Sintering device and system for preparing quartz glass

A quartz glass and sintering device technology, applied in glass forming, glass manufacturing equipment, manufacturing tools, etc., can solve the problems of low efficiency, difficult gas discharge and high cost, and achieve the goal of reducing cost, improving product quality and improving sintering efficiency. Effect

Active Publication Date: 2016-11-16
CHINA BUILDING MATERIALS ACAD
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] For the larger silica soot body, during sintering, the gas in the pores inside the silica soot body is not easy to be discharged, and the gas discharge effect is poor through the method of introducing helium in the prior art, and the obtained quartz There are still many pores in the glass, and the product quality cannot meet the requirements of aerospace, laser nuclear technology, precision optics and instruments, semiconductors, liquid crystal display and other fields; the existing zone melting step by step sintering method has low efficiency and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Sintering device and system for preparing quartz glass
  • Sintering device and system for preparing quartz glass
  • Sintering device and system for preparing quartz glass

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0054] Such as figure 1 As shown, one embodiment of the present invention proposes a sintering method for preparing quartz glass and quartz glass, which are used to sinter a silica loose body in a sintering space to obtain a finished quartz glass, wherein the silica There are pores in the loose body, and the porosity of the silicon dioxide loose body can be 20-90%. ; The diameter of the silica loose body can be more than 300mm; such as φ350mm, φ550mm, φ750mm, φ850mm, φ950mm. The above method can be realized by the device provided in the second embodiment below.

[0055] The silicon dioxide loose body can be synthesized from silicon-containing raw materials through low-temperature chemical vapor deposition. The silicon dioxide loose body is a high-purity silicon dioxide loose body, and the silicon dioxide in the high-purity silicon dioxide loose body is The content is above 99.99%. Or the silica soot body is a doped silica soot body, and the doping elements are boron (B), al...

Embodiment 2

[0107] Embodiment 2 of the present invention provides a sintering device for preparing quartz glass, which is used for sintering a soot silica body to obtain a finished quartz glass product, wherein the soot silica body has pores; the soot silica body has a diameter of Can be more than 300mm; such as φ350mm, φ550mm, φ750mm, φ850mm, φ950mm.

[0108] The silicon dioxide loose body can be synthesized from silicon-containing raw materials through low-temperature chemical vapor deposition. The silicon dioxide loose body is a high-purity silicon dioxide loose body, and the silicon dioxide in the high-purity silicon dioxide loose body is The content is above 99.99%. Or the silica soot body is a doped silica soot body, and the doping elements are boron (B), aluminum (Al), fluorine (F), iron (Fe), titanium (Ti), cerium (Ce), At least one of calcium (Ca), magnesium (Mg), sodium (Na), potassium (K), barium (Ba), yttrium (Y), lanthanum (La), zirconium (Zr), and germanium (Ge).

[0109] ...

Embodiment 3

[0139] Such as Image 6 As shown, a system for preparing quartz glass provided by Embodiment 3 of the present invention includes:

[0140] A low-temperature chemical vapor deposition device (not shown in the figure) is used for synthesizing silicon-containing raw materials through low-temperature chemical vapor deposition to obtain a silicon dioxide loose body, and the silicon dioxide loose body is a high-purity silicon dioxide loose body or a doped silicon dioxide Heterosilica soot body, wherein the content of silicon dioxide in the high-purity silica soot body is above 99.99%;

[0141] A sintering device 100 for preparing quartz glass, the sintering device for preparing quartz glass includes:

[0142] a furnace body, the furnace body has a sintering space for accommodating the silica loose body;

[0143] The furnace body also has a heater for heating the sintering space;

[0144] The furnace body is also equipped with a vacuum passage connecting the sintering space, which...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
porosityaaaaaaaaaa
Login to View More

Abstract

The invention relates to a sintering device and system for preparing quartz glass, relating to the field of preparing quartz glass and mainly aiming at avoiding or reducing the generation of bubbles in preparation of the quartz glass by adopting indirect synthesis method technology, and improving the sintering efficiency of the quartz glass and lowering the cost. The sintering device for preparing quartz glass comprises a furnace body, wherein a vacuumizing channel communicated with a sintering space is also arranged on the furnace body, and used for vacuumizing the sintering space to a negative pressure environment so as to sinter silica loose body in the sintering space, pores in the silica loose body are discharged under the negative pressure environment, and the silica loose body is sintered to transparent quartz glass. According to the sintering device and system for preparing quartz glass, the sintering device for preparing the quartz glass can conduct sintering under the negative pressure environment, and the content of bubbles in the obtained finised quartz glass after sintering can be decreased, so that the quality of the quartz glass product is improved, the whole body is heated and sintered simultaneously, the sintering efficiency of the silica loose body is increased and the cost is lowered.

Description

technical field [0001] The invention relates to the field of quartz glass preparation, in particular to a sintering device and system for preparing quartz glass. Background technique [0002] Quartz glass has good properties, such as high temperature resistance, low expansion coefficient, thermal shock resistance, high chemical stability and good electrical insulation performance. It is a special industrial technical glass mainly composed of silicon dioxide. It is classified according to its purity. There are three types: high-purity, common and doped. [0003] At present, the preparation process of quartz glass is mainly divided into direct method and indirect method. In the direct method, quartz glass is made of crystal, silica, and silicon-containing compounds as raw materials, which are melted at high temperature or chemical vapor deposition. Melting methods include electric melting, gas refining, chemical vapor deposition CVD and plasma chemical vapor deposition PCVD. ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03B20/00
CPCC03B19/066C03B2201/02C03B2201/06
Inventor 聂兰舰向在奎饶传东王蕾刘飞翔邵竹锋王慧王宏杰贾亚男符博张辰阳王玉芬
Owner CHINA BUILDING MATERIALS ACAD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com