High-uniformity polyurethane coating fabric and preparation method thereof

A technology of polyurethane coating and uniformity, applied in the field of polyester fiber, can solve the problems of uneven strength, difficulty of silk processing, uneven fineness, etc., and achieve the effect of good interface bonding and improving use efficiency.

Active Publication Date: 2016-11-23
JIANGSU HENGLI CHEM FIBER
View PDF6 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] In the spinning process, although the surrounding air has obvious advantages, it still cannot solve the problem of uneven cooling of porous filaments: since the spun silk is extruded from the circular spinneret, it is cooled by the surrounding air, Due to the large number of circles of the circular spinneret, it is difficult for the ring air to enter the innermost layer, resulting in that the innermost filaments may not be cooled after the outermost filaments have cooled, resulting in uneven fineness of the resulting filaments. Problems such as uneven strength make subsequent further processing of silk difficult

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • High-uniformity polyurethane coating fabric and preparation method thereof
  • High-uniformity polyurethane coating fabric and preparation method thereof
  • High-uniformity polyurethane coating fabric and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] A preparation method of modified polyester, specifically comprising the following steps:

[0066] (1) Preparation of glycol terephthalate:

[0067] Put terephthalic acid and 2-pentyl-1,3 propanediol with a molar ratio of 1:1.3 into a slurry and add it to the reactor at a concentration of 50 wt%, and the addition amount is 0.3% of the weight of terephthalic acid. Under the catalysis of sulfuric acid, esterification reaction is carried out. The esterification reaction is pressurized in a nitrogen atmosphere. The pressurized pressure is normal pressure and the temperature is 180°C. Time is the end point of the esterification reaction to obtain diol terephthalate;

[0068] (2) Preparation of ethylene terephthalate:

[0069] Put terephthalic acid and ethylene glycol into a slurry with a molar ratio of 1:1.2 and add them into the reactor to carry out esterification reaction. The esterification reaction is pressurized in a nitrogen atmosphere. The pressurized pressure is nor...

Embodiment 2

[0076] The preparation method of the modified polyester of embodiment 2, wherein the preparation process of modified polyester is with embodiment 1, wherein main technical parameter is referring to table 1; After step (3) adds glycol terephthalate, Stirring and mixing for 16 minutes, under the action of 0.011% catalyst antimony trioxide of the total weight of terephthalic acid and 0.02% of the stabilizer triphenyl phosphate of the total weight of terephthalic acid, under negative Start the polycondensation reaction in the low vacuum stage under the condition of high pressure, the pressure in this stage is steadily pumped from normal pressure to the absolute pressure of 490Pa, the temperature is controlled at 262 ° C, and the reaction time is 31 minutes; then continue to vacuumize and carry out the polycondensation reaction in the high vacuum stage. The reaction pressure was reduced to an absolute pressure of 90 Pa, the reaction temperature was controlled at 276° C., and the rea...

Embodiment 3

[0079] The preparation method of the modified polyester of embodiment 3, wherein the preparation process of modified polyester is with embodiment 1, wherein main technical parameter is referring to table 1; After step (3) adds glycol terephthalate, Stirring and mixing for 16 minutes, under the action of the 0.03% catalyst antimony trioxide and the 0.02% stabilizer triphenyl phosphate of the terephthalic acid gross weight in an add-on, under negative Start the polycondensation reaction in the low vacuum stage under the condition of high pressure, the pressure in this stage is steadily pumped from normal pressure to the absolute pressure of 498Pa, the temperature is controlled at 263 ° C, and the reaction time is 32 minutes; then continue to vacuumize and carry out the polycondensation reaction in the high vacuum stage. The reaction pressure was reduced to an absolute pressure of 90 Pa, the reaction temperature was controlled at 277° C., and the reaction time was 57 minutes to pr...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
water pressureaaaaaaaaaa
peel strengthaaaaaaaaaa
thermal resistanceaaaaaaaaaa
Login to View More

Abstract

The invention relates to a high-uniformity polyurethane coating fabric and a preparation method thereof. The raw material of high-uniformity polyurethane coating fabric industrial yarn is modified polyester composed of terephthalic acid chain segments, ethylene glycol chain segments and dihydric alcohol chain segments containing a branched chain. The preparation method of the high-uniformity polyurethane coating fabric industrial yarn comprises the steps that terephthalic acid and dihydric alcohol containing the branched chain are subjected to an esterification reaction under the catalytic action of concentrated sulfuric acid, and phthalic acid dibasic alcohol ester is obtained; terephthalic acid and ethylene glycol are prepared into slurry to be subjected to an esterification reaction, and terephthalic acid glycol ester is obtained; phthalic acid dibasic alcohol ester and terephthalic acid glycol ester are stirred and mixed, under the action of a catalyst and a stabilizer, a polycondensation reaction in a low vacuum stage and a polycondensation reaction in a high vacuum stage are conducted, and modified polyester is obtained; modified polyester is subjected to solid phase polycondensation tackifying, metering, porous spinneret plate extruding, cooling, oiling, stretching, heat setting and winding, and the high-uniformity polyurethane coating fabric industrial yarn is obtained; a fabric layer is obtained through weaving, the fabric layer is subjected to two dipping and two rolling and coating to be synthesized into polyurethane resin, and the high-uniformity polyurethane coating fabric is obtained.

Description

technical field [0001] The invention belongs to the technical field of polyester fibers, and relates to a high-uniformity polyurethane coated fabric and a preparation method thereof. Background technique [0002] Since its inception, polyethylene terephthalate (PET fiber or polyester fiber) fiber has high breaking strength and elastic modulus, moderate resilience, excellent heat setting, good heat resistance and light resistance, acid resistance, alkali resistance and corrosion resistance. It has a series of excellent performances such as anti-wrinkle and anti-wrinkle, good stiffness, etc. It is widely used in clothing, home textiles and other fields. [0003] Polyester-TPU (thermoplastic polyurethane) coated fabric is a composite material made of polyester fabric as the base and TPU as the coating. Because of its advantages of light weight, high strength, hygiene and environmental protection, it is widely used in sportswear, raincoats, kayaks, Widely used in tents, soft wa...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): D06N3/00D06N3/14D01D5/08D01D5/092D01D5/096D01D5/24D01D5/253D01F6/92C08G63/183
CPCC08G63/183D01D5/08D01D5/092D01D5/096D01D5/24D01D5/253D01F6/92D06N3/0036D06N3/14
Inventor 范红卫孙晓华宋光坤赵慧荣王山水杨大矛范晓兵张元华
Owner JIANGSU HENGLI CHEM FIBER
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com