder into the reactor, add isopropanol and phenol ether phosphate, heat to 40℃, stir and react for 60 minutes, and dissolve copper sulfa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a high-brightness and high-stability of corrosion-resistant water-based aluminum pigment, which is prepared from the following raw materials in parts by weight: 40 to 45 parts of flaky aluminum powder, 100 to 110 parts of isopropyl alcohol, 0.3 to 0.35 parts of copper sulfate crystal, an appropriate amount of deionized water, 4 to 4.5 parts of phenolic ether phosphate, an appropriate amount of absolute ethanol, 9 to 10 parts of ethyl orthosilicate, 6 to 7 parts of vinyl triethoxysilane, 9 to 10 parts of ammonia with concentration of 20wt%, 200 to 220 parts of butyl acetate, 5 to 6 parts of acrylic acid, 5 to 6 parts of methacrylic acid, 0.6 to 0.65 part of dibenzoyl peroxide, 13 to 15 parts of propylene glycol monomethyl ether, 1.2 to 1.5 parts of polyvinyl alcohol, 0.3 to 0.4 part of sodium polyacrylate, 6 to 7 parts of nano antimony tin oxide, 1.2 to1.4 parts of dimethyl silicone oil, and 0.8 to 1 part of polydimethylsiloxane. The product prepared by the invention is not corroded in an aqueous system and has strong stability.

Description

Technical field [0001] The invention relates to the technical field of pigments, in particular to a high-brightness, high-stability, corrosion-resistant water-based aluminum pigment. Background technique [0002] Aluminum pigment is one of the important metal pigments. Due to its unique aesthetic effect and anti-corrosion, it has been widely used in anti-corrosion coatings, industrial coatings, automotive coatings, architectural interior and exterior decoration coatings, household appliances coatings, printing inks and plastic processing industries in recent years. application. With the continuous improvement of people's awareness of environmental protection and the continuous improvement of government environmental regulations, traditional organic solvent-based coatings will inevitably be replaced by environmentally-friendly water-based coatings. Aluminum pigments used in water-based coatings and solvent-based coatings have different requirements: First, the surface of the pigm...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D5/10C09D7/12C09D11/037C09C1/64C09C3/08C09C3/12C09C3/06
CPCC09C1/648C09C3/006C09D5/103C09D11/037
Inventor 董前年谷圣军周辉操玉节朱双单
Owner HEFEI SUNRISE PIGMENTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap