Modifying preparation and application of tertiary amine oxide modified attapulgite adsorbent containing rosinyl ternary phenanthrene ring structure

A technology of rosin-based ternary phenanthrene and modified attapulgite, which can be used in adsorption water/sewage treatment, other chemical processes, chemical instruments and methods, etc., can solve problems such as environmental and ecological hazards, reduce residues and reduce treatment costs. , good adsorption performance

Inactive Publication Date: 2016-11-23
GUANGXI UNIV FOR NATITIES +1
View PDF2 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although there are many studies on the adsorption of pollutants in water by modified attapulgite at home and abroad, the quaternary ammonium salts (such as hexadecyl trimethyl chloride (bromine) mainly with long-chain alkyl groups as lipophilic groups ammonium chloride and cetylpyridinium bromide, etc.) modified attapulgite, but the above-mentioned surfactants have certain potential harm to the environment and ecology
At present, there is no report on how to use the adsorption of N,N-dimethyl dehydroabietyl amine oxide modified attapulgite to remove humic acid, anionic dyes and anionic inorganic ions in water.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Modifying preparation and application of tertiary amine oxide modified attapulgite adsorbent containing rosinyl ternary phenanthrene ring structure
  • Modifying preparation and application of tertiary amine oxide modified attapulgite adsorbent containing rosinyl ternary phenanthrene ring structure
  • Modifying preparation and application of tertiary amine oxide modified attapulgite adsorbent containing rosinyl ternary phenanthrene ring structure

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0038] One, the preparation method of the tertiary amine oxide modified attapulgite containing rosin base ternary phenanthrene ring structure comprises the following steps:

[0039] (1) Acid-treated attapulgite

[0040]Grind the attapulgite fully, pass through a 200-mesh sieve, and then add the sieved attapulgite powder to 2mol / L hydrochloric acid solution, the mass volume ratio of the added attapulgite powder to hydrochloric acid is 1:10, and the reaction Ultrasonic dispersion was carried out at 60°C for 15 minutes, and the ultrasonic power was 50 W. After the reaction was completed, the precipitate was collected by filtration, and the precipitate was washed until neutral to obtain acidified attapulgite.

[0041] (2) Firing: Add water to the attapulgite obtained in step (1) to prepare a thick liquid, centrifuge at a speed of 5000 rpm to remove the supernatant, and then fire it in a tube furnace in a nitrogen environment at 400 ° C. Adjust the heating rate to 50 ℃ / min, the fi...

Embodiment 2

[0048] One, the preparation method of the tertiary amine oxide modified attapulgite containing rosin base ternary phenanthrene ring structure comprises the following steps:

[0049] (1) Acid-treated attapulgite

[0050] Grind the attapulgite fully, pass through a 100-mesh sieve, then add the sieved attapulgite powder into 1mol / L nitric acid solution, the mass volume ratio of the added attapulgite powder to nitric acid is 1:20, and the reaction Ultrasonic reaction was carried out at 80°C for 30 minutes, and the ultrasonic power was 30W. After the reaction was completed, the precipitate was collected by filtration, and the precipitate was washed until neutral to obtain acidified attapulgite.

[0051] (2) Firing: centrifuge the attapulgite soil thick liquid obtained in step (1) at a speed of 5000 rpm to remove the supernatant, and then fire it in a tube furnace in a nitrogen environment at 300°C, and adjust the heating rate to 50°C / min , the firing time is set to 1h, and then it...

Embodiment 3

[0057] One. The preparation method of the tertiary amine oxide modified attapulgite containing the rosin-based ternary phenanthrene ring structure comprises the following steps:

[0058] (1) Acid-treated attapulgite:

[0059] Grind attapulgite fully, pass through a 200-mesh sieve, and then add the sieved attapulgite powder into 4mol / L sulfuric acid solution, and the mass volume ratio of the added attapulgite powder to hydrochloric acid is 1:15 , ultrasonic reaction at a reaction temperature of 70° C. for 20 minutes, and an ultrasonic power of 60 W. After the reaction was completed, the precipitate was collected by filtration, and the precipitate was washed until neutral to obtain acidified attapulgite.

[0060] (2) Firing: Centrifuge the attapulgite soil thick liquid obtained in step (1) at a speed of 5000 rpm to remove the supernatant, and then fire it in a tube furnace in a nitrogen environment at 350°C, and adjust the heating rate to 50°C / min , the firing time is set to 1h...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
clearance rateaaaaaaaaaa
clearance rateaaaaaaaaaa
Login to View More

Abstract

The invention discloses a preparing method and application of tertiary amine oxide modified attapulgite containing a rosinyl ternary phenanthrene ring structure and belongs to the technical fields of water source purification and pollutant treatment. The preparing method comprises the steps of acidizing and firing attapulgite with hydrochloric acid solution firstly, and then modifying attapulgite with tertiary amine oxide containing the rosinyl ternary phenanthrene ring structure to prepare the tertiary amine oxide modified attapulgite containing the rosinyl ternary phenanthrene ring structure. The adsorbent can be applied to removal of environment pollutants including humic acid, fluorinion and Congo red in drinking water. The preparing process is simple, utilization rate is high, cost is low, application range is wide, operation is easy, both a modifier and a matrix are environment-friendly materials, and popularization is easy.

Description

technical field [0001] The invention belongs to the technical field of water source purification and pollutant treatment, and relates to an adsorbent, in particular to the modification preparation and application of a modified attapulgite adsorbent. Background technique [0002] In recent years, with the rapid development of my country's social economy, the discharge of water pollutants has increased year by year, and the problem of micro-pollution in the water environment has become increasingly prominent. The pollution of surface water bodies not only poses a threat to aquatic organisms, but also destroys the ecological environment, and ultimately endangers human health. Many pollutants such as humic acid, fluoride ions, and dyes from industrial wastewater exist in the surface water of our country, such as rivers, lakes, and reservoirs. Therefore, it is an urgent task to develop effective treatment methods to reduce natural organic matter represented by humic acid, inorga...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): B01J20/22B01J20/30C02F1/28C02F101/14C02F101/30C02F101/34
CPCB01J20/12B01J20/22C02F1/288C02F2101/14C02F2101/308C02F2101/34
Inventor 刘绍刚刁开盛赵芳黄婉婷覃太生马亚红张文珍杜寒春雷福厚谭学才
Owner GUANGXI UNIV FOR NATITIES
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com